Abstract
Among functional monomers used in contemporary dental adhesives, 10-methacryloyloxydecyl dihydrogen phosphate (MDP) has been found to interact chemically with hydroxyapatite (HAp) most intensively and stably. This effect was thought to be the basis of the superior bonding effectiveness of MDP-based self-etch adhesives to enamel/dentin. To elucidate fully the chemical interaction and reactivity of MDP with HAp, we used 31P CP-MAS NMR spectroscopy and powder x-ray diffraction. In an aqueous ethanol solution, Ca ions were leached from HAp to form, at short term, a MDP-calcium salt (CaMHP2) layered structure on the HAp surface. When MDP was allowed to interact for longer time (< 24 hrs), CaHPO4·2H2O precipitated on top of this MDP-calcium salt layered structure. In conclusion, the intense chemical interaction of MDP with HAp must be ascribed to superficial dissolution of HAp induced by the MDP adsorption and subsequent deposition of MDP-calcium salt with a solubility lower than that of CaHPO4·2H2O.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.