Crack growth in cross-linked polyvinylchloride and thermoplastic polyethersulfone foams under mode fatigue cycling has been experimentally examined. Polyvinylchloride foams of densities ranging from 45 to 100 kg/m3 and polyethersulfone foams of densities ranging from 60 to 130 kg/m3 were considered. All cyclic tests employed the sandwich double cantilever beam test specimen. The test results revealed that crack growth rate (da/dN) compared at a constant cyclic energy release rate (ΔG) decreased with increasing density of the foam. The crack propagation rates in low-density polyethersulfone foams were much less than in polyvinylchloride foams of similar density. The crack growth rate in the high-density polyethersulfone foam was highly dependent on the loading R-ratio. The crack front in the low-density polyethersulfone foam displayed marked deviations from a straight shape, where the edge regions propagated faster than the center of the specimen. All polyvinylchloride foams and high-density polyethersulfone foam displayed straight crack fronts.
OlurinOBMcCulloughKYGFleckNA. Ashby, Fatigue Crack Propagation in Aluminum Alloy Foams. Int J Fatigue2001; 23: 375–382.
4.
ShipshaABurmanMZenkertD. Interfacial fatigue growth in foam core sandwich structures. Fatigue Fract Eng Mater Struct1999; 22: 123–131.
5.
GillespieJWCarlssonLAGawandiAA. Fatigue crack growth at the face sheet-core interface in a discontinuous ceramic-tile core sandwich structure. Compos Struct2012; 94: 3186–3193.
6.
Manca M, Quispitupa A, Berggreen C, et al. Face/core debond fatigue crack growth characterization using the sandwich mixed mode bending specimen. Compos: Part A 2012; 43: 2120–2127.
7.
MaitiSAshbyMGibsonL. Fracture toughness of brittle cellular solids. Scripta Metall1984; 18: 213–217.
JamesMNewmanJ. The effect of crack tunneling on crack growth: experiments and CTOA analyses. Eng Fract Mech2003; 70: 457–468.
18.
LanWDengXSuttonM. Investigation of crack tunneling in ductile materials. Eng Fract Mech2010; 77: 2800–2812.
19.
Zamrik SY, Mirdamamdi M and Davis DC. A proposed model for biaxial fatigue analysis using the triaxiality factor concept. Advances in Multiaxial Fatigue. ASTM STP 1191 (1993) 85.
20.
NitturPGKarlssonAMCarlssonLA. Implementation of a plastically dissipated energy criterion for three-dimensional modeling of fatigue crack growth. Int J Fatigue2013; 54: 47–55.
21.
ASTM E399-09e2, Standard test method for linear-elastic plane-strain fracture toughness of metallic materials, ASTM, 2001.
22.
ASTM D5528-01, Standard test method for mode I interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites, ASTM, 2001.