Viscosity effect of titanium pickup by mould fluxes for stainless steel

Abstract

Mould flux samples from an operating continuous caster showed a steady state increase in titanium oxide content of 3–4% for a titanium stabilised ferritic stainless steel and about 6% for a titanium stabilised austenitic stainless steel. Owing to the reduction of silica the flux basicity increased from 0.8 to 0.9, and from 0.95 to 1.2, for the ferritic and austenitic steels, respectively. Similar changes in composition were found for mould shims, which had been recovered from the mould after casting the ferritic steel. The increased titanium oxide content caused a decrease in the flux viscosity, for the original basicity. However, when the flux basicity was increased from 0.95 to 1.2, the apparent viscosity of the mould flux of the austenitic steel increased markedly, for 10% TiO₂ and temperatures of 1250°C and below. Precipitation of perovskite was found to be responsible for the higher apparent viscosity.

Get full access to this article

View all access options for this article.

References

Liao

Fruehan

R. J.

: Iron Steelmaker, 1989, 16, (10), 91–97.

Sharan

Jimbo

Cramb

A. W.

: Iron Steelmaker, 1994, 21, (12), 37–41.

Ozturk

: Metall. Materials Trans. B, 1992, 23B, 523–526.

Riquier

Lambert

Dumortier

: Bull. Cercle Etud. Metaux, 1997, 16, (14), 5.1–5.18.

Bommaraju

: Steelmaking Conf. Proc., 1991, 74, 131–146.

Mukongo

Pistorius

P. C.

: ‘Effects of titanium pickup in mould fluxes for stainless steel’, Proc. ISSTech2003, 27–30 April 2003, Indianapolis, IN, USA, Iron and Steel Society, 675–682.

Johnston

P. W.

Brooks

: Proc. 5th Int. Conf. on ‘Molten slags, fluxes and salts’, Sydney, Australia, January 1997, ISS, 845–850.

Kishi

Takeuchi

Yamimaya

, ‘Mold powder technology for continuous casting of titanium-stabilized stainless steel’, Technical Report 34, Nippon Steel, Japan, 1987, 11–20.

Pelton

A. D.

: Personnal communication, Ecole Polytechnique de Montreal, Canada, 2003.

10.

Turkdogan

E. T.

: Iron Steel Soc. Trans., 1990, 11, 39–53.

11.

Ozturk

Matway

Fruehan

R. J.

: Metall. Mater. Trans. B, 1995, 26B, 563–567.

12.

Schürmann

Djurdjevic

Ndeljkovic

: Steel Res., 1997, 68, 101–106.

13.

Bezuidenhout

G. A.

Pistorius

P. C.

: Ironmaking Steelmaking, 2000, 27, 387–391.

14.

Kubaschevski

Alcock

C. B.

Spencer

P. J.

: ‘Materials thermochemistry’, 6th edn, 258–323; 2001, Oxford, Pergamon.

15.

Sigworth

G. K.

Elliott

J. F.

: Met. Sci., 1974, 8, 298–310.

16.

Bale

C. W.

Chartrand

Degterov

S. A.

Eriksson

Hack

Ben Mahfoud

Melancon

Pelton

A. D.

Petersen

: Calphad, 2002, 26, 189–228.

17.

‘Steelmaking data sourcebook’, The Japan Society for the Promotion of Science, 19th Committee on Steelmaking, 280–293; 1988, New York, NY, Gordon and Breach Science.

18.

Roscoe

: Brit. J. Appl. Phys., 1952, 3, 267–269.

19.

Mukongo

. ‘Effect of titanium pickup on mould flux viscosity in continuous casting of titanium-stabilised stainless steel’, MEng thesis, University of Pretoria, South Africa, 2003.