Microstructural analysis of varistors prepared from nanosize ZnO

Abstract

ZnO nanoparticles were prepared by a solid state pyrolysis reaction of zinc acetate dihydrate and oxalic acid dihydrate at 500°C. The course of reaction at various temperatures was followed by XRD. Subsequently varistors were fabricated from this nano-ZnO material by solid state mixing with various oxide additives and sintering to 1050°C. The microstructure of the sintered material was studied using XRD, field emission SEM (FESEM), and EDX, and ZnO grains, bismuth rich regions and spinel phases were identified. Discs made from oxide doped nanoZnO show considerably higher breakdown voltage (656 ± 30 V mm^-1) compared to those prepared from micrometre sized ZnO (410 ± 30 V mm^-1) and commercial varistors (454 ± 30 V mm^-1). However, varistors made from the nano-ZnO show very low densification and high leakage current, making them unsuitable for device fabrication.

Keywords

NANOSTRUCTURES ZINC OXIDE VARISTORS BREAKDOWN VOLTAGE

Get full access to this article

View all access options for this article.

References

GUPTA

T. K.

: J. Am. Ceram. Soc., 1990, 73, 1817–1840.

CLARKE

D. R.

: J. Am. Ceram. Soc., 1999, 82, 485–502.

LEVINSON

L. M.

and PHILIP

H. R.

: Ceram. Bull., 1986, 65, 639–646.

MATSUOKA

: Jpn. J. Appl. Phys., 1971, 10, 736–746.

WISEMAN

G. H.

: Key. Eng. Mater., 1998, 150, 209–218.

PILLAI

S. C.

, KELLY

J. M.

, MCCORMACK

D. E.

, O'BRIEN

and RAMESH

: J. Mater. Chem., 2003, 13, 2586–2590.

PUYANE

, TOAL

and HAMPSHIRE

J. Sol Gel Sci Technol, 1996, 6, 219–225.

WESTIN

, EKSTRAND

, NYGREN

, OSTERLUND

and MERKELBACH

: J. Mater. Chem, 1994, 4, 615–621.

K. X.

, YIN

, DE

T. M.

and JING

T. M.

: Mater. Res. Bull., 1998, 33, 1703–1708.

10.

VISWANATH

R. N.

, RAMASAMY

, RAMAMOORTHY

, JAYAVEL

and NAGARAJAN

: Nanostruct. Mater., 1995, 6, 993–996.

11.

HISHITA

YAO

and SHIRASAKI

S-I.

: J. Am. Ceram. Soc., 1989, 72, 338–340.

12.

HINGORANI

, PILLAI

, KUMAR

, MULTANI

M. S.

and SHAH

D. O.

: Mat. Res. Bull, 1993, 28, 1303–1310.

13.

LIN

, ZHANG

, TANG

, YUAN

and LI

: Adv. Mater. Opt. Electron., 1999, 9, 205.

14.

SHEN

R. J.

, JIA

D. Z.

, DIM

Y. M.

and WANG

J. Y.

J. Inorg. Mater., 2001, 16, 625–629.

15.

WANG

, ZHANG

, YUAN

, YAN

and WANG

: Nanotechnology, 2003, 14, 11–15.

16.

WEST

A. R.

: ‘Solid state chemistry and its applications’ 174; 1984, London, John Wiley & Sons.

17.

GUO

, XU

, wu

and SIMON

: J. Mater. Chem., 2003, 13, 754–757.

18.

INADA

: Jpn. J. Appl. Phys., 1980, 19, 409–419.

19.

C.-H.

, CHYI

, WONG

H.-W.

and HWANG

W.-J.

: Mater. Chem. Phys., 2000, 62, 164–168.

20.

SAUSA

V. C. DE

, MORELLI

M. R.

, KIMINAMI

R. H. G. A.

and M. S. cAsHzo: J. Mater. Sci Mater. Electron., 2002, 13, 319–325.

21.

BANARJEE

, RAMMOHAN

T. R.

and PATNI

M. J.

: Mater. Res. Bull, 2001, 36, 1259–1267.

22.

AGARWAL

and SPEYER

R. F.

: J. Mater. Res., 1997, 12, 2447–2454.

23.

DURAN

, CAPEL

, TARTAJ

and MOURE

: J. EUr. CCMM. Soc., 2002, 22, 67–77.

24.

HINGORANI

, SHAH

D. O.

and MULTANI

M. S.

: J. Mater. Res., 1995, 10, 461–467.

25.

PILLAI

S. C.

, KELLY

J. M.

, MCCORMACK

D. E.

and RAMESH

: J. Mater. Client, 2004, 14, 1572–1578.

26.

CHEN

I. W.

and WANG

X.-H.

: Nature, 2000, 404, 168–171.

27.

DURAN

, CAPEL

, TARTAJ

and mouRE

J. AM. Cerallt Soc., 2001, 84, 1661–1668.

28.

BINNER

J. G. P.

, CARO

and FIRKINS

: J. Microw. Power Electromagn. Energy, 1999, 34, 131–136.