Measurement of Interface Fracture Toughness of Sandwich Structures under Mixed Mode Loadings

Abstract

Fracture of sandwich structures loaded with axial forces and bending moments is analyzed in the context of linear elastic fracture mechanics. A closed form expression for the energy release rate of interface cracking of a sandwich specimen is found by analytical evaluation of the J-integral. A method for determining the mode mixity is described and applied. Expressions are presented whereby the mode mixity can be calculated analytically for any load combination when the mode mixity is known for just one load case.

The theory presented is applied to a new test method based on double cantilever beam sandwich specimens loaded with uneven bending moments. The interface fracture toughness of two sandwich types are measured as function of the mode mixity. The sandwich structures that are tested consist of glass fiber reinforced polyester skins and PCV core. The tests show that the interface fracture toughness depends strongly on the mode mixity. Under dominated normal crack opening, the crack grows just below the interface in the core at a constant fracture toughness. Under dominated tangential crack deformation, the crack grows into the laminate resulting in extensive fiber bridging and an increase in fracture toughness. As a result of the development of a large process zone due to fiber bridging, the analysis by linear elastic fracture mechanics becomes invalid and modeling with cohesive zones is proposed.

Keywords

fracture toughness fiber bridging energy release rate mode mixity LEFM.

Get full access to this article

View all access options for this article.

References

Zenkert, D. (1991). Strength of Sandwich Beams with Interface Debondings , Composite Structures, 17: 331—350.

Carlsson, L.A. and Prasad, S. (1993). Interfacial Fracture of Sandwich Beams, Engineering Fracture Mechanics, 44(4): 581—590.

Ratcliffe, J. and Cantwell, W.J. (2001). Center Notch Flexure Sandwich Geometry for Characterizing Skin-core Adhesion in Thin-skinned Sandwich Structures, Journal of Reinforced Plastics & Composites , 20(11): 945—970.

Suo, Z. (1989). Singularities, Interfaces and Cracks in Dissimilar Anisotropic Media, Proc. R. Soc. Lond. A, 427: 331—358.

Liechti, K.M. and Chai, Y.S. (1992). Asymmetric Shielding in Interfacial Fracture under Inplane Shear, Journal of Applied Mechanics, 59: 295—304.

Toftegaard, H. and Goutianos, S. (2006). Composite Skin Elastic Constants from Monolithic In-plane Specimens and Bonded Out-of-plane Specimens , Journal of Sandwich Structures and Materials (in press).

Zenkert, D. (1997). The Handbook of Sandwich Constructions, Engineering Materials Advisory Services Ltd., UK.

Berggren, C. , Simonsen, B.C. and Borum, K.K. (2006). Numerical and Experimental Study of Interface Crack Propagation in Foam Cored Sandwich Beams, Journal of Composite Materials (in press).

Hutchinson, J. and Suo, Z. (1992). Mixed Mode Cracking in Layered Materials, Advances in Applied Mechanics, 29: 63—191.

10.

Rice, J.R. (1988). Elastic Fracture Mechanics Concepts for Interfacial Cracks, Journal of Applied Mechanics, 55: 98—103.

11.

stergaard, R.C. and Sørensen, B.F. (2006). Interface Crack in Sandwich Specimens, submitted, International Journal of Fracture .

12.

Rice, J.R. (1968). A Path-independent Integral and the Approximate Analysis of Strain Concentration by Notches and Cracks, Journal of Applied Mechanics, 35: 376—386.

13.

Suo, Z. and Hutchinson, J. (1990). Interface Crack between Two Elastic Layers, International Journal of Fracture, 43: 1—18

14.

Beuth, J. (1996). Separation of Crack Extension Modes in Orthotropic Delamination Models, International Journal of Fracture, 77: 305—321.

15.

Matos, P.P.L. , McMeeking, R.M. , Charalambides , P.G. and Drory, M.D. (1989). A Method for Calculating Stress Intensities in Bimaterial Fracture, International Journal of Fracture, 40: 235—254.

16.

Sørensen, B.F. , Jørgensen, K. , Jacobsen, T.K. and stergaard , R.C. (2006). DCB-specimen Loaded with Uneven Bending Moments, International Journal of Fracture, 141: 163—176.

17.

Matteson, R.C. , Carlsson, L.A. , Aviles, A.V. and Loup, D.C. (2005). On Crack Extension in Foam Cored Sandwich Fracture Specimens, In: Proceedings of the 7th International Conference on Sandwich Structures, Aalborg University, Denmark, Springer, Dordrecht, The Netherlands.

18.

Suo, Z. , Bao, G. and Fan B. ( 1992). Delamination R-curve Phenomena due to Damage, J. Mech. Phys. Solids, 40(1): 1—16.

19.

Tvergaard, V. and Hutchinson, J.W. (1993). The Influence of Plasticity on Mixed Mode Interface Toughness, J. Mech. Phys. Solids, 41: 1119—1135.

20.

Evans, A.G. and Hutchinson, J.W. (1989). Effects of Non-planarity on the Mixed Mode Fracture Resistance of Bimaterial Interfaces, Acta. Metall., 37(3): 909—916.

21.

Thouless, M.D. and Evans, A.G. (1990). Comment on the Spalling and Edge-cracking of Plates. Scripta Metallurgica et Materialia , 24(8): 1507—1510.

22.

Hutchinson, J.W. and Evans, A.G. (2000). Mechanics of Materials: Top Down Approaches to Fracture, Acta Materialia, 48: 125—135.

23.

Tvergaard, V. (1990). Effect of Fibre Debonding in a Whiskers Reinforced Metal, Mater. Sci. Engng. A, 125: 203—213.

24.

Jin, Z.H. and Sun, C.T. (2005). Cohesive Zone Modeling of Interface Fracture in Elastic Bi-materials, Engineering Fracture Mechanics, 72(12): 1805—1817.

25.

Jacobsen, T.K. and Sørensen, B.F. (2001). Mode I Intra-laminar Crack Growth in Composites — Modelling of R-curves from Measured Bridging Laws, Composites Part A: Applied Science and Manufacturing , 32(1): 1—11.

26.

Jones, R.M. (1975). Mechanics of Composite Materials, McGraw-Hill, Washington, D.C.