AA7075-T6 sheets with 1, 1.5, and 2 mm thicknesses were tailor-welded using the gas tungsten arc welding process. The welded blanks were solution heat treated, hot stamped, and simultaneously quenched to produce U-shaped components, and finally artificially aged. A finite element model using the ABAQUS software was developed to simulate the forming process. The experimental and numerical results showed no rupture in the components. Tensile and hardness tests revealed that the maximum tensile strength, yield strength, and microhardness of the aged specimen were approximately 96%, 93%, and 107% of the initial material, respectively. Maximum and minimum microhardness of 196 and 145 HV were observed in the heat-affected and fusion zones of the specimens, respectively. Increasing the tailoring ratio increased the strengthening behavior of the components. With a tailoring ratio of 1, the maximum and minimum elongations at break were 70% and 40% of the original aluminum sheet for 2 mm and 1 mm thick sheets, respectively.
EL FakirOWangLBalintD, et al.Numerical study of the solution heat treatment, forming, and indie quenching (HFQ) process on AA5754. Int J Mach Tools Manuf2014; 87: 39–48.
2.
ZhangYZhuPChenGL. Lightweight design of automotive front side rail based on robust optimization. Thin-Walled Struct2007; 45: 670–676.
3.
FeisterTKimHGwinnA, et al.Failure predictions in warm forming of 7075-T6 aluminum structural parts. IOP Conf Ser: Mater Sci Eng2018; 418: 012024.
4.
HarrisonNRLuckeySG. Hot stamping of a B-pillar outer from high strength aluminum sheet AA7075. SAE Int J Mater Manuf2014; 7: 567–573.
5.
RokniMRZarei-HanzakiARoostaeiAA,et al.An investigation into the hot deformation characteristics of 7075 aluminum alloy. Mater Des2011; 32: 2339–2344.
6.
HuaLHuXHanX. Microstructure evolution of annealed 7075 aluminum alloy and its influence on room-temperature plasticity. Mater Des2020; 196: 109192.
7.
ZhengKPolitisDJWangL,et al.A review on forming techniques for manufacturing lightweight Complex-shaped aluminum panel components. Int J Lightweight Mater Manuf2018; 1: 55–80.
8.
XiaoWCWangBYKangY, et al.Deep drawing of aluminum alloy 7075 using hot stamping. Rare Met2017; 36: 485–493.
9.
SotirovNSimonPWaltenbergerT, et al.Verbessertes umformverhalten von höchstfesten 7xxx-aluminiumblechen durch halbwarmumformen. HTM J Heat Treatm Mat2011; 66: 37–43.
10.
MohamedMSFosterADLinJ, et al.Investigation of deformation and failure features in hot stamping of AA6082: experimentation and modeling. Int J Mach Tools Manuf2012; 53: 27–38.
11.
GarrettRPLinJDeanTA. Solution heat treatment and cold die quenching in forming AA6xxx sheet components: a feasibility study. Adv Mat Res2005; 6: 673–680. www.scientific.net/AMR.6-8.673
12.
GengHWangYWangZ,et al.Investigation on contact heating of aluminum alloy sheets in hot stamping process. Metals (Basel)2019; 9: 1341.
13.
DegnerJHornAMerkleinM. Experimental study on the warm forming and quenching behavior for hot stamping of high-strength aluminum alloys. J Phys Conf Ser2017; 896: 012055.
14.
AbbasiMNaderiMSaeed-AkbariA. Isothermal versus non-isothermal hot compression process: a comparative study on phase transformations and structure–property relationships. Mater Des2013; 45: 1–5.
15.
KumarMRossNG. Investigations on the hot stamping of AW-7921-T4 alloy sheet. Adv Mater Sci Eng2017; 2017: 1–10.
16.
XiaoWWangBZhengK. An experimental and numerical investigation on the formability of AA7075 sheet in hot stamping condition. Int J Adv Manuf Technol2017; 92: 3299–3309.
17.
YanKShiZQWangXL. Influence of heat treatment on microstructure and mechanical properties of spray formed 7 series aluminum alloy TIG weld joint. Trans China Weld Inst2012; 33: 33–40.
18.
WangZZhangZChengJ, et al.Simultaneously increased strength and plasticity of TIG-welded 7075-T6 aluminum alloy joints via a novel post-weld composite treatment process. J Mater Res Technol2023; 26: 542–555.
19.
MamusiHMasoumiAHashemiR,et al.A novel approach to the determination of forming limit diagrams for tailor-welded blanks. J Mater Eng Perform2013; 22: 3210–3221.
20.
HabibiMHashemiRFallah TaftiM,et al.Experimental investigation of mechanical properties, formability and forming limit diagrams for tailor-welded blanks produced by friction stir welding. J Manuf Process2018; 31: 310–323.
21.
ZadpoorAASinkeJBenedictusR. Mechanics of tailor-welded blanks: an overview. Key Eng Mater2007; 344: 373–382.
22.
SokolukMCaoCPanS,et al.Nanoparticle-enabled phase control for arc welding of unweldable aluminum alloy 7075. Nat Commun2019; 10: 98.
23.
AbbasiMKetabchiMShakeriHR,et al.Formability enhancement of galvanized IF-steel TWB by modification of forming parameters. J Mater Eng Perform2012; 21: 564–571.
24.
MarionMMarenJMichaelL,et al.A review on tailored blanks - production, applications and evaluation. J Mater Process Technol2014; 214: 151–164.
25.
El FakirODasSStoneI, et al.Solution heat treatment, forming and in-die quenching of a commercial sheet magnesium alloy into a Complex-shaped component: Experimentation and FE simulation. Key Eng Mater2014; 622-623: 596–602.
26.
LiuJGaoHEl FakirO, et al.Hot stamping of AA6082 tailor welded blanks: experiment and FE simulation. Manuf Rev2016; 3: 8.
27.
TemmarMHadjiMSahraouiT. Effect of post-weld aging treatment on mechanical properties of tungsten inert gas welded low thickness 7075 aluminum alloy joints. Mater Des2011; 32: 3532–3536.
28.
ShenJAgrawalPRodriguesTA, et al.Microstructure evolution and mechanical properties in a gas tungsten arc welded Fe42Mn28Co10Cr15Si5 metastable high entropy alloy. Mater Sci Eng A2023; 867: 144722.
29.
KaramiVMollaei DarianiBHashemiR. Investigation of forming limit curves and mechanical properties of 316 stainless steel/St37 steel tailor-welded blanks produced by tungsten inert gas and friction stir welding method. CIRP Ann Manuf Technol2021; 32: 437–446.
30.
MabuwaSMsomiV. Review on friction stir processed TIG and friction stir welded dissimilar alloy joints. Metals (Basel)2020; 10: 142.
31.
IdreesUAhmadSAlam ShahI, et al.Finite element analysis of car frame frontal crash using lightweight materials. J Eng Res2023; 11: 100007.
32.
BalasubramanianVRavisankarVReddyGM. Influences of pulsed current welding and post-weld aging treatment on fatigue crack growth behavior of AA7075 aluminum alloy joints. Int J Fatigue2008; 30: 405–416.
33.
SallehMNMIshakMShahLH,et al.The effect of ER4043 and ER5356 filler metal on welded al 7075 by metal inert gas welding. WIT Trans Built Environ2017; 166: 213–224.
34.
LiuJWangALGaoHX, et al.Studies on the hot forming and cold-die quenching of AA6082 tailor welded blanks. Key Eng Mater2016; 716: 941–947.
35.
GomezJMSalazarDEUrenaA, et al.TIG, and MIG welding of 6061 and 7020 aluminum alloys. Microstructural studies and mechanical properties. Weld Int2010; 13: 293–295.