Abstract
Oxygen inhibits free radical polymerization and yields polymers with uncured surfaces. This is a concern when thin layers of resin are being polymerized, or in circumstances where conventional means of eliminating inhibition are inappropriate. In this study, we tested the hypothesis that viscosity, filler content, and polymerization temperature modify oxygen diffusion in the resin or the reactivity of radical species, and affect the degree of conversion near the surface. Confocal Raman micro-spectroscopy was used to measure monomer conversion from the surface to the bulk of cured resins. Increased viscosity was shown to limit oxygen diffusion and increase conversion near the surface, without necessarily modifying the depth of inhibition. The filler material was shown to increase, simultaneously, oxygen diffusivity and the viscosity of the resin, which have opposite effects on conversion. Polymerization at a temperature above ~ 110°C was shown to eliminate oxygen inhibition.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.