Fracture toughness of selectively reinforced Al2124 alloy: Precrack tip in the aluminium alloy side

Abstract

The fracture toughness of Al2124/Al2124+SiC bimaterials is affected by thermal residual stresses, elastic/plastic mismatch, precrack tip position, and failure mechanism. When the precrack tip is in the Al2124 side, final catastrophic failure occurs when ductile fracture of the Al2124 layer between the precrack tip and the composite side takes place, followed by fracture of the composite layer. For a precrack tip 2·0 mm from the interface, K _Q(5%) values are lower than the ‘Al2124 only’ value due to the near crack tip tensile residual stresses and higher stress triaxiality within the Al alloy ligament. At 0·5 mm from the interface, K _Q(5%) values increase and are usually as high as the ‘Al2124 only’ value due to the stronger shielding of the elastic/plastic mismatch. If the precrack tip is 2·0 mm from the interface, K _crit values of the bimaterial are higher than the ‘Al2124 only’ value and this is deduced to be due to the elastic/plastic mismatch shielding. At 0·5 mm from the interface, K _crit values are reduced because both the near tip tensile residual stress is higher and stress triaxiality levels of the ductile ligament are higher, although the elastic/plastic mismatch shielding is also higher at this position.