Abstract
The effects of metallurgical condition, stress level and applied polarisation potentials on the cracking of 410 stainless steel in boiling sodium sulphide solution have been investigated. The dead load technique was applied. The results indicated that failure mechanism involves both active path corrosion and hydrogen embrittlement depending on thepolarisation potential applied.
Get full access to this article
View all access options for this article.
References
1.Report of Technical Practices Committee 1-G , Corrosion , 1952 , 8, 351
2.
Schuetz
A. E.
, &
Robertson
W. D.
ibid. , 1957 , 13 , 437f
3.
Baldy
M. F.
, ibid. , 1961 , 17 , 509t
4.
Burns
D.
, Mater. Perf. , 1976 , 15 , 21
5.
Lyle
F. F.
, &
Norris
E. B.
Corrosion , 1978 , 34 , 193
6.
Hudgins
C. M.
,
McGlasson
R. I.
,
Mehdizadeh
P.
, &
Rosborough
W. M.
ibid. , 1966 , 22 , 238
7.
Phelps
E. H.
, ‘Fundamental Aspects of Stress Corrosion Cracking’ , Proc. Natn. Ass. Corros. Engrs., Houston, TX , 1969 , p. 398
8.
Greer
J. B.
, Mater. Perf. , 1975 , 14 , 11
9.
Fraser
J. P.
, &
Treseder
R. S.
Corrosion , 1952 , 8 , 342
10.
Dvoracek
L. M.
, Mater. Perf :, 1976 , 15 , 9
11.
Kane
R. D.
,
Watkins
M.
, &
Greer
J. B.
Corrosion , 1977 , 33 , 231
12.
Kane
R. D.
,
Watkins
M.
,
Jacobs
D. F.
, &
Hancock
G. L.
ibid. , 1977 , 33 , 309
13.
Gouda
V. K.
, El-Sayed, H., Staehle, R. W., & Begley, J. A., Proc. 7th Int. Congr. metallic Corros., Rio de Janeiro , 1978 , p. 724
14.
El-Sayed
H.
A., El-Sobki, K. M., & Gouda, V. K. , Surf. Technol. , 1981 , 14 , 245
15.
Gouda
V. K.
, & El-Sayed, H. A. , ibid. , 1983 , 18 , 327
16.
Lillys
P.
, &
Nehrenberg
A. E.
Trans. Am. Soc. Met. , 1956 , 48, 327
17.
Parkins
R. N.
, Br. Corros. J. , 1972 , 7 , 15
18.
Pourbaix
M.
, ‘Atlas of Electrochemical Equilibria in Aqueous Solutions’ 1966 (New York : Pergamon )
19.
Uhlig
H. H.
, Mater. Perf , 1976 , 16 , 22
20.
Hoke
J. H.
, Corrosion , 1968 , 24 , 429
21.
Ladley
R. S.
, ibid. , 1960 , 16 , 539
22.
Snape
E.
, ibid. , 1967 , 23 , 157
23.
Greer
J. B.
,
Von Rosenberg
E. L.
& Martinez, J. , ibid. , 1972 , 28 , 378
24.
Yangchu
W.
,
Qun
Li
Sh., Mei Haiao, Ch. , & Zuor Tien, J. , ibid. , 1980 , 36 , 475
25.
Vollmer
L. W.
, ibid. , 1952 , 8 , 326
26.
Bloom
F. K.
, ibid. , 1955 , 11 , 351
27.
Warren
D.
, &
Beckman
G. W.
ibid. , 1957 , 13, 631