The objectives of this study were to develop a cost-effective, environmental-friendly, mechanochemical reclaiming process for compounded nitrile rubber (NBR) latex waste generated from the dipping and treatment plants of the glove manufacturing process and evaluate properties of reclaimed NBR and virgin NBR/reclaimed NBR blend compounds. Initially, compounded NBR latex waste containing NBR latex mixed with compounding ingredients was dried and reclaimed mechanically by varying the milling time from 0 min to 12.5 min at 2.5-min time interval. Properties such as initial plasticity, Mooney viscosity, swelling, and cross-link density of the mechanically reclaimed NBR samples were evaluated. Also, a series of mechanochemically reclaimed NBR samples were produced using urea and varying its amount from 0 phr to10 phr at 2 phr intervals and milling according to the selected milling time. The mechanochemically reclaimed NBR samples were also tested for the above properties. Finally, a reclaimed NBR sample was prepared by applying the best urea loading and the optimum milling time. Further, a series of virgin NBR/reclaimed NBR blend compounds was prepared by varying the reclaimed NBR from 0% to 70% at 10% interval. Cure characteristics of the above blend compounds were evaluated and compared with those of the 100% virgin NBR (control) compound. Initial plasticity and Mooney viscosity of mechanochemically reclaimed NBR revealed that urea is effective as a reclaiming agent for dried compounded NBR latex waste. Results in overall indicated that 5 min is the optimum milling time and 6 phr is the optimum loading of urea required to produce the best reclaimed NBR in terms of properties and energy consumption. Minimum torque and cure time of the 50:50 virgin NBR/reclaimed rubber blend compound were higher compared to the control, whereas scorch time, maximum torque, and cure rate index of the former were lower compared to the latter.
PhadkeAABhattacharyaAKChakrabortySK, et al.Studies of vulcanization of reclaimed rubber. Rubb Chem Technol1983; 56: 726.
2.
BratonNRKoutskyJA. A new recycling technology: Compression molding of pulverized rubber waste in the absence of virgin rubber. Chem Eng News1974; 52(6): 21.
3.
BockstalLBerchemTSchmetzQ, et al.Devulcanisation and reclaiming of tires and rubber by physical and chemical processes: a review. J Clean Prod2019; 236: 117574.
4.
HarshaftAA. Solid waste treatment technology. Environ Sci Technol1972; 6(5): 412–421.
5.
SegharSAsaroLRolland-MonnetM, et al.Thermo-mechanical devulcanization and recycling of rubber industry waste. Resour Conserv Recycl2019; 144: 180–186.
6.
PhadkeAADeSK. Use of cryoground reclaimed rubber in natural rubber. Conserv Recycl1986; 9: 271.
7.
FixSR. Microwave devulcanization of rubber. Elastomerics1980; 112(6): 38.
8.
FormelaKHejnaAZedlerL, et al.Microwave treatment in waste rubber recycling–recent advances and limitations. Express Polym Lett2019; 13(6): 565–588.
9.
TukachinskyASchwormDIsayevAI, et al.Devulcanization of waste tire rubber by powerful ultrasound. Rubb Chem Technol1996; 69(1): 92–103.
AbrahamECherianBMElbiPA, et al.Recent advances in the recycling of rubber waste. In: FainleibAGrigoryevaO (eds) Recent developments in polymer recycling. Kerala, India: Transworld Research Network, 2011; Ch. 2, pp. 47–100.
16.
OkamotoHInagakiSOnauchiY, et al.Reclamation of waste rubber vulcanizates. I. Reclamation of crushed tire scrap by the mechano-chemical procedure with accelerators. Nippon Gomu Kyokaishi1979; 52(12): 774.
17.
KnorrK. Reclaim from natural and synthetic rubber scrap for technical rubber goods. Kautschuk Gummi Kunststoffe1994; 47: 54.
18.
AndersonEJr. Reclaiming of vulcanized rubber − a new method. Patent 4,544,675, USA, 1985.
19.
MasakiKOhkawaraSIHiranoT, et al.Devulcanization of nitrile butadiene rubber in nitrobenzene. J Appl Polym Sci2004; 91(5): 3342–3353.
20.
ZedlerLPrzybyszMKleinM, et al.Processing, physico-mechanical and thermal properties of reclaimed GTR and NBR/reclaimed GTR blends as function of various additives. Polym Degrad Stabil2017; 143: 186–195.
21.
KhalilAMEl-NemrKFHassanML. Acrylate-modified gamma-irradiated olive stones waste as a filler for acrylonitrile butadiene rubber / devulcanized rubber composites. J Polym Res2019; 26(11): 249.
22.
KohlerRO’NeilJ. New technology for the devulcanization of sulfur-cured scrap elastomers. Rubber World1997; 216(2): 32.
23.
SekharBC. Improvements in and relating to the reclaiming of natural and synthetic rubbers. European Patent Application EP0690091A1, 1995.
24.
DeDDasADeyB, et al.Reclaiming of ground rubber tire (GRT) by a novel reclaiming agent. Eur Polym J2006; 42: 917–927.
25.
DeDAdhikariBMaitiS.Reclaiming of rubber by a renewable resource material. Part 1. Reclaiming of natural rubber vulcanizates. J Polym Mater1997; 14: 333.
26.
DeDMaitiSAdhikariB.Reclaiming of rubber by a renewable resource material (RRM). II. Comparative evaluation of reclaiming process of NR vulcanizate by RRM and diallyl disulfide. J Appl Polym Sci1999; 73(14): 2951.
27.
HildebrandtH. A method for regenerating containing vulcanizates of synthetic rubbers. German Patent DE1244390B, 1967.
28.
YamashitaSKawabataNSaganS, et al.Reclamation of vulcanized rubbers by chemical degradation. V. Degradation of vulcanized synthetic isoprene rubber by the phenylhydrazine–ferrouschloride system. J Appl Polym Sci1977; 21: 2201.
29.
KawabataNOkuyamaBIYamashitaS.Reclamation of vulcanized rubber by chemical degradation. XV. Degradation of vulcanized synthetic isoprene by the phenylhydrazine–iron (II) chloride system. Appl Polym Sci1981; 26: 1417.
30.
StalinskiE. Reclaiming of natural or synthetic rubber. French Patent 11517694, 1968.
31.
Van DuinMNoordermeerJWMVerbruggenMAL, et al.Method for devulcanizing rubber with an amine. Patent Application US2003013776, 2003.
32.
WarnerWC. Methods of devulcanization. Rubb Chem Technol1994; 67: 559–565.
33.
JosephAMGeorgeBMadhusoodananKN, et al.Current status of sulphur vulcanization and devulcanization chemistry: process of vulcanization. Rubber Sci2015; 28(1): 82–119.
34.
DeDDeD. Processing and material characteristics of a reclaimed ground rubber tire reinforced styrene butadiene rubber. Mater Sci Appl2011; 2: 486–496.
35.
DeDMaitiSAdhikariB. Comparative evaluation of reclaiming process of NR vulcanizate by RRM and diallyl disulfide. J Appl Polym Sci1999; 73(14): 2951.
36.
HorikxMM. Chain scissions in a polymer network. J Polym Sci1956; 19: 445–454.
37.
FloryPJRehnerJJr.Statistical mechanics of crosslinked polymer networks I. Rubberlike elasticity. J Chem Phys1943; 11: 521.
38.
IshiakuUSChongCSIsmailH. Determination of optimum De-Link R concentration in a recycled rubber compound. Polym Test1999; 18: 621–633.
39.
EdirisingheDG.Chemical modification of rubber waste and characterization of their blends with natural rubber. PhD thesis, University of Moratuwa, Sri Lanka, 2012.
40.
PremachandraJKEdirisingheDGDe SilvaMI. A novel reclaiming agent for ground rubber tyre (GRT). Part 1: property evaluation of virgin natural rubber (NR)/novel reclaimed GRT blend compounds. Prog Rub Plast Recycl Tech2011; 27(1): 31–48.
41.
YamashitaS. Reclaimed rubber from rubber scrap. Int Polym Sci Technol1981; 8(12): 77–93.
42.
OnouchiYInagakiSOkamotoH, et al.Reclamation of scrap rubber vulcanizates III: reclamation of crushed tire scrap with dimethyl sulfoxide. Int Polym Sci Technol1982; 55: 58–62.
43.
SegharSAsaroLHocineNA. Experimental validation of the Horikx. Theory to be used in the rubber devulcanization analysis. J Polym Environ2019; 27(10): 2318–2323.
44.
BahrainSHMahmudJ. Swelling behaviour and morphological analysis of arenga pinnata–silicone biocomposite. Mater Lett2019; 242: 32–34.
45.
NasirMRNoimamNZIsmailH, et al.The influence of cure characteristics and crosslink density of virgin acrylonitrile butadiene rubber/recycled acrylonitrile butadiene rubber (vNBR/rNBR) blends. Key Eng Mater2013; 594–595: 735–739.
46.
IsmailHNordinRNoorAM. Cure characteristics, tensile properties and swelling behaviour of recycled rubber powder-filled natural rubber compounds. Polym Test2002; 21(5): 565–569.
47.
JacobCDeSK. Powdered rubber waste in rubber compounds. In: De SadhanKIsayevAIKhaitK (eds) Rubber recycling. Boca Raton: CRC Press, Taylor & Francis Group, 2005, vol. 14, pp. 213–246.
48.
YehiaAAIsmailMNHefnyYA, et al.Mechano-chemical reclamation of waste rubber powder and its effect on the performance of NR and SBR vulcanisates. J Elastom Plast2004; 36(2): 109–123.
49.
AdhikariBDeDMaitiS. Reclamation and recycling of waste rubber. Prog Polym Sci2000; 25(7): 909–948.
50.
SuryaIHayeemasaeNGintingM. Cure characteristics, crosslink density and degree of filler dispersion of kaolin-filled natural rubber compounds in the presence of alkanolamide. In: IOP Conference Series: Materials Science and Engineering, IOP Publishing, March2018.
51.
HanSCHanMH. Fracture behaviour of NR and SBR vulcanisates filled with ground rubber having uniform particle size. J Appl Sci2002; 85: 2491.
52.
LiSLamminmakiJHanhiK. Effect of ground rubber powder and devulcanisates on the properties of natural rubber compounds. J Appl Polym Sci2005; 97: 208–217.