Understanding the role of grain boundaries has been impeded by continued adoption of power law equations for identification of the processes governing creep and creep fracture of metals and alloys. In contrast, the dominant mechanisms can be clarified through new relationships which involve normalisation of the applied stress by the yield and ultimate tensile strengths determined from high strain rate tests at the creep temperatures.
NabarroF. R. N.: in ‘Report on conf. on strength of solids’, 75–90; 1948, London, Physical Society.
2.
HerringC.: J. Appl. Phys., 1950, 21, 437–445.
3.
CobleC.: J. AppL Phys., 1963, 34, 1679–1682.
4.
HarperJ. and DornJ. E.: Acta Metall., 1957, 5, 654–665.
5.
MishraR. S., MukherjeeA. K., MurtyK. L. (eds.): in ‘Creep behaviour of advanced materials for the 21st century’, 391-507; 1999, Warrendale, PA, TMS.
6.
HoldsworthS. R.: in: ‘Creep and fracture of high temperature components — design and life assessment issues’, (ed.ShibliI. A.et al), 380-393; 2005, London, DES tech Publ.
7.
WilshireB. and BurtH.: Metall Mater. Trans. A, 2006, 37A, 1005–1015.
8.
WilshireB. and BattenboughA. J.: Mater. Set Eng. A, 2007, A443,156–166.
9.
WilshireB. and ScharningP. J.: Inter. Mater. Rev., 2008, 53, 91–104.
10.
WilshireB. and ScharningP. J.: Mater. Set Technol, 2008, 24, 1–9.
11.
WilshireB. and ScharningP. J.: Int. J. Press. Vessels Pip., 2008, 85, 739–743.
12.
WilshireB. and ScharningP. J.: J. Mater. Sci., 2008, 43, 3992–4000.
13.
DaviesP. W., RichardsJ. D. and WilshireB.: J. Inst. Met., 1961-62, 90, 431–433.
14.
WilshireB. and PalmerC. J.: Ser. Mater., 2002, 46, 483–488.
15.
KaufmanJ. G.: in ‘Properties of aluminium alloys’: 1999, Materials Park, OH, ASM.
16.
SquiresR. L., WeinerR. T. and PhillipsM.: J. Nucl. Mater., 1963, 8, 77–80.
17.
HarrisJ. E. and JonesR. B.: J. Nucl. Mater., 1963, 10, 360–362.
18.
AigeltingerE. H. and GifkinsR. C.: J. Mater. Set, 1975, 10, 1889–1903.
19.
WilshireB. and BurtH.: Z. MetalL, 2005, 96, 552–557.