Survey of the Scientific,Technical and Educational Activities in the Field of Corrosion of the Member Countries of the European Federation of Corrosion in 1976
Restricted accessResearch articleFirst published online January, 1977
Survey of the Scientific,Technical and Educational Activities in the Field of Corrosion of the Member Countries of the European Federation of Corrosion in 1976
This report gives a survey of the activities in the field of corrosion in 1976 of Belgium, France, Germany, Hungary, Italy, the Netherlands, the Scandinavian countries, Switzerland and the UK. The material is classified under: Corrosion properties of metals, corrosive media, types of corrosion, corrosion prevention, special applications, test and measurement technology, information and education, economic aspects.
Get full access to this article
View all access options for this article.
References
1.
TrasattiS., The work function in electrochemistry, Adv. Electro-chem., 1976, 10–233–321
2.
FrieheW., Einfluss höherer Aluminiumgehalte in Stählen auf das Korrosionsverhalten in Meerwasser, Stahl Eisen, 1976, 96, 567
3.
BöhniH., Das Korrosionsverhalten von Stahl im Bauwesen. Vortrag LKI Kolloquium, T. U. München, November1976
4.
TrumanJ. E., Corrosion resistance of 13% chromium steels as influenced by tempering treatment, Br. Corros. J., 1976, 11–92
5.
EvansT. E., Film formation on stainless steel in a solution con-taining chromic and sulphuric acids, Corros. Sc., 1977, 17, 105
6.
BrennenS., Influence of sulphur and molybdenum on pitting of stainless steel in chloride solutions. Report No.1977: 9, Swedish Corrosion Institute
7.
SiiryP., On the behaviour of stainless steel strip-claddings with respect to intergranular corrosion, Mater. Chemisny, 1976, 1, 151
8.
ErasE., & AltorterH., Fin Korrosionsprodukt von Aluminium in was serigen Lösungen von Ammoniak und Kohlensiure. Vortrag EFK, Budapest, November1976
9.
GrauerR., & SchmokerP., Die Oxydation von Al—Mg—Legierungen in Sauerstoff bei erhöhter Temperatur, Werkstoffe Korros., 1976, 27, 769
10.
GrauerR., SchmokerP., & WiedmerE., Kinetische und motphologische Untersuchen ilber den Einfluss von Beryllium auf das Oxydationsverhalten von Al—Mg—Legierungen. Vortrag Dechema Fachausschuss ‘Anorganische überztige’, Frankfurt1976
11.
van de YenE. P.G. T., & Koelmans, H., The cathodic corrosion of aluminium, J. electrochem. Soc., 1976, 123, 143
12.
DattaM., & LandoltD.Film breakdown studies on nickel in nitrate electrolytes under ECM conditions. 27th I.S.E. Meeting, Zurich, September1976
13.
KellyJ. J., The influence of fluoride ions on the ‘passive’ dis-solution of Ti in concentrated H2SO4 solution, ibid., September1976
14.
SiiryP., & Semlitsch., M., Geftigeaufbau und Korrosionseigen-schaften von Co-Basislegierungen fiir künstliche Gelenke. Sonderband 6, Praktische Metallographie, 1976, p. 707
15.
SiiryP., & HiltbrunnerK., A comparative study of the corrosion rates of massive Mo and flame-sprayed Mo coatings in aqueous solutions. 27th I.S.E. Meeting, Zürich, September1976
16.
van MuylderJ., & Pourbaix, M., Influence de facteurs clirnatiques et polluants sur la corrosion atmospherique de l'acier. CEBELCOR Rapports Techniques, Vol. 130, December1976
17.
de JongH. F., Investigation of the influence of atmospheric exposure on the mechanical properties of A1-2024T3 and Al-7075T6 sheet with various surface treatments. Report VTH-210. Dept of Aerospace Engineering, Delft University of Technology, 1976
18.
UsselingF. P., & KrougmanJ. M., The corrosion behaviour of CuNil0Fe in sea water, Proc. 4th Int. Congr. mar. Corros. Fouling, Juan-les-Pins, 1976, pp. 285–295
19.
KolsterB. H., RademakersP. L. F., Burggraf, J., & Pfitzschke, M., Development of modified Cunifer alloys, 5th Int. Symp. Fresh Water from the Sea. Alghero, Sardinia, May, 1976, Vol. I, pp. 403–421
20.
SandegrenE., Korrosion pa stilstänger i olika jordar. Bull.No. 74. Swedish Corrosion Institute
21.
GibbsG. B, & Hales, R., The influence of metal lattice vacancies on the oxidation of high temperature materials, Corros. Sci., 1977, 17, 487
22.
LloydG.0., Saunders, S. R. J., Kent, B., & Furey, A„ Breakaway oxidation of Fe-10%Cr and Fe-20%Cr at temperatures up to 600°c, ibid., 1977, 17, 269
23.
BastowB. D., WhittleD. P., & WoodG. C., Diffusion controlled growth of solid solution scales on nickel—cobalt alloys, ibid., 1976, 16, 57
24.
El-DahshanJ. M., Whittle, D. P., & Stringer, J., The oxidation of cobalt—tungsten, nickel—tungsten alloys, ibid., 1976, 16, 77
25.
WildR. K., High temperature oxidation of austenitic stainless steel in low oxygen pressure, ibid., 1977, 17, 87
26.
FlowerH. M., & WilcoxB. A., In situ oxidation of Ni-30 wt-% Cr and TD NiCr in the high voltage electron microscope, ibid., 1977, 17–253
27.
CastleJ. E., & HuntM. R., In situ oxidation of iron and steel in the scanning electron microscope, ibid., 1976, 16, 137
28.
ScharwächterR., & Wilms, V., Entwicklung und Erprobung neuer durch Plasmaspritzen in Vakuum aufgebrachter Schutzschichten-systeme gegen Hochtemperaturkorrosion fiir Gasturbinenwerk-stoffe. Tagungshandbuch Symposium ‘Korrosionsforschung fiir die Praxis’. Braunlage1977, Proj. No. 0–4•511; 4.5/1
Development of facilities for the testing of protective coatings for jet engine components. Memo SL-77-107 National Aerospace Lab., NLR
31.
SchwenkW., Elektrochemische Untersuchungen zur Hochtem-peraturkorrosion von 18/10 Chrom—Nickel—Stahl. Tagungshand-buch Symposium ‘Korrosionsforschung fiir die Praxis’, Braunlage1977, Proj.No. 4. 1/1
32.
Proc. 2nd Int. ILZRO Galvanising Seminar. St. Louis, 1976
33.
SasseJ., Untersuchen iiber den Einfluss des Zinks und seiner Legierungselemente auf die Rissbildung von Stählen in Zink-schmelzen. Tagungshandbuch Symposium ‘Korrosionsforschung flir die Praxis’, Braunlage1977, Proj. No. 10–1/1
34.
FrieheW., Ermittlung der Ursachen rissbedingter Wanddurch-brilche an Schmelzkesseln aus Stahl ftir die Feuerverzinkung und Bleientsilberung, ibid., Proj. No. 0–10.2/1
35.
PetterF., Entwicklung einer Innenbeschichtung fiir Feuer-verzinkungskessel, ibid., Proj. No. 0-10- 2/2
36.
PohlmanR., Ultraschallmaterialpriifung innerhalb von flüssigen Metallen, ibid., Proj. No. 0–10. 3/1; 10. 3/1
37.
KolsterB. H., Mechanism of Fe- and Cr-transport by liquid sodium in non-isothermal loop systems, J. nucl. Mater., 1975, 55, 155
38.
KolsterB. H., & BosL., Corrosion, transport and deposition of stainless steel in liquid sodium, Proc. Int. Conf. Liquid Metal Technol. in Energy Production, Seven Springs, USA, 1976
39.
GräfenH., Wasserstoffversprödung von Feinkornstählen in Abhängigkeit von der Legierungszusammensetzung der Geftigeaus-bildung und der mechanischen Belastung. Tagungshandbuch Symposium ‘Korrosionsforschung far die Praxis’, Braunlage1977, Proj.No. 1. 1/1
40.
VibransR. C., Bruchaussehen und Bruchverhalten bei Wasser-stoffversprodung von Stahl., ibid., Proj.No. 1.1/6
41.
BauerE.Wasserstoffdiffusion durch Titan und -Legierungen, ibid., Proj.No. 1.1/1
42.
FranzJ, & Vibrans G., Versprficlung von Stahl durch Schwefel-wasserstoff, Werkstoffe Karros., 1976, 27, 237
43.
SiiryP., Similarities in the corrosion behaviour of iron, cobalt and nickel in acid solutions. A review with special reference to sulphide adsorption, Corros. Set., 1976, 16, 879
44.
LernkowitzS. M., VerhulstP., SchultzeW., A., Cohn, P. F., & van der Berg, P. J., Corrosion of alloys in gaseous ammonia—carbon dioxide—water mixtures in the conditions of the hot gas recirculation process for the synthesis of urea. To be published
45.
VoggH., & Vehlow, J„ Ermittlung der Korrosionsgeschwindig-keiten von hochlegierten Stählen und Hastelloy C in wasserfreien und wasserhalti gen Carbonsäuren. Tagungshandbuch Symposium ‘Korrosionsforschung ftir die Praxis’, Braunlage1977, Proj.No. 6. 1/1
46.
GearH., Kinetische Untersuchungen der durch Deckschichten beeinflussten Korrosionsprozesse an Metallen in niederen Carbon-säuren tnittels Impedanzspektren, ibid., Proj. No. 64/2
47.
HeitzE., Korrosion von Metallen in Halogenkohlenwasserstoffen, ibid., Proj.No. 6.3/1
48.
DeuchlerW., Korrosionsverhalten von unliegierten und Miter-legierten Stählen in Chlorkohlenstoff- und Chlorkohlenwasserstoffver-bindungen, ibid., Proj. No. 0–6.3/1
49.
GruhlW., Korrosionsuntersuchungen an ausgewählten Halogen-kohlenwasserstoffen, ibid., Proj.No. 6.3/1
50.
MogensenM., MaahnE., & Bech-Nielsen, G., Theory for the SCC of ductile iron alloys based on a model for the anodic dissolution reactions of pure iron, Br. COMOS. J., 1976, 11, 181
51.
LudvigsenP. B., & ArupH., SCC of mild steel in ammonia vapour above liquid ammonia, Corrosion, 1976, 32–430
52.
HewittP., & HockenhullB. S., The effect of microstructures on the SCC susceptibility of a 13% Cr martensitic stainless steel, Corros. Set., 1976, 16–47
53.
TrabanelliG., Application of electrochemical techniques in studying SCC inhibition. Rapports Techniques CEBELCOR 129. RT.234, 1976, pp. 94–100
54.
Microscopic study of SCC growth in an AlZnMg alloy. National Aerospace Lab., NLR MP77004U
55.
Heat treatment effects on SCC resistance of AlZnMg type forged materials, ibid., TR76008U
56.
The mechanism of SCC in AlZnMg alloy plate, ibid., TR76042U
57.
GrzembaB., & GruhlW., Interkristalline Rissneigung und Span-nungsrisskorrosionsverhalten von Al ZnMg-Legierungen, Metal!., 1976, 46–521
58.
ScamansG. M., AlaniR., & SwannP. R., Pre-exposure embritdement and stress corrosion failure in AlZnMg alloys, Corros. Set., 1976, 16–443
59.
WeberJ., & SiiryP., Intergranular SCC of Ni alloys in pressurised water, Mater. Perf, 1976 (Feb.), 34
60.
ArmstrongR. D., & CaitesA. C., A correlation between electro-chemical parameters and corrosion cracking, Corros. Set., 1976, 16, 423
61.
BuhlH., Prüfung der ‘Constant-Straining Method’ auf ihre Aus-sagefihigkeit in der Anwendungsorientierten Spannungskorrosion-prüfung. Tagungshandbuch Symposium ‘Korrosionsforschung ftir die Praxis’, Braunlage1977, Proj. No. 2. 1/2
62.
MomA. J. A., DencherR. T., van der WekkenC. J., & SchultzeW. A., Some aspects of the SC testing of austenitic, martensitic, ferritic-austenitic, and ferritic types of stainless steel by means of the ‘Constant Strain Rate’ method. Lecture: Strain Rate Meeting, Newcastle upon Tyne, 1977
63.
de JongH. F., The Constant Strain Rate method: A useful method for testing SCC. Report VTH-214. Dept of Aerospace Engineering, Delft University of Technology, 1976
64.
KaescheH., Spannungsrisskorrosion der Metalle-Ergebnisse und Probleme der Forschung, Z. Metallk., 1976, 67, 439
65.
BlundyR. F., & ShreirL. L., The effect of pressure on the permeation of hydrogen through steel, Corros. Sc., 1977, 17, 509
66.
van LeeuwenH. P., A quantitative analysis of hydrogen-induced cracking.Thesis, Delft University of Technology, 1976
67.
SmithC. J. E., & HughesA. N., Construction and operation of a multi-specimen rotating bending corrosion fatigue machine, Br. Corros. J., 1976, 11, 12
68.
SchwenkW.Potentialabhängigkeit der Schwingungsriss-korrosion von h6herfestem Stahl in Salzwasser. Tagungshandbuch Symposium ‘I (orrosionsforschung fir die Praxis’, Braunlage1977, Proj. No. 24/7
69.
EffertzP. H., HagenL., & F orchhammer, P., Untersuchung des S chwingungsrisskorrosionsverhaltens von Turbinebaustählen bei beginnender Dampfnksse, ibid., Proj.No. 2.4/2
70.
DetertK., Kurzzeituntersuchungen zur Auswahl von rost-beständigen Cr-Stählen mit verbessertem Widerstand gegen Schwin-gungsrisskorrosion, ibid., Proj.No. 14/3
71.
Schmitt-ThomasKh.BildungskinetikG.von Deckschichten und Schwingungsrisskorrosionsverhalten ferritischer C hromstähle in Abhängigkeit von Gefügezustand und Molybdänzusatz in chlorid-haltigen A ngriffsmitteln, ibid., Proj. No. 2.4/5
72.
Schmitt-ThomasK h. G., & LeidigA., Schwingungsrisskorrosion an Zugstäben aus einer Ni-Co-B asislegierung in chloridhaltigen Medien bei 200°c, Werkstoffe Korros., 1976, 27, 486
73.
Environmental effects on fatigue crack growth in AlCuMg and AlZnMg sheet material. National Aerospace Lab., NLR TR76104U
74.
V ogelesang, L. B., Some aspects of the environmental effect on the fatigue mechanism of a high strength Al alloy. Report VTH -200, Dept of Aerospace Engineering, Delft University of Technology, 1976
75.
SchijveJ., & ArkemaW. J., Crack closure and the environ-mental effect on fatigue crack growth. Report VTH-217, ibid.
76.
RowlandJ. C., Crevice corrosion of stainless steels and nickel alloys under marine conditions, Br. Corros. J., 1976, 11, 195
77.
KrougmanJ. M., & UsselingF. P., Crevice corrosion of austenitic stainless steel X3CrNilMoN 17/13/5 in sea water, Proc. 4th Int. Congr. mar. Corros. Fouling. Juan-leg-Pins, 1976, pp. 285–295
78.
HeitzE., Mechanismus der Erosionskorrosion von unlegierten und legierten Eisenwerkstoffen in Wässern hoher Str6mungsge-schwindigkeit. Tagungshandbuch Symposium ‘K orrosionsforschung fur die Praxis’, Braunlage1977, Proj.No. 3. 4/1
79.
MollenkopfG., Praxisnahe Prilfung von korrosions- und erosions-b eständig en Pumpenwerkstoffen, ibid., Proj.No. 3. 4/ 213
80.
WeberJ., Entwicklung einer hochgeschwindigkeits-Strömungs-machine für/und Untersuchung des Einflusses der Strómungsge-schwindigkeit von Meerwasser auf das Korrosionsverhalten von metallischen Werkstoffen, ibid., Proj. No. 0–3.4/4
81.
WeberJ., Einfluss der Strömungsgeschwindigkeit von feststoff-haltigen neutralen Wassern auf das Korrosionsverhalten von Metallen, ibid., Proj. No. 0–3.4/5
82.
GI-WenH., Horn, E.-M., & Diekmann, H., Praxisnahe Prüfung von korrosions- und erosionsbeständigen Werkstoffen, ibid., Proj. No. 3. 4/2A
83.
PiniG. C., BachmannE., & OerkenyiG., Werkstoffprüfung bei hohen Strömungsgeschwindigkeiten, Werkstoffe Korros., 1976, 27, 693
84.
KingR. A., DittmerC. K., & MillerJ. D. A., Effect of ferrous ion concentration on the corrosion of iron in semicontinuous cultures of sulphate reducing bacteria, Br. Corros. J., 1976, 11, 105
85.
MayneJ. E.0., & Turgoose, S, Inhibition of the corrosion of iron by lead azelate. I. Uptake and distribution of azelate and lead ions, Br. Corros. J., 1976, 11–204
86.
PiniG. C., Dampfphaseninhibitoren gegen Korrosion von Fe-Werkstoffen, Maschinenmarkt, 1976, 82, 8
87.
PiniG. C., & WeberJ., Prilfung und Auswahl von K avitations-inhibitoren, Werkstoffe Korros., 1976, 27–6
88.
GräfenH., & Kuron, D., Einfluss der Rezeptur auf die Lebens-dauer von C hlor-K autschuk-B eschichtungen bei kathodischem K orrosionsschutz in Meerwasser. Tagungshandbuch Symposium ‘K orrosionsforschung für die Praxis’. Braunlage1977, Proj.No. 12. 4/1
89.
JostanJ. L., Korrosion und Korrosionsschutz bei gedruckten Schaltungen und anderen elektronischen Bauteilen und Systemen, ibid., Proj. No. 9- 1/1
90.
PiniG. C., & WeberJ., Abscheidung von B lei-Dispersions-überzüg en, Proc. 8th World Congress on Metal Finishing, Amsterdam, 1976
91.
JeneyI., Die Wirkung der Stromdichte und der C hloridkonzen-tration auf die Struktur des aus Sulfamat-Elektrolyten abgeschiedenen Nickels, Maschinenbautechnologie(H), No. 10, 1976
92.
JeneyI., The effect of superimposed alternating current on the hardness, internal stress, and texture of nickel deposited from sulphamate electrolytes, Trans. Inst. Metals, No. 1, 1976
93.
BodM., HalmayL., & KonczvaldA., Prilfung von Klorosiliiber-zilg en, Korrosionsbeobachter (IV, 1976, pp. 164–168
94.
Korrosionsskydd vid tillverkning av personbilar. Bull. No.80, Br. Corros. J., 1977, Vol. 12, No. 4 Swedish Corrosion Institute.
95.
LeideN. G., Ytbehandlung av fartygskrov-översikt av utfOrda undersökningar. Report No.1977: 7, Swedish Corrosion Institute
96.
AsherR. C., DaviesD., & BeerhamS. A., Some observations on the compatibility of structural materials with molten lead, Corros. Sci., 1977, 17–545
97.
C orrosione‘on load’ denneggiamento da idrageno e roture fragili nei generatori di vapore delle centrali termiche. Associazone Italiana di Metallurgia (AIM), M ilano, 1976
98.
SiiryP., Korrosionsprobleme in Dampferzeugern von Druck-wasserreaktoren, Kerntechnik, 1976, 18, 77
99.
Laszlo(Frau), SzabO, I., & Ratkovics, F., Prüfung von Kessel-korrosion, Energie und Atomtechnik (H), 1977, 30, No.1
100.
RatkovicsF., & SzaboI., V ersuche für Inhibitordosierung in Kesseln, ibid., 1977, 30, No.1
KruseC. L.’ Untersuchungen Ober das Korrosionsverhalten von metallischen Werkstoffen gegenilber Trinkwasser. Tagungshandbuch Symposium ‘Korrosionsforschung fur die Praxis’, Braunlage1977, Proj. No. 5. 2/1B
103.
BöhniH., Korrosionserscheinungen an metallischen Werk-stoffen, San-Inst., 1976, 54–41
104.
StickelW., Einfluss von Phosphaten undioder Silikaten auf die durch Kupferionen ausgelöste Lochkorrosion in verzinkten Warm-wasserrohren, ibid., Proj. No. 5.1/1
105.
SontheimerH., Einfluss natürlicher Wasserinhaltstoffe auf die Korrosion in Trinkwasserinstallationen, ibid., Proj.No. 5. 1/2
106.
WehleV., Einfluss von Phosphaten und/oder Silikaten auf das K orrosionsverhalten von Trinkwasser gegeniiber Installations-werkstoffen, ibid., Proj. No. 0–5. 1/3
107.
Erd6s, E.'M & Altorfer, H., E dem Malachit ähnliches basischesEisencarbonat als Korrosionsprodukt von Stahl, Werkstoffe Korros., 1976, 27, 304
108.
HeatonW. E., Impingement corrosion of condenser tubes, Br.Corros., J., 1977, 12, 15
109.
WeberJ., Problérnes de corrosion dans les condenseurs des installations frigorifiques et de climatisation, Me'taux, Ind. Corros., February1976
110.
Arbeitskreis ‘KiihImittelzusätze’, Untersuchung von KiihImittel-zusätze für die Kühlkreisläufe von Verbrennungsmotoren. Tagungs-handbuch Symposium ‘Korrosionsforschung für die Praxis’, Braunlage1977, Proj.No. 0-7-1/1
111.
SpeckhardtH., Untersuchungen der Wirksamkeit von Inhibitoren zur V erhinderung von Korrosion und Kavitation in geschlossenen Kühlwasserkreisläufen, ibid., Proj.No. 7. 1/1Risch., K. Untersuchung von Inhibierungsmöglichkeiten für Riickkiihlwasser, ibid., Proj. No. 0–1.3/2
112.
BodM., DócsJ., FeherI., HalmayL., & LukacsZ., K orrosionsschutz und thermische Isolierung von W armwasser-leitungen im B oden, Korrosionsbeobachter (H), 1976, pp. 152–157
113.
PiniG. C.& Baumgartner, H., K orrosionswiderstand von implantierten Hi;ftendprothesen bei Durchführung von Elektro-therapien, Mater. Chemistry, 1976, t, 2
114.
SilryP., K orrosionseigenschaften gegossener und geschmiedeter Werkstoffe für künstliche Gelenke, Medico, 1976, 6, 9
115.
HeitzE., & SchwenkW., Theoretical basis for the determina-tion of corrosion rates from polarisation resistance, Br. Corros. J., 1976, 11, 74: Werkstoffe Korros., 1976, 27, 241
116.
CallowL. M., RichardsonJ. A., & DawsonJ. L., Corrosion monitoring using polarisation resistance measurements, Br. Corros. J., 1976, 11, 123 and132
117.
C arre, G., Jordkorrosion-orsaker och mätmetoder. Bull.No. 83, Swedish C orrosion Institute
118.
SiiryZ., de AnnaP., & Joos, B., Polarisation resistance and corrosion of mild steel in aqueous sulphate/chloride solutions. 27th I.S.E. Meeting, Z Mich1976
119.
EistratK., & KuceraV., Korrosionsrisker i samband med brand i PVC -litteraturstudie och erfarenhetsinsamling. Report No.1977: 8, Swedish Corrosion Institute
120.
MayneJ. E.0., & Turgoose, S., Umschlagspunkt or Flade potential of iron, Br. Corros. J., 1976, 11, 140
121.
KuoH. C., & LandoltD., Galvanostatic transient study of anodic film formation on iron in concentrated chloride media, Corros. Sci., 1976, 16, 915
122.
WeberJ., Die elektrochemische Prüfung des K orrosions-verhaltens von galvanisch oder chemisch abgeschiedenen Metall-schichten, Oberildche-Surface, 1976, 3, 47
123.
MathieuJ. B., McClureD. E., MathieuH. J., & LandoltD., Application of Auger Electron Spectroscopy to the study of anodic films on titanium. 27th I.S.E. Meeting, Zürich1976
124.
CastleJ. E., EplerD. C., & PeplowD. B., ESCA investigation of iron-rich protective films on aluminium-brass condenser tubes, Corros. Sci., 1976, 16, 145
125.
Ion implantation and ion beam analysis techniques in corrosion studies, Corros. Sc., 1976, I6, Part10, pp. 110
126.
J ax, P., Untersuchungen ilber die Aussagefahigkeit der Schallemissionsanalyse bei der Feststellung und Lokalisierung von Risskorrosion in Behaltern und Rohrleitungen im Rahmen einer D ruck-probe. Tagungshandbuch Symposium ‘K orrosionsforschung für die Praxis’, Braunlage1977, Proj.No. 11. 2/3
127.
GellingsP. J., Introduction to Corrosion Prevention and Control for Engineers, Noordhoff, Rotterdam1976
128.
Survey of corrosion and protection in the UK. Report of the Committee on Corrosion and Protection. HMSO, London1971
129.
Material needs and the environment today and tomorrow. Final Report of National Commission on Materials Policy. Washington1973. Library Congr. Card No.73–600202
130.
WeberJ., Wirtschaftliche Bedeutung der K orrosion und des Korrosions-S chutzes, Schweizer Maschinenmarkt (Oberflahen-technik) 39 and 43(1976)