Ductile cast iron has been an important engineering material in the past 50 years. In that time, it has evolved from a complicated material that required the foundry metallurgist's highest skill and strict process control to being a commonly used material that can easily be produced with modern process technology. Yet, for the skilled metallurgist and foundry engineer, it is a material that can be engineered to meet extreme demands with regard to mechanical properties and geometrical complexity. It is therefore a material that has been in growing use since its discovery. And the results of the latest years of research indicate that ductile cast iron in the future will become a highly engineered material in which strict control of a range of alloy elements combined with intelligent design and highly advanced processing allows us to target properties to specific applications to a much higher degree than we have seen previously. It is the aim of the present paper to present ductile iron as a modern engineering material and present the many different possibilities that the material hides. Focus will be on the latest research in solidification and melt treatment. But for completeness and to illustrate how ductile iron's properties are optimised, the essentials of heat treatment are described too. It is the hope that researchers will find a comprehensive treatment of ductile cast iron metallurgy and that engineers and designers will be presented with the latest information on, and references to, the properties and possibilities in ductile cast iron.
PedersenK. M. and TiedjeN.: ‘Solidification and gravity IV’, Mater. Sci. Forum, 508,181–186.
15.
MampaeyF.: AFS Trans., 2002, 110, 869–2002.
16.
SkalandT.: AFS Trans., 2001, 109, 1073–1084.
17.
OnsoienM. I., 0. Grong, 0. Gundersen and T. Skaland: Metall Trans. A, 1999, 30A, 1053-1068.
18.
LesoultG., CastroM. and LacazeJ.: Acta Metall. Mater., 1998, 46, 983–995.
19.
HasseS.: Giesserei-Praxis, 1995, Vol. 8, 124–133.
20.
BastJ. and SolovjovV.: Giesserei, 1995, 11, 379–382.
21.
SkalandT.: Proc. Int. Conf. on ‘Best practices in the production, processing and thermal treatment of castings’, Singapore, October 1995, Cast Metals Development Ltd,1–23.
22.
SkalandT., GrongO. and GrongT.: Metall Trans. A, 1993, 24A, 2321–2345.
23.
D'AngeloL., JespersenF. N., TiedjeN. S. and HorsewellA.: ‘3-D analysis of graphite nodules in ductile cast iron using FIB-SEM’, Presentation D18, Proc. Conf. Euromat 2009, Glasgow, UK, September 2009, Institute of Materials, Minerals and Mining.
24.
MullinsJ. D.: ‘Ductile iron data for design engineers’; 2009, Montreal, Que., Rio Tinto Iron & Titanium, Inc.
25.
SpadaA.: Proc. 68th World Foundry Cong., Chennai, India, February 2008, Institute of Indian Foundrymen,7–13.
26.
CampbellJ.: Mater. Sci Technol, 1988, 4, 194–204.
27.
DawsonS.: Proc. 68th World Foundry Cong., Chennai, India, February 2008, Institute of Indian Foundrymen,93–99.
DoubleD. D. and HellawellA.: Acta Metall, 1974, 22, 481–487.
62.
SparkmanD.: Mod Cast., 1994, Vol. 1, 35–37.
63.
SertuchaJ., SuarezR., AsenjoI., LarranagaP., LacazeJ., FerrerI. and ArmendarizS.: ‘Thermal analysis of the formation of chunky graphite during solidification of heavy-section spheroidal graphite iron parts’, ISIJ Int., 2009, 49, (2), 220–228.
64.
LarranagaP., AsenjoI., SertuchaJ., SuarezR., FerrerI. and LacazeJ.: Metall Mater. Trans. A, 2009, 40A, 654–661.
65.
PedersenK. M., HattelJ. H. and TiedjeN.: Acta Mater., 2006,54, 5103–5114.
66.
SillenR.: Foundryman, 2003, 96, 245–246.
67.
NofalA. A., Parent-SimoninS. and RezkA. S.: Fonderie Fondeur d'Aujourd'hui, 1989, 83, 14–24.
68.
VelichkoA., HolzapfelC. and MfiklichF.: Adv. Eng. Mater., 2009, 9, 39–45.
69.
FredrikssonH., StjerndahlJ. and TinocoJ.: ‘On the solidification of nodular cast iron and its relation to the expansion and contraction’, Mater. Set Eng. A, 2005, A413-A414,363–372.
70.
PedersenK. M. and TiedjeN. S.: Undercooling, nodule count and carbides in thin walled ductile cast iron, 68th World Foundry Congress 2008, Chennai, India, pp.167–171.
71.
StefanescuD. M.: ISIJ Int., 1995, 35, 637–650.
72.
RiposanI., ChisameraM., StanS. and WhiteD.: AFS Trans., 2007, 115, 423–433
73.
SillenR. V.: Mod Cast., 1996, 86, 43–46.
74.
PedersenK. M. and TiedjeN. S.: Mater. Charact., 2008, 59, 1111–1121.
SkalandT. and OnsoienM. I.: AFS Trans., 2001, 109, 1139.
77.
HeineR. W.: Giesserei-Praxis1995, 13/14, 242–253.
78.
StefanescuD. M.: ‘Advanced casting and solidification technol-ogy’, Proc. COST 504 Conf., Espoo, Finland, September 1994, Tampere University of Technology, Finland, 27.
SkalandT.: Proc. 68th World Foundry Cong., Chennai, India, February 2008, Institute of Indian Foundrymen, 68th World Foundry Congress 2004, Istanbul, Turkey, pp.975–987.
84.
PedersenK. M. and TiedjeN. S.: Mater. Charact., 2007, 58, 456–461.
85.
MaguregiJ. I., CreoR. S. and GiiemesJ. A. G.: Proc. 66th World Foundry Cong., Istanbul, Turkey, September 2004, WFO,953–962.
YescasM. A. and BhadeshiaH. K. D. H.: Mater. Sci. Eng. A, 2001, A311,162–173.
94.
HayrynenK. L.: Proc. 2002 World Conf. on ‘Austempered ductile iron’, Louisville, KY, USA, American Foundry Society, 1-13,
95.
SturlasonA.: Proc. Conf. ‘Nordic Foundry Days, Tonsberg, Norway, August 2005, TBL and Stopforsk, Presentation no. 2.
96.
CabanneP.-M. and GagneM.: Proc. 66th World Foundry Cong., Istanbul, Turkey, September 2004, WFO,877–889.
97.
PaninskiM.: Proc. Annual Meet. Danish Foundry Association, Nyborg, Denmark, 10 June 2009, Danish Foundry Association Presentation 4.
98.
TiedjeN. S., DrivsholmC., Skov-HansenS. and CrepazR.: Proc. 68th World Foundry Cong., Chennai, India, February 2008, Institute of Indian Foundrymen,251–254.
99.
Skov-HansenS. and TiedjeN. S.: Giesserei, 2008, 95, 12–28.
100.
CampbellJ.: ‘Castings practice: the 10 rules of castings’; 2004, Oxford, Elsevier/Butterworth-Heinemann.
101.
LarsenP. L. and TiedjeN.: Proc. 66th World Foundry Cong., Istanbul, Turkey, September 2004, WFO,223–234.