Mn was introduced, with graphite, as fine ferromanganese particles to form compacts of Fe–3%Mn–0·5%C. Each was sintered in dry 25%H2 + 75%N2 for 3 min at 770, 1040, 1080, 1170 and 1220°C respectively, held for 3 min and quenched. The surface of a successively heated specimen was similarly examined. Specimens were sectioned and, especially the reacting ferromanganese particles and adjoining regions, investigated using light and scanning electron microscopy and EDX. Development of microstructure and microcompositions during sintering was related, from 740°C, to diffusion and condensation of Mn vapour on iron particle surfaces and subsequent chemical reactions. Above 1080°C microstructures included features resulting from a transient liquid phase, in accord with a ∼45 wt%Mn ternary eutectic calculated by ThermoCalc. The thicknesses of the highly Mn enriched regions were substantially higher than those resulting from bulk Mn diffusion in the Fe lattice; our interpretation invokes predominant operation of another type of mechanism: diffusion induced grain boundary migration.
ZapfG., HoffmannG. and DalalK.: Arch Eisenhiittenwes., 1975, 46, (4), 287–294.
2.
alakA.: Powder Metall Int., 1980, 2, 72–75.
3.
KleinA. N., OberackerR. and ThiimmlerF.: Powder Metall. Int., 1985, 7, 13-16/71–74.
4.
CaminhaI. M. V. and Risso AssuncaoF. C.: Proc. World Conf. on ‘Powder metallurgy’, London, UK, July 1990, The Institute of Metals, Vol. 3, 94-98.
5.
OberackerR.: Powder Metall Int., 1990, 22, 54–60.
6.
SchaefflerD. J., LawleyA. and CaustonR. J.: in ‘Advances in powder metallurgy & particulate materials’, (ed.CapusJ. M. and GermanR. M.), Vol. 5 (P/M Steels), 93-106; 1992, Princeton, NJ, MPIF.
7.
DanningerH., PötschancherR., JanggG., J. Seykammer and A. S'alak: Proc. World Cong. on ‘Powder metallurgy’, Paris, France, June 1994, Societe Francaise de Métallurgie et Matériaux, EPMA, SF2M, Vol. II, 879–882.
8.
ShivanathR., JonesP. K. and LawcockR.: ‘Advances in powder metallurgy & particulate materials’, (ed.CadleT. and NarasimhanS.), Vol. 4, 13-427/13-437; 1996, Princeton, NJ, MPIF.
9.
JonesP. K., GoderoderK. B., LawcockR. and ShivanathR.: ‘Advances in powder metallurgy & particulate materials’, Vol. 4, 13–439; 1996, Princeton, NJ, MPIF.
10.
CiasA., MitchellS. C. and WronskiA. S.: Proc. World Cong. on ‘Powder metallurgy’, Granada, Spain, Shrewsbury, October 1998, EPMA, Vol. 3, 179-184.
11.
CiasA., MitchellS. C. and WronskiA. S.: Powder Metall., 1999, 42, 227–233.
12.
WronskiA. S., CiasA., BarczyP. and StoytchevM.: ‘Tough, fatigue and wear resistant sintered gear wheels’, Final Report on EU Copernicus Contract CIPA CT-94-0108, Brussels, European Commission, 1998.
13.
MitchellS. C.: ‘The development of powder metallurgy manganese containing low-alloy steels’, PhD thesis, University of Bradford, Bradford, UK, 2000.
14.
MitchellS. C., WronskiA. S. and CiasA.: hdynieria Mater., 2001, XX1I, 633–646.
15.
CiasA., StoytchevM., MitchellS. C. and WronskiA. S.: ‘Advances in powder metallurgy & particulate materials’, Part 10, 131-141; 2001, Princeton, NJ, MPIF.
MitchellS. C., StoytchevM. and SeleckaM.: ‘Development of powder metallurgy manganese steels for structural components’, Final report on NATO Project ‘Science for Peace’, PN 972395, Brussels, 2003.
18.
DudrováE.., M. Kabetove, R. BidulskS7 and A. S. Wronski: Powder Metall., 2004, 47, 181–190.
MitchellS. C. and CiasA.: Powder Metall Prog., 2004, 4, (3), 132–142.
21.
SainzS., MartinezV., DouganM., BaumgaertnerF. and CastroF.: Proc. ‘Advances in powder metallurgy & particulate materials’, San Diego, CA, June 2006, MPIF, APMI, 624-637.
22.
LippK.: ‘HIGHPER-PM: design concepts for economic high-performance structural powder metallurgy components’, Final Technical Report on Contract no. G5RD-CT-2001-00531. Project no. GRD2-2000-30148 under the ‘Competitive and sustainable growth’ Programme (1998-2002) of the European Community, November 7 2007.
23.
HryhaE. and DudrováE..: Mater. Sci. Forum, 2007, 534–536, 761–764.
24.
DanningerH. and Ch. Gierl: Met. Chem. Phys., 2001, 67, 49–55.
25.
MitchellS. C. and BaumgaertnerF.: Proc. ‘Deformation and Fracture in Structural PM Materials, DFPM 2005’, 27-30 September 2005, Stare. Lesná., Slovakia, Edited by L. Parilál and H. Danninger, 11-18.
26.
MitchellS. C. and BaumgaertnerF.: Powder Metall Prog., 2005, 5, 234–242.
27.
SarasolaM., Gemez-AceboT. and CastroF.: Proc. Eur. Cong. on ‘Powder metallurgy’, Nice, France, October 2001, EPMA, 266-271.
28.
S&aposA.;alak: Sci. Sinter., 1989, 3, 145–154.
29.
S&aposA.;alak: Metall Mater., 1989, 27, 159–170.
30.
NavaraE.: Proc. 6th Int. Conf. on. ‘Powder metallurgy’, Brno, Czech, October 1982, EMPA, Vol. 1, 143-154.
31.
HillertM. and PurdyG. R.: Acta Metall., 1978, 26, 333–340.
32.
ChongmoLi and HillertM.: ActaMetall, 1981, 29, 1949-1960.
33.
HillertM. and Li Chongmo: Scand. J. Met., 1981, 10, 171.