In this study, an attempt has been made to synthesis Mo–Si–B nanocomposite alloys using a combination of mechanical alloying (MA) and heat treatment in various primary elemental compositions. For this purpose, Mo–14Si–10B, Mo–57Si–10B and Mo–47Si–23B (at.‐%) elemental powders were separately milled using an attritor mill. Mechanically alloyed (MAed) powders were annealed in an atmosphere controlled furnace under constant temperature for 10 h. Metallurgical characteristics of MAed and/or annealed powders were evaluated by atomic absorption spectrometry, SEM, TEM and X‐ray diffraction. The results did not show any formation of related intermetallics after MA. However, MoSi2, Mo5Si3, Mo5SiB2, MoB and Mo were successfully formed, when the MAed Mo–57Si–10B powders were subjected to annealing at a high temperature.
KrakhmalevPV: ‘Preparation of Mo(Si,Al) 2–ZrO2 nanocomposite powders by mechanical alloying’, Int. J. Refract. Met. Hard Mater., 2004, 22, 205–209.
3.
LiZ, PengLM: ‘Ultra-high temperature Mo–Si–B alloys – synthesis, microstructural and mechanical characterization’, Mater. Lett., 2008, 62, 2229–2232.
4.
JehannoP, HeilmaierM, SaageH, HeyseH, BoningM, KestlerH, SchneibelJH: ‘Superplasticity of a multiphase refractory Mo–Si–B alloy’, Scr. Mater., 2006, 55, 525–528.
5.
JehannoP, HeilmaierM, KestlerH: ‘Characterization of an industrially processed Mo-based silicide alloy’, Intermetallics, 2004, 12, 1005–1009.
6.
KuznetsovSA, RebrovEV, MiesMJM, de CroonMHJM, SchoutenJC: ‘Synthesis of protective Mo–Si–B coatings in molten salts and their oxidation behaviour in an air-water mixture’, Surf. Coat. Technol., 2006, 201, 971–978.
7.
JainP, AlurAP, KumarKS: ‘High temperature compressive flow behaviour of a Mo–Si–B solid solution alloy’, Scr. Mater., 2006, 54, 13–17.
8.
YamauchiA, YoshimiK, KurokawaK, HanadaS: ‘Synthesis of Mo–Si–B in situ composites by mechanical alloying’, J. Alloys Compd, 2007, 434–435, 420–423.
9.
MitraR, SrivastavaAK, PrasadNE, KumariS: ‘Microstructure and mechanical behaviour of reaction hot pressed multiphase Mo–Si–B and Mo–Si–B–Al intermetallic alloys’, Intermetallics, 2006, 14, 1461–1471.
10.
PaswanS, MitraR, RoySK: ‘Isothermal oxidation behaviour of Mo–Si–B and Mo–Si–B–Al alloys in the temperature range of 400–800°C’, Mater. Sci. Eng. A, 2006, A424, 251–265.
11.
SakidjaR, ParkJS, HamannJ, PerepezkoJH: ‘Synthesis of oxidation resistant silicide coatings on Mo–Si–B alloys’, Scr. Mater., 2005, 53, 723–728.
12.
AlurAP, KumarKS: ‘Monotonic and cyclic crack growth response of a Mo–Si–B alloy’, Acta Mater., 2006, 54, 385–400.
FanX, IshigakiT: ‘Mo5Si3–B and MoSi2 deposits fabricated by radio frequency induction plasma spraying’, J. Therm. Spray Technol., 2001, 10, (4), 611–617.
15.
FanX, IshigakiT: ‘Mo5Si3-boron composites fabricated by induction plasma deposition and their high-temperature oxidation resistance’, J. Am. Ceram. Soc., 1999, 82, (8), 1965–1968.
16.
KangP, YinZ: ‘Phase formation during annealing as-milled powders of molybdenum disilicide’, Mater. Lett., 2003, 57, 4412–4417.
17.
ZhangH, LiuX: ‘Analysis of milling energy in synthesis and formation mechanisms of molybdenum disilicide by mechanical alloying’, I. J. Refractory Metals & Hard Materials, 2001, 19, 203–208.
18.
ZuoK, XiS, ZhouJ: ‘Structure evolution and thermodynamics analysis of MoSi2 during mechanical alloying’, Mater. Sci. Eng. A, 2007, A445–A446, 48–53.
19.
KangPC, YinZD: ‘Formation mechanism and nanocrystalline phase transformation of molybdenum disilicide by mechanical alloying’, Nanotechnology, 2004, 15, 851–855.
20.
NowotnyH, DimakopoulouE, KudielkaH: ‘Untersuchungen in den dreistoffsystemen: molybdan–silizium–bor, wolfram–silizium–bor und in dem system: VSi2–TaSi2’, Chem. Mon., 1957, 88, 180–192.
21.
StruttPR, KearBH, BolandRF: ‘Method of manufacture of nanostructured feeds’, US patent no. 6025034, 2000.
22.
BakhshiSR, SalehiM, EdrisH, BorhaniGH: ‘Structural evaluation of Mo–Si–B multiphase alloy during mechanical alloying and heat treatment’, Powder Metall., 2008, 51, (2), 119–124.
23.
ZhangDL: ‘Phase formation during mechanical alloying of Mo and Si powders’, J. Mater. Sci. Lett., 1995, 14, 1508–1511.