The influence of palm oil-derived plasticizers and lubricants on the rheological and mechanical properties of styrene butadiene rubber

Abstract

Researchers have recently focused on green processing aids made from plants and vegetables to avoid the high concentration of polycyclic aromatic hydrocarbons (PAHs) from petroleum-based processing oils, which is hazardous to human health. This paper focuses on the effect of lubricants and plasticisers produced from palm oil on the rheological, mechanical and thermal aging properties of styrene-butadiene rubber (SBR). These lubricants and plasticisers are known as glycerol trioleate (GTO), n-butyl stearate (NBS), ethylene bis-steramide (EBS), ethylene bis-oleamide (EBO), pentaerythritol tetrastearate (PETS) and stearyl stearate. The abrasion performance, visual inspection appearance, and cure characteristics of the lubricants and plasticisers on SBR were examined and compared to processing oil-treated distillate aromatic extract (TDAE), paraffin wax, microcrystalline wax, polyethylene (PE) wax, epoxidised soybean oil (ESBO), and stearic acid. It discovered that rubber compounds based on GTO, stearic acid, and EBS exhibited better abrasion resistance and cure properties than rubber compounds based on processing oil. These samples were selected and subjected to mechanical properties, thermal aging effects analysis and comparison with processing oil. Tensile strength shows that SBR with EBS (22.49 MPa) and EBS with GTO (EBS/GTO; 21.25 MPa) are closely similar to SBR compounds with processing oil (21.02 MPa). The findings imply that EBS and EBS/GTO, green plasticisers and lubricants, are viable alternatives to petroleum-based processing oils while being cost-effective for tire production.