Cathodic protection requirements for high strength steel in sea water assessed by potentiostatic weight loss measurements

Abstract

A potentiostatic weight loss technique has been used to compare the corrosion rates of Weldox 700 high strength low alloy steel exposed to both natural and sterile sea water at potentials ranging from the free corrosion condition to - 1000 mV (SCE). Anodic polarisation curves with Tafel constants of 54 and 64 mV per decade were fitted to the data and the minimum levels of protection required to limit the corrosion rate to 0·001 mm per year were found to be - 770 and - 790 mV (SCE) in natural and sterile sea water, respectively. Lower corrosion rates occurred in filtered natural sea water than in sterile sea water but the highest rates were recorded on specimens ex posed to a seabed sediment. The reasons for this behaviour are discussed in terms of the biofilms and the numbers of sulphate reducing bacteria present on the surfaces.

Get full access to this article

View all access options for this article.

References

Sharp

J. V.

: J. Mater. Sci., 1979, 14, 1773–1779.

Thomas

C. J.

, EDYVEAN

R. G. J.

, and BROOK

: Biofouling, 1988, 1, 65–78.

Hinton

B. R. W.

and PROCTER

R. P. M.

: Corros. SCi., 1983, 23, 101–123.

Lucas

K. A.

and ROBINSON

M. J.

: Corros. Sci., 1986, 26, 705–717.

Robinson

M. J.

, PARKER

C. H. J.

, and SEAL

K. J.

: Proc. Conf. UK Corrosion ‘87, Brighton, UK, October 1987, 279–290; Institution of Corrosion Science and Technology.

Benett

W. J.

Jr ., L. CADIOU, and L. COUDREUSSE: Proc. 3rd Int. Conf. on ‘Self elevating structures’, London, UK, 1991, City University.

‘Preparing, cleaning and evaluating corrosion test specimens’, Standard GI, Philadelphia, PA, USA, ASTM.

Postgate

J. R.

: The sulphate reducing bacteria’, 2nd edn; 1984, Cambridge, Cambridge University.

Batt

: ‘Optimising cathodic protection requirements for high strength steels in the marine enviromnent’, PhD thesis, Cranfield University, UK, 2000.

10.

Hartt

W. H.

, CULBERSON

C. H.

, and SMITH

S. W.

: Corrosion, 1984, 40, 818.

11.

Pourbaix

: ‘Atlas of electrochemical equilibria in aqueous solution’; 1974, Houston, TX, NACE.

12.

Moore

B. T.

and SMITH

B. S.

: ‘Cathodic protection criterion for a new hull steel’, Report no. DSTO—GD-0035, DSTO Aeronautical and Maritime Research Laboratory, Melbourne, Victoria, Australia, 1995.

13.

Yahaya

: The influence of environment on cathodic protec-tion requirements of steel in sea water’, MSc thesis, Cranfield University, UK, 1992.

14.

‘Design and operational guidance on cathodic protection of offshore structures, subsea installations and pipelines’, Publication 90/102, 241–260; 1990, Marine Technology Directorate.

15.

‘Cathodic protection design’, Veritas Recommended Practice RPB401, Det Norske Veritas, 1986.

16.

‘Control of corrosion of offshore steel pipelines’, Publication RP- 06–75; 1975, Houston, TX, NACE.

17.

‘NACE corrosion engineer's reference book’, (ed. Treseder

R. S.

et al.), 2nd edn; 1991, Houston, TX, NACE.

18.

Wanklyn

J. N.

: in ‘Cathodic protection theory and practice’, (ed. Ashworth

and Booker

C. J. L.

), 68–77; 1986, Chichester, Ellis Horwood.

19.

‘Corrosion’, (ed. Shrier

L. L.

et al.), Vol. 1; 1994, Butterworth Heinemann.

20.

Bogar

E D.

and PETERSON

M. H.

: in Laboratory corrosion tests and standards’, STP 866, (ed. Haynes

G. S.

and Baboian

), 197–206; 1985, Philadelphia, PA, ASTM.

21.

Robinson

M. J.

and KILGALLON

P. J.

: ‘A review of the effects of sulphate reducing bacteria in the marine environment on the corrosion fatigue and hydrogen embrittlement of high strength steels’, Offshore Technology Report 0TH 555; 1981, HSE Books.