Abstract

Traditional 11·5 wt-%Cr ferritic stainless steels are single stabilised with Ti or dual stabilised with Ti–Nb additions. A dual-stabilised ferritic stainless steel 409 with Zr–Ti additions was studied, which was selected through thermodynamic and kinetics analysis. The alloy was subjected to thermomechanical processing using both hot and cold rolling and annealing. The intergranular corrosion resistance and microstructure of this alloy was evaluated. Of particular interest was to study the stabilisation behaviour of this alloy under all processing conditions. The results showed that the precipitation of Cr_xC_y was effectively prevented; hence, the alloy used in this investigation had an excellent resistance to intergranular corrosion.

Keywords

Precipitation Sensitisation Intergranular corrosion Ferritic stainless steel

Get full access to this article

View all access options for this article.

References

Demo

J. J.

: Corrosion, 1971, 27, 531–544.

Semchyshen

Bond

A. P.

and Dunas

H. J.

: Proc. Symp. on ‘toward improved ductility and toughness’, Kyoto, Japan, October 1971, ISIJ, 239–253.

Plumtree

and Gullbert

: J. Test. Eval., 1974, 2, (5), 331–336.

Demo

J. J.

: TMS-AIME, 1974, 5, 2253–2256.

Knot

R. J.

Lakso

G. E.

and Matejka

W. A.

: Chem. Eng., 1970, 77, (11), 170–176.

Demo

J. J.

: Canadian patent no. 952 741, 13 August 1974.

British patent no. 1565419.

Preliminary data bulletin: Stainless steel AL 466, Allegheny Ludlum Steel Corporation, Pittsburgh, PA, USA, 1993.

Rege

: ‘Annealing behaviour and formability of low interstitial ferritic stainless steels’, MS thesis, University of Pittsburgh, PA, USA, 1993

10.

: Proc. Symp. on ‘Low carbon steels for the 90's’, 397–404; 1993, Warrendale, PA, TMS.

11.

Hua

Garcia

C. I.

and DeArdo

A. J.

: Proc. 38th Conf. on ‘Mechanical working and steel processing’, Cleveland, OH, USA, April 1997, ISS, 41–44.

12.

Gaskell

D. R.

: ‘Introduction to the thermodynamics of materials’, 3rd edn; 1995, Oxford, Taylor and Francis.

13.

Narita

: J. Chem. Soc. Jpn, 1959, 80, (266).

14.

Taylor

K. A.

: Scr. Metall. Mater., 1995, 32, (1), 7–12.

15.

Akamatsu

: ISIJ Int., 1994, 34, (1), 9–16.

16.

Wada

and Pehlke

R. D.

: Met. Trans., 1985, 16B, 815–822.

17.

Kubascheuski

and Evans

E. L.

: ‘Metallurgical thermochemistry’; 1979, New York, Wiley.

18.

‘Standard practices for detecting susceptibility to intergranular attack in ferritic stainless steels’, A763-93, ASTM, Philadelphia, PA, USA, 1999, 429–437.

19.

Fritz

J. D.

and Franson

I. A.

: ‘Material selection and design’, MP, August 1997, 57–61.

20.

‘Standard specification for heat-resisting chromium and chromium-nickel stainless steels plate, sheet, and strip for pressure vessels’, ASTM A240/240M-94a, in ‘Annual book of ASTM standards’; 2004, Philadelphia, PA, ASTM.

Stabilisation of ferritic stainless steels with Zr and Ti additions

Abstract

Keywords

Get full access to this article

References