Abstract
The superplastic properties and microstructure evolution of a 0.15%Zr and 0.7%Cu modified 6061 aluminium alloy were examined in tension at temperatures ranging from 475 to 600°C and strain rates ranging from 7 × 10-6 to 2.8 × 10-2 s-1. The refined microstructure with an average grain size of about 11 μm was produced in thin sheets by a commercially viable thermomechanical process. It was shown that the modified 6061 alloy exhibits a moderate superplastic elongation of 580% in the entirely solid state at 570°C and ϵ = 2.8 × 10-4 s-1. Superior superplastic properties (elongation to failure of 1300% with a corresponding strain rate sensitivity coefficient m of about 0.65) were found at the same strain rate and a temperature of 590°C, which is higher than the incipient melting point of the 6061 alloy (∼575°C). The microstructural evolution during superplastic deformation of the 6061 alloy has been studied quantitatively. The presence of a slight amount of liquid phase greatly promotes the superplastic properties of the 6061 alloy, reducing the cavitation level.
Get full access to this article
View all access options for this article.