To investigate the tensile behavior of 3D-printed ultrahigh performance concrete (UHPC), this study developed a 3D-printable steel fiber-reinforced UHPC with a cube compressive strength of up to 115 MPa. Through direct tension tests on dogbone specimens and computed tomography scanning, the influence of the 3D printing methods, specimen thickness and number of specimen layers on the failure mode, cracking strength, peak strength, energy absorption, and orientation of steel fibers in 3D-printed UHPC was analyzed in detail. The results indicate that under direct tension, the failure mode of the 3D-printed UHPC specimens remained in the tensile test section, with no significant difference from those of the cast UHPC specimens. After cracking, a large number of steel fibers were observed in the cracks of the 3D-printed UHPC specimens, forming the effect of a “steel fiber bridge” and exhibiting a trend of directional orientation along the printing direction. This was notably different from the relatively random orientation of steel fibers in the cast specimens. The experimental results show that with 3D printing preparation, the orderly arrangement of steel fibers could significantly improve the tensile performance of UHPC. Moreover, by reducing the nozzle thickness, the steel fibers can be distributed in a wide range along the printing direction. Therefore, the peak tensile stress, peak strain, and energy absorption values of the 3D-printed UHPC specimens could be significantly increased.
RojasEM, AramvareekulP. Is construction labor productivity really declining? J Constr Eng Manage, 2003; 129(1):41–46; doi: 10.1061/(ASCE)0733-9364(2003)129:1(41)
2.
LingardH, CookeT, ZelicG, et al.A qualitative analysis of crane safety incident causation in the Australian construction industry. Saf Sci, 2021; 133:105028; doi: 10.1016/j.ssci.2020.105028
3.
HuoT, TangM, CaiW, et al.Provincial total-factor energy efficiency considering floor space under construction: An empirical analysis of China’s construction industry. J Clean Prod, 2020; 244:118749; doi: 10.1016/j.jclepro.2019.118749
4.
LowkeD, DiniE, PerrotA, et al.Particle-bed 3D printing in concrete construction–possibilities and challenges. Cem Concr Res, 2018; 112:50–65; doi: 10.1016/j.cemconres.2018.05.018
5.
ZhangJ, WangJ, DongS, et al.A review of the current progress and application of 3D-printed concrete. Compos Appl Sci Manuf, 2019; 125:105533; doi: 10.1016/j.compositesa.2019.105533
6.
WengY, LiM, RuanS, et al.Comparative economic, environmental and productivity assessment of a concrete bathroom unit fabricated through 3D printing and a precast approach. J Clean Prod, 2020; 261:121245; doi: 10.1016/j.jclepro.2020.121245
7.
De SchutterG, LesageK, MechtcherineV, et al.Vision of 3D printing with concrete—Technical, economic and environmental potentials. Cem Concr Res, 2018; 112:25–36; doi: 10.1016/j.cemconres.2018.06.001
8.
ZhangY, ZhangY, SheW, et al.Rheological and harden properties of the high-thixotropy 3D printing concrete. Constr Build Mater, 2019; 201:278–285; doi: 10.1016/j.conbuildmat.2018.12.061
9.
NematollahiB, XiaM, SanjayanJG. Current progress of 3D concrete printing technologies. In: International Symposium on Automation and Robotics in Construction (ISARC). Taipei, June, 2017. pp.260–267.
10.
AsproneD, MennaC, BosFP, et al.Rethinking reinforcement for digital fabrication with concrete. Cem Concr Res, 2018; 112:111–121; doi: 10.1016/j.cemconres.2018.05.020
11.
BesterF, van den HeeverM, KrugerJ, et al.Reinforcing digitally fabricated concrete: A systems approach review. Addit Manuf, 2021; 37:101737; doi: 10.1016/j.addma.2020.101737
12.
DingT, XiaoJ, ZouS, et al.Flexural properties of 3D-printed fiber-reinforced concrete with recycled sand. Constr Build Mater, 2021; 288:123077; doi: 10.1016/j.conbuildmat.2021.123077
13.
ZhuB, PanJ, NematollahiB, et al.Development of 3D printable engineered cementitious composites with ultra-high tensile ductility for digital construction. Mater Des, 2019; 181:108088; doi: 10.1016/j.matdes.2019.108088
14.
Chaves FigueiredoS, RodríguezCR, AhmedZY, et al.An approach to develop printable strain hardening cementitious composites. Mater Des, 2019; 169:107651; doi: 10.1016/j.matdes.2019.107651
15.
YuK, McGeeW, NgTY, et al.3D-printable engineered cementitious composites (3DP-ECC): Fresh and hardened properties. Cem Concr Res, 2021; 143:106388; doi: 10.1016/j.cemconres.2021.106388
16.
YeJ, CuiC, YuJ, et al.Effect of polyethylene fiber content on workability and mechanical-anisotropic properties of 3D-printed ultra-high ductile concrete. Constr Build Mate, 2021; 281:122586; doi: 10.1016/j.conbuildmat.2021.122586
17.
YangY, WuC, LiuZ, et al.Experimental investigation on the dynamic behaviours of UHPFRC after exposure to high temperature. Constr Build Mater, 2019; 227:116679; doi: 10.1016/j.conbuildmat.2019.116679
18.
SongQ, YuR, ShuiZ, et al.Optimization of fiber orientation and orientation for a sustainable Ultra-High Performance fiber Reinforced Concrete (UHPFRC): Experiments and mechanism analysis. Constr Build Mater, 2018; 169:8–19; doi: 10.1016/j.conbuildmat.2018.02.130
19.
SongQ, YuR, ShuiZ, et al.Intrinsic effect of hybrid fibers 3D network on the electrochemical characteristics of Ultra-High Performance fiber Reinforced Composites (UHPFRC). Cem Concr Compos, 2020; 114:103818; doi: 10.1016/j.cemconcomp.2020.103818
20.
FanDQ, YuR, ShuiZH, et al.A new design approach of steel fiber reinforced ultra-high performance concrete composites: Experiments and modeling. Cem Concr Compos, 2020; 110:103597; doi: 10.1016/j.cemconcomp.2020.103597
21.
YooDY, BanthiaN. Mechanical properties of ultra-high-performance fiber-reinforced concrete: A review. Cem Concr Compos, 2016; 73:267–280; doi: 10.1016/j.cemconcomp.2016.08.001
22.
AbbasS, SolimanAM, NehdiML. Exploring mechanical and durability properties of ultra-high performance concrete incorporating various steel fiber lengths and dosages. Constr Build Mater, 2015; 75:429–441; doi: 10.1016/j.conbuildmat.2014.11.017
23.
YuK, YuJ, DaiJ, et al.Development of ultra-high performance engineered cementitious composites using Polyethylene (PE) fibers. Constr Build Mater, 2018; 158:217–227; doi: 10.1016/j.conbuildmat.2017.10.040
24.
ArunothayanAR, NematollahiB, RanadeR, et al.Development of 3D-printable ultra-high performance fiber-reinforced concrete for digital construction. Constr Build Mater, 2020; 257:119546; doi: 10.1016/j.conbuildmat.2020.119546
25.
ArunothayanAR, NematollahiB, RanadeR, et al.Digital fabrication of eco-friendly ultra-high performance fiber-reinforced concrete. Cem Concr Compos, 2022; 125:104281; doi: 10.1016/j.cemconcomp.2021.104281
26.
ArunothayanAR, NematollahiB, KhayatKH, et al.Rheological characterization of ultra-high performance concrete for 3D printing. Cem Concr Compos, 2023; 136:104854; doi: 10.1016/j.cemconcomp.2022.104854
27.
ArunothayanAR, NematollahiB, RanadeR, et al.Fiber orientation effects on ultra-high performance concrete formed by 3D printing. Cem Concr Res, 2021; 143:106384; doi: 10.1016/j.cemconres.2021.106384
28.
YangY, WuC, LiuZ, et al.Mechanical anisotropy of ultra-high performance fiber-reinforced concrete for 3D printing. Cem Concr Compos, 2022; 125:104310; doi: 10.1016/j.cemconcomp.2021.104310
29.
ChuSH, LiLG, KwanAKH. Development of extrudable high strength fiber reinforced concrete incorporating nano calcium carbonate. Addit Manuf, 2021; 37:101617; doi: 10.1016/j.addma.2020.101617
30.
DongL, YangY, LiuZ, et al.Microstructure and mechanical behaviour of 3D-printed ultra-high performance concrete after elevated temperatures. Addit Manuf, 2022; 58:103032; doi: 10.1016/j.addma.2022.103032
31.
ArunothayanAR, SanjayanJG. Elevated temperature effects on 3D-printed ultra-high performance concrete. Constr Build Mater, 2023; 367:130241; doi: 10.1016/j.conbuildmat.2022.130241
32.
MaG, BaiG, WangL, et al.Explosion resistance of 3D printing ultra-high performance concrete based on contact explosion tests. Int J Impact Eng, 2022; 169:104316; doi: 10.1016/j.ijimpeng.2022.104316
33.
YangY, WuC, LiuZ, et al.Characteristics of 3D-printing ultra-high performance fiber-reinforced concrete under impact loading. Int J Impact Eng, 2022; 164:104205; doi: 10.1016/j.ijimpeng.2022.104205
34.
GosselinC, DuballetR, RouxP, et al.Large-scale 3D printing of ultra-high performance concrete–a new processing route for architects and builders. Mater Des, 2016; 100:102–109; doi: 10.1016/j.matdes.2016.03.097
35.
BaiG, WangL, WangF, et al.In-process reinforcing method: Dual 3D printing procedure for ultra-high performance concrete reinforced cementitious composites. Mater Lett, 2021; 304:130594; doi: 10.1016/j.matlet.2021.130594
36.
JavedA, MantawyIM, AzizinaminiA. 3D-Printing of ultra-high-performance concrete for robotic bridge construction. Transp Res Rec, 2021; 2675(7):307–319; doi: 10.1177/03611981211011645
37.
XiaoJ, HouS, DuanZ, et al.Rheology of 3D printable concrete prepared by secondary mixing of ready-mix concrete. Cem Concr Compos, 2023; 138:104958; doi: 10.1016/j.cemconcomp.2023.104958
38.
Chinese standard JGJ/T 70-2009. Standard for Test Method of Performance on Building Mortar. Chinese standard JGJ/T 70-2009: China; 2009.
39.
MaG, LiZ, WangL. Printable properties of cementitious material containing copper tailings for extrusion based 3D printing. Constr Build Mater, 2018; 162:613–627; doi: 10.1016/j.conbuildmat.2017.12.051
40.
ASTM C109. Test Method for Compressive Strength of Hydraulic Cement Mortars. ASTM C109: America; 2002.
41.
WuZ, ShiC, HeW, et al.Uniaxial compression behaviour of ultra-high performance concrete with hybrid steel fiber. J Mater Civ Eng, 2016; 28(12):6016017; doi: 10.1061/(ASCE)MT.1943-5533.0001684