The combined effect of temperature and seawater on the compression properties of carbon fiber vinyl ester composites for sandwich structures

Abstract

For naval applications, composite sandwich structures are of significant interest, and are often manufactured using thin (2 to 4 mm) composite facings made from carbon or glass fiber reinforcement, attached to a thick (25 to 50 mm) section of PVC cellular foam or balsa wood-based core materials using a suitable polymeric resin. In the present study, we focus on the hygrothermal effect on the fiber-dominated compression properties of carbon fiber reinforced vinyl ester resin based polymeric composite (CF/VE), used as “skin” for a polymeric composite sandwich material. Hygrothermal conditioning is achieved by saturating samples in simulated seawater at 40°C. Compression properties are evaluated for coupons extracted along warp and fill undergoing- no conditioning, conditioning till saturation (up to 6 months), and long-term conditioning (2 years). Sea-water saturation yields in up to 12% drop in compression strength with a further 3–4% drop resulting from long-term conditioning. No statistically significant modulus degradation is noticed due to short or long-term hygrothermal exposure. The failure mechanism of the warp extracted coupon, which fails in a splitting failure mode originating due to the delamination between the 0/90 interface, or the fill extracted coupon, which fails due to the instability caused by tow micro-buckling, remains unchanged due to combined exposure (short or long-term) of seawater and temperature. The loss in strength is attributed to the degradation of the fiber-matrix interface, which is validated via conducting single fiber push-in tests with a nominal diameter of 7 micron for conditioned and unconditioned coupons.