Nickel-based alloy Inconel 617 is a candidate material for advanced ultra-supercritical units. Stress corrosion cracking (SCC) susceptibility of Inconel 617 under low-pressure superheated steam (0.1 MPa), high-pressure superheated steam (8 MPa) and supercritical water (25 MPa) at 650 °C was studied through slow strain rate tensile tests at strain rate of 5 × 10−7 s−1. The results indicate that Inconel 617 is susceptible to SCC in both superheated steam and supercritical water, with susceptibility increasing with pressure. In a nitrogen atmosphere, fractures were predominantly transgranular ductile. The fracture surface featured dimples and micropores. In three corrosive environments, both intergranular and transgranular fractures were observed. The rock sugar-like morphology becomes more and more obvious as the pressure increases. A large number of cracks perpendicular to the loading axis were found on gauge surface. The SCC mechanism for Inconel 617 in superheated steam and supercritical water conditions is internal oxidation.
WangQWangXSZhangNQ. Investigation of the fatigue damage mechanism of Inconel 617 at elevated temperatures obtained by in situ SEM fatigue tests. Int J Fatigue2021; 153: 106518.
2.
NicolK. Status of advanced ultra-supercritical pulverised coal technology. London, UK: IEA Clean Coal Centre, 2013.
3.
ZhangNQYueGQLvFB, et al.Crack growth rate of stress corrosion cracking of Inconel 625 in high temperature steam. J Chin Soc Corros Prot2017; 37: 9–15.
4.
GianfrancescoAD. Materials for ultra-supercritical and advanced ultra-supercritical power plants. Britain: Woodhead Publishing, 2016.
5.
KlöwerJHusemannRUBaderM. Development of nickel alloys based on alloy 617 for components in 700 °C power plants. Procedia Eng2013; 55: 226–231.
6.
Stein-BrzozowskaGFĺorezDMMaierJ,et al.Nickel-base superalloys for ultra-supercritical coal-fired power plants: fireside corrosion, laboratory studies and power plant exposures. Fuel2013; 108: 521–533.
7.
ViswanathanRColemanKRaoU. Materials for ultra-supercritical coal-fired power plant boilers. Int J Press Vessels Pip2006; 83: 778–783.
8.
YangHCLinFSXieXS, et al.R&D progress of 700 °C power generation technology and alloy 617 in Europe. Power Equip2012; 26: 355–359.
9.
JiangHDongJXZhangMC,et al.A review of the study on alloy 617 for 700 °C ultra supercritical power plants. World Iron Steel2014; 14: 26–39.
10.
WangTJFanHZhangBQ, et al.Nickel-based superalloy for key components of ultra-supercritical steam turbine operating above 700 °C. Dongfang Turbine2012; 2: 46–53.
11.
WangTJFanHZhangBQ, et al.Nickel-based superalloy for key components of advanced ultra-supercritical steam turbine operating above 700 °C. In: 2012 technical exchange conference for ultra supercritical units, Ningbo, Zhejiang, China, 2012, p. 7.
12.
PengJQSunFMWangMY. Discussion on materials for high and medium pressure rotors of ultra supercritical steam turbines above 700 °C. In: 2012 technical exchange conference for ultra supercritical units, Ningbo, Zhejiang, China, 2012, p. 10.
13.
WangJDongJXZhangMC,et al.Equilibrium-phase precipitation behaviors of typical nickel-base alloys for 700 °C advanced ultra-supercritical boiler tubes. J Univ Sci Technol Beijing2012; 34: 799–807.
14.
MankinsWLHosierJCBassfordTH. Microstructure and phase stability of INCONEL alloy 617. Metall Trans1974; 5: 2579–2590.
15.
GuoYWangCXLiTJ, et al.Microstructure and precipitates of alloy 617B used for 700 °C advanced ulta-supercritical power units. Chin J Mater Res2016; 30: 841–847.
16.
GuoYWangBHHouSF, et al.Aging precipitates of alloy 617 mod used for 700 °C ultra supercritical unit. Proc CSEE2014; 34: 2314–2318.
17.
YinTCaiLXBaoC. Mechanical properties of Inconel 617B alloy at ultra-supercritical temperature. J Mech Strength2018; 40: 1078–1084.
18.
KaoumiDHrutkayK. Tensile deformation behavior and microstructure evolution of Ni-based superalloy 617. J Nucl Mater2014; 454: 265–273.
19.
WangYChenZLiaoY, et al.A damage-coupled viscoplastic constitutive model considering tension-compression asymmetry for modeling low cycle fatigue mechanical behaviors of Inconel 617 at elevated temperature. Int J Pressure Vessels Piping2023; 206: 105040.
20.
ZhouGBBianSChenZY, et al.Experimental study on high-temperature low cycle fatigue performance of Inconel 617 and C-HRA-2 alloys for advanced ultra-supercritical units. J Chin Soc Power Eng2022; 42: 475–483.
21.
MaierGRiedelHSomsenC. Cyclic deformation and lifetime of Alloy617B during isothermal low cycle fatigue. Int J Fatigue2013; 55: 126–135.
22.
RaoCVSrinivasNCSSastryGVS,et al.Low cycle fatigue, deformation and fracture behaviour of Inconel 617 alloy. Mater Sci Eng, A2019; 765: 138286.
23.
CabetCCarrollLWrightR. Low cycle fatigue and creep-fatigue behavior of alloy 617 at high temperature. J Press Vess-T ASME2013; 135: 061401-1–7.
24.
TotemeierTCTianH. Creep-fatigue–environment interactions in INCONEL 617. Mater Sci Eng, A2007; 468-470: 81–87.
25.
ZhuZLMaCHLiYY, et al.Oxidation behavior of nickel-based alloy Inconel617B in supercritical water at 700 °C. J Chin Soc Corros Prot2022; 42: 655–661.
26.
JiaoYZhangSHTanY. Research progress on stress corrosion cracking of stainless steel for nuclear power plant in high-temperature and high-pressure water. J Chin Soc Corros Prot2021; 41: 417–428.
27.
EPRI. Steam generator progress report. Palo Alto, CA: Electric power research institute, 2011.
28.
YehTHuangGWangM,et al.Stress corrosion cracking in dissimilar metal welds with 304L stainless steel and Alloy 82 in high temperature water. Prog Nucl Energy2013; 63: 7–11.
29.
ShenZZhangLTangR,et al.SCC Susceptibility of type 316Ti stainless steel in supercritical water. J Nucl Mater2015; 458: 206–215.
30.
YooSCChoiKJKimT,et al.Effects of thermal aging and stress triaxiality on PWSCC initiation susceptibility of nickel-based Alloy 600. J Mech Sci Technol2016; 30: 4403–4406.
31.
ChenKWangJShenZ, et al.Comparison of the stress corrosion cracking growth behavior of cold worked Alloy 690 in subcritical and supercritical water. J Nucl Mater2019; 520: 235–244.
32.
ChenKWangJShenZ, et al.Effect of intergranular carbides on the cracking behavior of cold worked alloy 690 in subcritical and supercritical water. Corros Sci2020; 164: 108313.
33.
ShenZAriokaKLozano-PerezS. A mechanistic study of SCC in Alloy 600 through high-resolution characterization. Corros Sci2018; 132: 244–259.
34.
WestEAWasGS. IGSCC of grain boundary engineered 316L and 690 in supercritical water. J Nucl Mater2009; 392: 264–271.
35.
VadlamaniRARevankarSTRiznicJR. Stress corrosion cracking models and mechanisms for Inconel 600, part 2: crack growth. Int J Adv Eng Appl2012; 5: 1–17.
36.
LiuQYLiuZDGanGY,et al.Effect of solid solution treatment on microstructure and hardness of Haynes 282 heat resistant alloy. Heat Treat Met2016; 41: 52–57.
37.
LiuYTChenZYZhuZL, et al.SCC Susceptibility of 2.25Cr1Mo steel and its weld joints in high temperature steam. J Chin Soc Corros Prot2022; 42: 647–654.
38.
KhanHIZhangNXuW, et al.Effect of maximum stress intensity factor, loading mode, and temperature on corrosion fatigue cracking behavior of Inconel 617 in supercritical water. Int J Fatigue2019; 118: 22–34.
39.
KhanHIZhangNZhuZ, et al.Behavior and susceptibility to stress corrosion cracking of a nickel-based alloy in superheated steam and supercritical water. Mater Corros2019; 70: 48–56.
40.
ShimSHSzklarska-SmialowskaZ. Effect of fluid flow rate on the intergranular stress corrosion cracking of AISI 304 stainless steel. Corrosion1987; 43: 280–286.
41.
HicklingJ. Discussion: the effect of fluid flow on the stress corrosion cracking of ASTM A508 Cl 2 steel in high temperature water. Corrosion1984; 40: 36–38.
42.
SuiGTitchmarshJMHeysGB,et al.Stress corrosion cracking of alloy 600 and alloy 690 in hydrogen/steam at 380 °C. Corros Sci1997; 39: 565–587.
43.
ShenZDuDHSunY, et al.Corrosion behavior of nickel based alloy 825 in supercritical water. Atom Energy Sci Technol2014; 48: 1660–1665.
44.
FujisawaRNishimuraKNishidaT, et al.Cracking susceptibility of Ni base alloys and 316 stainless steel in less oxidizing or reducing SCW. In: NACE 60th annual conference & exposition (CORROSIONNACEXPO 2005), 2005, pp.3871–3883.
45.
TsuchiyaYKanoFSaitoN, et al.Corrosion and SCC properties of fine grain stainless steel in subcritical and supercritical pure water, corrosion 2007. NACE International2007; 13: 07415:1–07415:13.
46.
ShenZWuLLZhangLF, et al.Corrosion behavior of nickel base alloy 800H in high-temperature and high-pressure water. Corros Sci Prot Technol2014; 26: 113–118.
47.
LiuBPZhangZMWangJQ, et al.Review of stress corrosion crack initiation of nuclear structural materials in high temperature and high pressure water. J Chin Soc Corros Prot2022; 42: 513–5522.
48.
JeHKimuraA. Stress corrosion cracking susceptibility of oxide dispersion strengthened ferritic steel in supercritical pressurized water dissolved with different hydrogen and oxygen contents. Corros Sci2014; 78: 193–199.
49.
XuWQ. Corrosion fatigue behavior of Inconel 617 alloy for boiler in supercritical water environment. Vol. Master. Beijing: North China Electric Power University, 2018.
50.
GuiJJ. Environmentally assisted cracking behavior of candidate nickel-based alloy for 700 °C USC boiler in supercritical water. Vol. Master. Beijing: North China Electric Power University, 2019.
51.
SantariniG. Comprehensive interpretation of CERTs: a method for the characterization and the prediction of IGSCC. Corrosion1989; 45: 369–381.
52.
KuangWJWasGS. The effect of grain boundary carbide density and strain rate on the stress corrosion cracking behavior of cold rolled alloy 690. Corros Sci2015; 97: 107–114.
53.
MossTWasGS. Accelerated stress corrosion crack initiation of alloys 600 and 690 in hydrogenated supercritical water. Metall Master Trans A2017; 48: 1613–1628.
54.
MaCPengQJHanEH,et al.Review of stress corrosion cracking of structural materials in nuclear power plants. J Chin Soc Corros Prot2014; 34: 37–45.
55.
KhanHIZhangNYueG, et al.Environmentally assisted crack growth rate of an austenitic steel TP347HFG in high-temperature medium. Mater Corros2018; 69: 1064–1076.
56.
KruppUKaneWPfaendtnerJA, et al.Oxygen-induced intergranular fracture of the nickel-base alloy IN718 during mechanical loading at high temperatures. Mater Res (São Carlos, São Paulo, Brazil)2004; 7: 35–41.
57.
ZhangKQHuSLTangZM,et al.Review on stress corrosion crack propagation behavior of cold worked nuclear structural materials in high temperature and high pressure water. J Chin Soc Corros Prot2018; 38: 517–522.
58.
BetovaIBojinovMKinnunenP, et al.Influence of Zn on the oxide layer on AISI 316L (NG) stainless steel in simulated pressurised water reactor coolant. Electrochim Acta2009; 54: 1056–1069.
59.
ChuWYQiaoLJLiJX, et al.Hydrogen embrittlement and stress corrosion cracking. Beijing: Science Press, 2013.
KarabelaAZhaoLGTongJ, et al.Effects of cyclic stress and temperature on oxidation damage of a nickel-based superalloy. Mater Sci Eng, A2011; 528: 6194–6202.
62.
ZhangNQXuHBaiY. Microstructure and self-diffusion coefficient of supercritical water by molecular dynamics simulation. Electr Power2011; 44: 47–50.
63.
GuzonasDNovotnyR. Supercritical water-cooled reactor materials – summary of research and open issues. Prog Nucl Energy2014; 77: 361–372.