Influence of Face/Core Interface on Debond Toughness of Foam and Balsa Cored Sandwich

Abstract

The face/core debond fracture resistance of sandwich panels consisting of glass fiber/vinylester face sheets over a 155 kg/m ³ end-grain balsa wood core and a 200 kg/m ³ PVC foam core has been examined. The sandwich panels were prepared using a variety of resin infusion strategies with the objective of comparing face/core adhesion. The resin infusion methods include machining grooves in the core, adding a layer of continuous filament mat at the face/core interface, resin distribution medium on top of the face sheet fibers, and no infusion aid but significantly delayed gel-time by addition of cure inhibitor. The tilted sandwich debond (TSD) method is used for determination of debond fracture toughness (G _C). It was found that the use of a continuous filament mat between the face and core provided the toughest interface, although the panels prepared using the resin cure inhibitor are almost as tough. Overall, the PVC foam core provided higher toughness than the balsa wood core.

Keywords

debonding glass fiber foam core balsa core vacuum infusion interface fracture toughness

Get full access to this article

View all access options for this article.

References

Li, X. and Carlsson, L.A. (1999). The Tilted Sandwich Debond (TSD) Specimen for Face/ Core Interface Characterization , J. Sandwich Struct. Mater., 1 (1): 60–75 .

Viana, G.M. and Carlsson, L.A. (2003). Influences of Foam Density and Core Thickness on Debond Toughness of Sandwich Specimens with PVC Foam Core , J. Sandwich Struct. Mater., 5 (2): 103–118 .

Shivakumar, K.N. and Smith, S.A. (2004). In-Situ Fracture Toughness Testing of Core Materials in Sandwich Panels , J. Compos. Mater., 38 (8): 655–668 .

Majumdar, P. , Srinivasagupta, D. , Mahfuz, H. , Joseph, B. , Thomas, M. and Christensen, S. (2003). Effect of Processing Conditions and Material Properties on the Debond Fracture Toughness of Foam-core Sandwich Composites: Experimental Optimization , Composites: Part A, 34 (11): 1097–1104 .

Aviles, F. (2005). Local Buckling and Debond Propagation in Sandwich Columns and Panels, PhD Dissertation, Florida Atlantic University, Boca Raton, FL, May, 2005.

Advani, S.G. and Sozer, E.M. (2002). Process Modeling in Composites Manufacturing, Marcel Dekker, New York .

Pfund, B. (2005). Core Installation , Professional Boat Builder, 94: 48–69 .

DIAB . ProBalsa Technical Manual, 10.00. DIAB AB, Laholm, Sweden (available at http://www.diabgroup.com).

DIAB . Divinycell H-Grade Technical Manual, 10.00. DIAB AB, Laholm, Sweden (available at http://www.diabgroup.com).

10.

Owens Corning . Kyntex Woven Rovings Technical Data Sheet. One Owens Corning Parkway, Toledo , OH 43659 (available at http://secure.owenscorning.net).

11.

Dow Derakane . Technical Data Sheet for Derakane 8084 Resin. Columbus, OH (available at http://www.derakane.com).

12.

Carlsson, L.A. , Matteson, R.C. , Aviles, F. and Loup, D.C. (2005). Crack Path in Foam Cored DCB Sandwich Fracture Specimens , Compos. Sci. Tech., 65 (15–16): 2612–2621 .

13.

Ozdil, F. and Carlsson, L.A. (1992). Mode I Interlaminar Fracture of Interleaved Graphite/ Epoxy , J. Compos. Mater., 26 (3): 432–459 .