Effect of test temperature on fracture toughness of modified 9Cr–1Mo steel

Abstract

The quasi-static fracture behaviour (J–R curves) of modified 9Cr–1Mo (P91) steel was studied. The J–R curves were established at 298, 653, 823 and 893 K, and fracture toughness J_0·2 at 0·2 mm of crack extension was determined. The value of ∼J_0·2 at 653 K was lower compared to that at 298 K followed by increases in J_0·2 values at 823 and 893 K. The decrease in J_0·2 at 653 K can be attributed to the influence of dynamic strain aging. At 893 K, a significantly higher (more than 200) J_0·2 was observed, since plastic deformation of the net section, rather than crack growth, occurred in this condition.