Melt conditioning by advanced shear technology (MCAST) is a new process for microstructural refinement of both cast and wrought magnesium alloys. Melt conditioned direct chill (MCDC) casting combines the MCAST process with conventional direct chill (DC) casting. In the present work, melt conditioning has been combined with permanent mould casting to simulate the production of DC cast AZ91D billets and slabs. The results show that the MCDC process can achieve significantly finer grain size and more uniform microstructure than conventional DC process for both billets and slabs. Grain refinement in the MCDC process is due to the fine and well dispersed oxide particles produced after processing in the MCAST unit.
MordikeB. L. and EbertT.: Mater. Sci. Eng. A, 2001, A302, 37–45.
2.
ZhangS. M. , FanZ. and ZhenZ.: Mater. Sci. Technol., 2006, 22, 1489–1498.
3.
QiuD. , ZhangM. X. , TaylorJ. A. , FuH. M. and KellyP. M.: Acta Mater., 2007, 55, 1863–1871.
4.
St JohnD. H. , QianM. , EastonM. A. , CaoP. and HildebrandZ.: Metall. Mater. Trans. A, 2005, 36A, 1669–1679.
5.
LeeY. C. , DahleA. K. and St JohnD. H.: Metall. Mater. Trans. A, 2000, 31A, 2895–2906.
6.
QianM. and DasA.: Scr. Mater., 2006, 54, 881–886.
7.
LiP. J. , TangB. and KandalovaE. G.: Mater. Lett., 2005, 59, 671–675.
8.
JinQ. L. , EomJ.-P. , LimS.-G. , ParkW.-W. and YouB.-S.: Scr. Mater., 2003, 49, 1129–1132.
9.
CaoP. , QianM. and StD. H. John: Scr. Mater., 2006, 54, 1853–1858.
10.
EastonM. A. , SchifflA. , YaoJ.-Y. and KaufmannH.: Scr. Mater., 2006, 55, 379–382.
11.
GaoD. M. , LiZ. J. , HanQ. Y. and ZhaiQ. J.: Mater. Sci. Eng. A, 2009, A502, 2–5.
12.
LiuX. B. , OsawaY. , TakamoriS. and MukaiT.: Mater. Lett., 2008, 62, 2872–2875.
13.
GuoS. J. , CuiJ. Z. , LeQ. C. and ZhaoZ. H.: Mater. Lett., 2005, 59, 1841–1844.
14.
FanZ. , XiaM. , ZhangH. , LiuG. , PatelJ. B. , BianZ. , BayandorianI. , WangY. , LiH. T. and ScamansG. M.: Int. J. Cast Met. Res., 2009, 22, 103–107.
15.
FanZ. , WangY. , ZhangZ. F. , XiaM. , LiH. T. , XuJ. , GranasyL. and ScamansG. M.: Int. J. Cast Met. Res., 2009, 22, 318–322.
16.
LiuG. , WangY. and FanZ.: Mater. Sci. Eng. A, 2008, A472, 251–257.
17.
TzamtzisS. , ZhangH. , BabuN. and FanZ.: ‘Melt conditioning high pressure die casting (MC-HPDC) of Mg alloys’, Proc. Conf. on ‘Magnesium technology’, San Francisco, CA, USA, February 2009, TMS, 91–96.
18.
BianZ. , BayandorianI. , ZhangH. W. and FanZ.: Solid State Phenom., 2008, 141–143, 195–200.
19.
BayandorianI. , BianZ. , XiaM. , ZhangH. and FanZ.: ‘Magnesium alloy strips produced by a melt conditioned twin roll casting (MC-TRC)’, Proc. Conf. on ‘Magnesium technology’, San Francisco, CA, USA, February 2009, TMS, 363–368.
20.
‘Standard test procedure for aluminium alloy grain refiners (TP-1)’, The Aluminium Association, Washington, DC, USA, 1990.
21.
XiaM. , WangY. , LiH. , ArumuganatharS. , ZuoY. , ScamansG. M. and FanZ.: ‘Refinement of solidification microstructure by MCAST process’, Proc. Conf. on ‘Magnesium technology’, San Francisco, CA, USA, February 2009, TMS, 135–140.
22.
ZhangM. X. , KellyP. M. , QianM. and TaylorJ. A.: Acta Mater., 2005, 53, 3261–3270.
23.
FuH. M. , QiuD. , ZhangM. X. , WangH. , KellyP. M. and TaylorJ. A.: J. Alloys Compd, 2008, 456, 390–394.