Abstract
Localised corrosion leading to fatigue cracks occurred preferentially round certain ‘active’ inclusions; these contained Mn and S, and sometimes, Fe and Si.
Get full access to this article
View all access options for this article.
References
1.
Smialoswki
M.
, Szklarska-Smialowska, Z., Rychcik, M., & Szummer, A. , Corros. Sci. , 1969 , 9, 123
2.
Wranglén
G.
, ibid. , 1969 , 9 , 585
3.
Szklarska-Smialowska
Z.
,
Szummer
A.
& Zanik-Czachor, M. , Br. Corros. J. , 1970 , 5, 159
4.
Janik-Czachor
M.
,
Szummer
A.
& Szklarska-Smialowska, Z. , ibid. , 1972 , 7 , 90
5.
Szklarska-Smialowska
Z.
, Corrosion , 1972 , 28 , 388
6.
Szummer
A.
, & Janik-Czachor, M. , Br. Corros. J. , 1974 , 9, 216
7.
Wranglén
G.
, Corros. Sc. , 1974 , 14 , 331
8.
Wallwork
G. R.
, &
Harris
B.
Localised Corrosion’, NA CE–3, 292
9.
Wranglén
G.
, ibid. , 1974 , NACE-3 , 462
10.
Gainer
L. J.
, &
Wallwork
G. R.
Corrosion , 1979 , 35 , 435
11.
Scotto
V.
,
Ventura
G.
, &
Traverso
E.
Corros. Sc. , 1979 , 19 , 237
12.
Parker
J. G.
, Br. Corros. J. , 1973 , 8 , 125
13.
Ray
G. P.
, Trans. Inst. Met. Finish. , 1978 , 56 , 168