Abstract
Functional monomers chemically interact with hydroxyapatite that remains within submicron hybrid layers produced by mild self-etch adhesives. The functional monomer 10-MDP interacts most intensively with hydroxyapatite, and its calcium salt appeared most hydrolytically stable, as compared with 4-MET and phenyl-P. We investigated the hypothesis that additional chemical interaction of self-etch adhesives improves bond stability. The micro-tensile bond strength (μTBS) of the 10-MDP-based adhesive did not decrease significantly after 100,000 cycles, but did after 50,000 and 30,000 cycles, respectively, for the 4-MET-based and the phenyl-P-based adhesives. Likewise, the interfacial ultrastructure was unchanged after 100,000 thermocycles for the 10-MDP-based adhesive, while that of both the 4-MET- and phenyl-P-based adhesives contained voids and less-defined collagen. The findings of this study support the concept that long-term durability of adhesive-dentin bonds depends on the chemical bonding potential of the functional monomer.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.