Interpretation of creep behaviour of a 9Cr–Mo–Nb–V–N (T91) steel using threshold stress concept

Abstract

The creep behaviour and the microstructural evolution of a 9Cr–Mo–Nb–V (T91) steel were extensively evaluated by means of short term constant load creep tests and TEM analysis. Statistical analysis of the microstructural data revealed that the precipitated phases M₂₃ C₆ (where M is a metal, mainly Cr or Fe) and MX (where M is Nb or V, and X is C and/or N) were subject to coarsening during creep exposure. The coarsening law and its dependence on applied stress were identified, and the model was used to predict the magnitude of the Orowan stress at the time corresponding to the minimum creep rate. The minimum creep rate dependence on applied stress at 873 K was described by incorporating the threshold stress concept in a power law with stress exponent n = 5. In the resulting phenomenological model, the strengthening effect of the dispersed phases was thus expressed by a threshold stress proportional to the Orowan stress.