Aluminium–Copper (Al-10Cu) alloys are widely used for structural components in the aviation sector. This study focuses on the synthesis and characterisation of Al-10Cu alloy reinforced with Al2O3-30(Ni-20Al) cermet particles to evaluate their microstructural, mechanical, tribological and corrosion properties. The Al-10Cu alloy was cast with varying percentages of cermet (2% and 4%) using a controlled casting process. Comprehensive microstructural analyses, including optical microscopy, SEM and EBSD, were performed to assess the grain structure and cermet distribution. The mechanical properties were evaluated through Vickers microhardness and tensile testing, while tribological performance was assessed using a Pin-on-Disc tribometer. Corrosion resistance was investigated through exfoliation and immersion corrosion tests. The results indicated significant improvements in microhardness and wear resistance with the addition of cermet particles, while the tensile strength showed a complex interplay between ductility and brittleness. Corrosion tests revealed enhanced resistance in cermet-reinforced specimens. This study demonstrates the potential of Al2O3-30(Ni-20Al) cermet as an effective reinforcement for aluminium alloys to achieve superior performance in structural applications.
AmirkhanlouSJiS. Casting lightweight stiff aluminum alloys: a review. Crit Rev Solid State Mater Sci2020; 45: 171–186.
2.
KrögerFTonnB. Application of design of experiments for alloy development of an aluminum copper casting alloy. J Mater Sci Eng A2020; 10: 6–23.
3.
AmerSBarkovRYProsviryakovA, et al.Structure and properties of new heat-resistant cast alloys based on the Al–Cu–Y and Al–Cu–Er systems. Phys Met Metallogr2021; 122: 908–914.
4.
BakkeAOArnbergLLiY. Achieving high-strength metallurgical bonding between A356 aluminum and copper through compound casting. Mater Sci Eng A2021; 810: 140979.
5.
WuY, et al.In situ radiographic study of the grain refining behavior of Al3Sc during the solidification of Al-10Cu alloy. J Mater Sci Technol2022; 122: 33–43.
6.
FengH, et al.Current-carrying wear characteristics of Al-Cu alloys against stainless steel. Mater Lett2023; 343: 134374.
7.
AlamoudiMTM. Correlating rapid solidification microstructure morphology and mechanical properties in hypo-eutectic Al-Cu alloy. Pennsylvania, United States: University of Pittsburgh, 2022.
8.
AlamoudiMWiezorekJ. Probing effects of solute trapping on the mechanical properties of α-al in rapidly solidified hypoeutectic Al-10at.% Cu after surface laser melting. Mater Sci Eng A2024; 890: 145934.
9.
StojanovicBBukvicМEplerI. Application of aluminum and aluminum alloys in engineering. Appl Eng Lett J Eng Appl Sci2018; 3: 52–62.
10.
PremkumarRVigneshRPadmanabanR, et al.Investigation on the microstructure, microhardness, and tribological behavior of AA1100-hBN surface composite. KOM–Corros Mater Protect J2021; 65: 1–11.
11.
AlexAJVigneshRVPadmanabanR, et al.Effect of heat treatment on the mechanical and wear behavior of friction stir processed AA5052 alloy. Mater Today Proc2020; 22: 3340–3346.
12.
JoseSAJohnMMenezesPL. Cermet systems: synthesis, properties, and applications. Ceramics2022; 5: 210–236.
13.
ElgazzarAZhouS-JOuyangJ-H, et al.A critical review of high-temperature tribology and cutting performance of cermet and ceramic tool materials. Lubricants2023; 11: 122.
KübarseppJJuhaniKTarrasteM. Abrasion and erosion resistance of cermets: a review. Materials2021; 15: 69.
16.
SenderowskiC. Synthesis, properties and applications of intermetallics, ceramic and cermet coatings. MDPI2022; 15: 8408.
17.
EfimochkinIYBazylevaOArginbayevaE, et al.High-Temperature cermet material based on intermetallic nickel matrix. Inorg Mater Appl Res2020; 11: 297–303.
18.
AgureevL, et al.Study of the structure and properties of cermets based on the NiAl–Al2O3 system. Russ J Non-Ferrous Metal2021; 62: 763–770.
19.
BhardwajVSaravananRGovindarajuM, et al.Investigations on the mechanical and tribological performance of nickel aluminum bronze-CaCO3 composite. IOP Conf Series: Mater Sci Eng2021; 1059: 012059.
20.
KübarseppJJuhaniK. Cermets with Fe-alloy binder: a review. Int J Refractory Metal Hard Mater2020; 92: 105290.
21.
ShettyVPatilB. Evaluation of the mechanical properties and microstructure analysis of heat treated LM-12 alloy with SiO2 and CNT hybrid metal matrix composites. Mater Today Proc2021; 46: 2880–2883.
22.
MadhusudanSSarcarMMMRaoNBRM. Mechanical properties of aluminum-copper (p) composite metallic materials. J Appl Res Technol2016; 14: 293–299.
23.
JokhioMHPanhwerMIUnarMA. Manufacturing of aluminum composite material using stir casting process. MEHRAN UNIVERSITY RESEARCH JOURNAL OF ENGINEERING & TECHNOLOGY2011; 30: 1–12.
24.
MehdiHSharmaSAnasM, et al.The influences of variation of copper content on the mechanical properties of aluminium alloy. Int J Mater Sci Innov2015; 3: 74–86.
25.
DeeviSSikkaV. Nickel and iron aluminides: an overview on properties, processing, and applications. Intermetallics1996; 4: 357–375.
26.
DeeviSSikkaVSwindemanC, et al.Reactive spraying of nickel-aluminide coatings. J Thermal Spray Technol1997; 6: 335–344.
27.
Da CostaCZapataWVelascoF, et al.Wear behaviour of aluminum reinforced with nickel aluminide MMCs. J Mater Proc Technol1999; 92: 66–70.
28.
NosewiczSRojekJMackiewiczS, et al.The influence of hot pressing conditions on mechanical properties of nickel aluminide/alumina composite. J Compos Mater2014; 48: 3577–3589.
29.
BlauPJDeVoreCE. Sliding behavior of alumina/nickel and alumina/nickel aluminide couples at room and elevated temperature. Tribol Int1988; 23: 226–234.
30.
TolpygoVClarkeD. Microstructural study of the theta-alpha transformation in alumina scales formed on nickel-aluminides. Matert High Temp2000; 17: 59–70.
31.
RaoGB, et al.Impact on the microstructure and mechanical properties of Al-4.5 Cu alloy by the addition of MoS2. Int J Lightweight Mater Manufact2021; 4: 281–289.
32.
QiuF, et al.Microstructures and tensile properties of Al–Cu matrix composites reinforced with nano-sized SiC p fabricated by semisolid stirring process. Metals2017; 7: 49.
33.
AgboolaJKhanR. Effects of aging temperature and time on microstructure and mechanical properties of LM12 aluminium alloy. J Eng Res2018; 23: 35–42.
34.
SureshaPChikkannaNBiradarIM. Effect of mechanical and physical properties of aluminum alloy LM12 with the reinforcement of silicon carbide. Int J Product Technol Manag2019; 10: 1–8.
35.
VamsiKKrishnakumarMSaravananR. Effect of preheating temperatures on distribution of FeTiO3 on A 360 aluminium alloy by stirring. Materi Today Proc2020; 27: 2412–2417.
36.
Lokesh KumarR, et al.Microstructure, tribology, and corrosion characteristics of hot-rolled AZ31 magnesium alloy. In: Vignesh RV, Padmanaban R and Govindaraju M (eds) Advances in processing of lightweight metal alloys and composites. Springer, 2022, pp.299–326.
37.
Vaira VigneshRPadmanabanRGovindarajuM. Study on the corrosion and wear characteristics of magnesium alloy AZ91D in simulated body fluids. Bullet Mater Sci2020; 43: 1–12.
38.
VigneshRVPadmanabanRGovindarajuM. Investigations on the surface topography, corrosion behavior, and biocompatibility of friction stir processed magnesium alloy AZ91D. Surf Topogr Metrol Prop2019; 7: 025020.
39.
VigneshRVPadmanabanR. Intergranular corrosion susceptibility of friction stir processed aluminium alloy 5083. Mater Today Proc2018; 5: 16443–16452.
40.
TerziSSalvoLSueryM, et al.Coarsening mechanisms in a dendritic Al–10% Cu alloy. Acta Materialia2010; 58: 20–30.
41.
LimodinN, et al.In situ and real-time 3-D microtomography investigation of dendritic solidification in an Al–10 wt.% Cu alloy. Acta Materialia2009; 57: 2300–2310.
42.
KotadiaHRQianMEskinDG, et al.On the microstructural refinement in commercial purity Al and Al-10wt% Cu alloy under ultrasonication during solidification. Mater Des2017; 132: 266–274.
43.
YehiaHMAllamS. Hot Pressing of Al-10 wt% Cu-10 wt% Ni/x (Al2O3–Ag) nanocomposites at different heating temperatures. Met Mater Int2021; 27: 500–513.
44.
GopiVSellamuthuRArulS. Measurement of hardness, wear rate and coefficient of friction of surface refined Al-Cu alloy. Procedia Eng2014; 97: 1355–1360.
45.
JangJ-HNamD-GParkY-H, et al.Effect of solution treatment and artificial aging on microstructure and mechanical properties of Al–Cu alloy. Trans Nonferrous Met Soc China2013; 23: 631–635.
46.
BoukhrisNLalloucheSDebiliMY, et al.Microhardness variation and related microstructure in Al–Cu alloys prepared by HF induction melting and RF sputtering. Eur Phys J Appl Phys2009; 45: 30501.
47.
El AalMIA, et al.Tensile properties and fracture characteristics of ECAP-processed Al and Al-Cu alloys. Met Mater Int2010; 16: 709–716.
48.
FangD, et al.Effect of equal channel angular pressing on tensile properties and fracture modes of casting Al–Cu alloys. Mater Sci Eng A2006; 426: 305–313.