The effects of neodymium rich rare earth elements [RE(Nd)] on microstructure and mechanical properties of as cast AZ31 magnesium alloy were investigated. The microstructures of as cast AZ31–xRE(Nd) alloys display a dendrite configuration, and the secondary dendrite spacing of the α-Mg phase was decreased with the increasing Nd content. The addition of RE(Nd) resulted in the formation of Al2Nd and Mg12Nd phases. Mechanical properties were improved significantly due to grain refinement and precipitation of intermetallic phases. When the amount of RE is 1·0 wt-%,The as cast AZ31 alloy reached its maximum tensile strength of 249 MPa at room temperature, yield strength of 169 MPa and elongation of 9·0%.
HuangXF, WangQD, ZengXQ, YuanGY, ZhuYP, DingWJ: ‘Influence of rare earth on mechanical properties and high temperature creep properties of AM50 magnesium alloy’, J. Chn Rare Earth Soc., 2004, 22, (4), 493–496.
2.
PelcovaJ, SmolaB, StulikovaI: ‘Influence of processing technology on phase transformations in a rare-earth-containing Mg–Zn–Zr alloy’, Mater. Sci. Eng. A, 2007, A462, 334.
3.
SomekawaH, MukaiT: ‘Effect of texture on fracture toughness in extruded AZ31 magnesium alloy’, Scr. Mater., 2005, 53, 541.
4.
MuraiT, MatsuokaS, MiyamotoS, OkiY: ‘Effects of extrusion conditions on microstructure and mechanical properties of AZ31B magnesium alloy extrusions’, J. Mater. Proc. Technol., 2003, 141, 207.
5.
XiaoDH, SongW, ChenKH, HuangBY: ‘Effects of erbium addition on microstructure and mechanical properties of as-cast Mg–Al–Zn–Mn magnesium alloys’, Spec. Cast. Nonferr. Alloys, 2007, 27, (11), 165–169.
6.
HuangXF, WangQD, ZengXQ, LuC, ZhuYP, DingWJ: ‘Effect of Neodymium on Microstructure and High Temperature Creep Properties of Mg–5Al–1Si Magnesium Alloy’, J. Chn Rare Earth Soc., 2004, 22, (3), 65–70.
7.
HuGX, QianMG: ‘Metallography’; 1980, Shanghai, Shanghai Science and Technology Press.
8.
KearnsMA, CooperPS: ‘Effects of solutes on grain refinement of selected wrought aluminum alloys’, Mater. Sci. Techenol., 1997, 13, (2), 650–654.
9.
ApelianD, SigworthGK, WhalerKR: ‘Assessment of grain refinement and modification of Al–Si foundry alloys by thermal analysis’, AFS Trans., 1984, 92, (2), 297–307.
10.
LiuHM, ChenYG, TangYB, HuangDM, NiuG, TuMJ, ZhaoM, LiYG: ‘Microstructure and properties of MgAl6C0·12B0·24 alloys with the addition of Nd–Pr mixed metal’, J. Chn Rare Earth Soc., 2005, 23, (11), 236–239.