NixTi1 - 3xM2xO2 (M = Sb, Nb; 0·05 ≤ x ≤ 0·10) samples have been synthesised from mixtures of NiO, Nb2O5, Sb2O3, and TiO2. From characterisation of these samples, x = 0·05 was chosen to compare results with different nickel precursors. Thus samples of Ni0·05Ti0·85M0·10O2 (M = Sb, Nb) were also prepared from NiCO3.3Ni(OH)2.4H2O, NiCl2.6H2O, Ni(NO3)2.6H2O, NiSO4.6H2O, and Ni(CH3COO)2.4H2O. A eutectic mixture of alkaline halides (NaF:2NaCl) was used as fluxing agent. Optimal yellow colour was found in the mixture of NiSO4.6H2O, Sb2O5, and TiO2 fired at 1100°C for 2 h.
‘DCMA classification and chemical description of the mixed metal oxide inorganic coloured pigments’, 2nd edn; 1982, Washington, DC, Dry Color Manufacturers Association.
2.
BADENESJ. A., VICENTJ. B., LLUSARM., TENAM. A. and MONRÓSG.: J. Mater. Sci., 2002, 37, 1413–1420.
3.
ROSSMANG. R., SHANNONR. D. and WARINGR. K.: J. Solid State Chem., 1981, 39, 277–287.
4.
CZAJKOWSKIW. and KRASKAJ.: Pol. J. Chem., 1984,58, 479–485.
5.
KUCHENW., MOOTZD., POLLW. and STEPHANR.: Acta Crystallogr. A, 1984, 40, C309–C309.
6.
SORLÍS., TENAM. A., BADENESJ. A., CALBOJ., LLUSARM. and MONRÓSG.: J. Eur. Ceram. Soc., to be published.
7.
GARCÍAA., LLUSARM., SORLÍS., TENAM. A., CALBOJ. and MONRÓSG.: Br. Ceram. Trans., 2002, 101, 242–246.
8.
LLUSARM., CALBOJ., BADENESJ. A., TENAM. A. and MONRÓSG.: J. Mater. Sci., 2001, 36, 153–163.
9.
TENAM. A., MESTREA., GARCIAA., SORLÍS. and MONRÓSG.: J. Sol-Gel Sci. Technol., 2003, 26, 813–816.
10.
GARCÍAA., LLUSARM., CALBOJ., TENAM. A. and MONRÓSG.: Green Chem., 2001, 3, 238–242.
11.
‘Recommendations on uniform color spaces, color difference equations, phychometric color terms’, Supplement 2 of CIE Publication 15 (E1-1.31); 1971, Paris, Bureau Central de la CIE.