By using a low SEM accelerating voltage in the range of 5–7·5 kV with an electron backscatter diffraction system, the interaction volume of electrons with matter is markedly decreased, and the spatial resolution is improved. The authors present measurements which prove this relationship. Electron backscatter diffraction at low acceleration voltage, however, is not a straightforward technique with the current equipment and a standard set-up. The authors show that an optimised working distance and dedicated sample preparation are essential to obtain improved spatial resolution for detailed nanoscale microstructure investigations.
IsabellT. C. and DravidV. P.: ‘Resolution and sensitivity of electron backscattered diffraction in a cold field emission gun SEM’, Ultramicroscopy, 1997, 67, (1-4), 59–68.
2.
ZaeffererS.: ‘On the formation mechanisms, spatial resolution and intensity of backscatter Kikuchi patterns’, Ultramicroscopy, 2007, 107, (2-3), 254–266.
3.
RenS. X., KenikE. A., AlexanderK. B. and GoyalA.: ‘Exploring spatial resolution in electron back-scattered diffraction experiments via Monte Carlo simulation’, Microsc. Microanal, 1998,4, (1), 15–22.
4.
AlamM. N., BlackmanM. and PashleyD. W.: ‘High-angle Kikuchi patterns’, Proc. Roy. Soc. Lond A Math Phys. Sci., 1954, 221, (1145), 224242.
5.
HumphreysF. J.: ‘Characterisation of fine-scale microstructures by electron backscatter diffraction’, Scr. Mater., 2004,51, (8), 771–776.
6.
HarlandC. J., KleinJ. H., AkhterP. and VenablesJ. A.: ‘Electron back-scattering patterns in a field emission gun scanning electron microscope’, Proc. 9th Int. Cong. on ‘Electron microscopy’, Toronto, Ont., Canada, August 1978, Microscopical Society of Canada,564–565.
7.
HarlandC. J., AkhterP. and VenablesJ. A.: ‘Accurate microcrystallography at high spatial-resolution using electron backscattering patterns in a field-emission gun scanning electron-microscope’, J. Phys. E, 1981, 14E, (2), 175–182.
8.
DingleyD. J. and RandleV.: ‘Microtexture determination by electron back-scatter diffraction’, J. Mater. Sci., 1992, 27, (17), 4545–4566.
9.
Baba-KishiK. Z.: ‘Measurement of crystal parameters on backscatter Kikuchi diffraction patterns’, Scanning, 1998, 20, (2), 117–127.
10.
FarstadO., JohannessenK. and HjelenJ.: ‘Spatial resolution of EBSP using fully automated pattern indexing’, Electron Microsc. 1998, 3, 1998, 753–754.
11.
PriorD. J., BoyleA. P., BrenkerF., CheadleM. C., DayA., LopezG., PeruzzoL., PottsG. J., ReddyS., SpiessR., TimmsN. E., TrimbyP., WheelerJ. and ZetterstromL.: ‘The application of electron backscatter diffraction and orientation contrast imaging in the SEM to textural problems in rocks’, Am. Mineral., 1999, 84, (11-12), 1741–1759.
12.
DingleyD.: ‘Progressive steps in the development of electron backscatter diffraction and orientation imaging microscopy’, J. Microsc., 2004, 213, 214–224.
13.
KellerR. R., RoshkoA., GeissR. H., BertnessK. A. and QuinnT. P.: ‘EBSD measurement of strains in GaAs due to oxidation of buried AlGaAs layers’, Microelectron. Eng., 2004, 75, (1), 96–102.
14.
HumphreysF. J. and BroughI.: ‘High resolution electron backscatter diffraction with a field emission gun scanning electron microscope’, J. Microsc., 1999, 195, 6–9.
15.
HumphreysF. J., HuangY., BroughI. and HarrisC.: ‘Electron backscatter diffraction of grain and subgrain structures — resolu-tion considerations’, J. Microsc., 1999, 195, 212–216.
16.
ZaeffererS.: ‘Orientation microscopy in SEM and TEM: funda-mentals, techniques and applications in physical metallurgy’, Habilitation thesis, RWTH Aachen, Aachen, Germany, 2009.