The morphology of alumina was studied in laboratory experiments and in samples from the steel plant. Varying morphologies of alumina were observed after deoxidation and reoxidation but a clear discrimination between alumina formed by deoxidation or reoxidation was not observed. Local concentration gradients during the addition and dissolution of aluminium can explain different growth mechanisms which lead to the observed varying morphologies of alumina.
RastogiR.CrambA. W.: ‘Inclusion formation and agglomeration in aluminum killed steels’, ISS Steelmaking Conf. Proc., 2001, 84, 789–829.
3.
SteinmetzE.LindenbergH.-U.MörsdorfW.HammerschmidP.: ‘Ausbildungsformen und Entstehung von Aluminiumoxiden in Rohblöcken und Stranggubbrammen’, Stahl und Eisen, 1997, 97, (23), 1154–1159.
4.
MatsuuraH.WangC.WenG.ShridharS.: ‘The transient stages of inclusion evolution during Al and/or Ti additions to molten iron’, ISIJ Int., 2007, 47, (9), 1265–1274.
5.
WangC.NuhferN. T.ShridharS: ’Transient behavior of inclusion chemistry, shape, and structure in Fe–Al–Ti–O melts: effect of Ti/Al ratio’, Metall. Mater. Trans. B, 2009, 40B, 1022–1034.
6.
BeskowK.SichenD.: ‘Experimental study of the nucleation of alumina inclusions in liquid steel’, Scand. J. Metall., 2003, 32, 320–328
7.
van EndeM.-A.GuoM.ProostJ.BlanpainB.WollantsP.: ‘Morphology of Al2O3 inclusions formed at the Fe/Fe–Al alloy interface’, Proc. Euromat Conf., Glasgow, UK, September 2009, Ironmaking Steelmaking, 2010, 37, (7), 496–501.
8.
ZhangL.PluschkellW.: ‘Nucleation and growth kinetics of inclusions during liquid steel deoxidation’, Ironmaking Steelmaking, 2003, 30, (2), 106–110.
9.
OoiH.SekineT.SakaiG.: ‘On the mechanism of alumina cluster formation in molten iron’, Trans. ISIJ, 1975, 15, 371–379.
10.
TiekinkW.BrockhoffJ.MaesR.: ‘Total oxygen measurements at Hoogovens IJmuiden BOS No.2’, ISS Steelmaking Conf. Proc., 1994, 81, 49–51.
11.
PieletH.-M.TsaiH. T.GassR. T.: ‘Characterisation of inclusions in TISULC steels from degasser to mould’, ISSTech2003Conf. Proc., Indianapolis, Indiana, April 2003, ISS, 241–255.
12.
EnderA.PetryS.: in ECSC research 7210–PR/333, ‘Optimisation and evaluation of different secondary metallurgy routes to achieve high quality strip steel’, Fandrich, et al, ISBN 978–92-79-11981, EUR 23888, 2009, 23–45.
13.
TiekinkW.BoomR.OverboschA.LandskroonJ.DeoB.: ‘Initial stages of alumina formation’, Proc. 7th Int. Conf. on ‘Clean steel’, Balatonfüred, Hungary, June 2007, Hungarian Mining and Metallurgical Society, 48–57.
14.
TurkdoganE. T.: in‘BOF steelmaking’, (ed. PehlkeR. D., et al.), Vol. 2, Chap. 4, 163; 1975, New York, ISS.
15.
MelzerS.ZinngrebeE.: ‘Using EBSD to study orientation relationships in individual corundum clusters from desoxidation of Al-killed steel’, a poster at the EBSD meeting2007, Royal Microscopic Society, New Lanark, Scotland.
16.
van EndeM.-A.: ‘Formation and morphology of non-metallic inclusions in aluminium killed steels’, PhD thesis, Katholieke Universiteit Leuven and Universite´ Catholique de Louvain, Belgium, January2010, 146–152.
17.
KawakamiM.YokoyamaS.TakagiK.NishimuraM.KimJ.-S.: ‘Effect of aluminum and oxygen content on diffusivity of aluminum in molten iron, ISIJ Int., 1997, 37, (5), 425–431.
18.
FruehanR. J.: ‘Ladle metallurgy principles and practices’, ISS, USA, 1985, ISBN No. 0–932897-01-0, 14
19.
WangY.ShridharS.CrambA. W.GomezA.CicuttiC.: ‘Reoxidation of low-carbon, aluminium-killed steel’, Iron Steel Technolo., 2004, 1, (2), 87–96.
20.
OkohiraK.SatoN.MoriH.: ‘Observation of three-dimensional shapes of inclusions in low-carbon aluminium-killed steel by scanning electron microscope’, Trans. ISIJ, 1974, 14, 103–109.
21.
OvtchinnikovS.KazakovS.JankeD.: ‘Formation of oxide inclusions during deoxidation and solidification of high purity steels’, Ironmaking Steelmaking, 2003, 30, (6), 487–496.
22.
WasaiK.MukaiK.MiyanagaA.: ‘Observation of inclusion in aluminium deoxidized iron’, ISIJ Int., 2002, 42, (5), 459–466.