The mechanism responsible for sodium-hypochlorite-induced reduction in dentin bond strength and its reversal with reducing agents is unknown. This study examined the relationship between nanoleakage and reversal of compromised bonding to oxidized dentin. Acid-etched dentin was completely depleted of demineralized collagen matrix when sodium hypochlorite was used. Specimens were bonded with two single-bottle dentin adhesives. They were immersed in ammoniacal silver nitrate for 24 hrs before being processed for transmission electron microscopy. For both adhesives, tensile bond strengths of acid-etched dentin were significantly reduced after sodium hypochlorite treatment, but were reversed when sodium ascorbate was used. After sodium hypochlorite application, reticular nanoleakge patterns in hybrid layers were replaced by vertical, shag-carpet-like patterns along the demineralization front. This type of nanoleakage was completely eliminated after sodium ascorbate treatment with the materials tested. Residual sodium hypochlorite within the porosities of mineralized dentin may result in incomplete resin polymerization, and hence compromised bond strength.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.