Mode Mixity and Crack Tip Yield Zones in TSD Sandwich Specimens with PVC Foam Core

Abstract

In an effort to examine the relation between core fracture toughness and face/core debond toughness, fracture mechanics analysis was conducted on core and debond fracture specimens. H30, H80, H100, H200 and R400 PVC foam cores were examined. Stress intensity factors and size of the plastic zone around the crack tip in foam core Single-Edge Notch Bend (SENB), and Tilted Sandwich Debond (TSD) specimens with foam core were estimated from the elastic displacement and stress fields near the crack tip. Analysis of the influence of core thickness and crack depth on the plastic zone size was performed on TSD specimens with H100 and R400 cores. It was found that the crack loading in the TSD specimen is essentially mode I, and that shear loading is not a factor explaining the higher debond than core toughness. At onset of fracture, the plastic zone height in the TSD specimen is much larger than that in a corresponding foam SENB specimen. It is believed that the plastic zone enlargement is a major factor explaining the elevation of debond toughness over the core toughness.

Get full access to this article

View all access options for this article.

References

1. Zenkert, D. (1997). An Introduction to Sandwich Construction, London: EMAS.

2. Li, X. and Carlsson, L.A. (1999). The tilted sandwich debond (TSD) specimen for face/core interface fracture characterization. J. Sandwich Struct. Mater, 1: 60-75.

3. Viana, G.M. (May 2001). Factors influencing face/core crack propagation in PVC foam core sandwich. Master Thesis, Florida Atlantic University.

4. Viana, G.M. and Carlsson, L.A. Influence of foam density and core thickness on debond toughness of sandwich specimens with PVC foam core. J. Sandwich Struct. Mater. (in press).

5. Viana-Camps, G.M. , Carlsson, L.A. and Li, X. (2000). Influence of core on face/core debond toughness. In: Rajapakse, Y.D.S. , Kardomateas, G.A. and Birman, V. (eds.), Mechanics of Sandwich Structures AD - Vol. 62/AMD-Vol. 245, New York: ASME.

6. Smith, S.A. and Shivakumar, K.N. (2001). Modified Mode-I Cracked Sandwich Beam (CSB) Fracture Test. 42nd AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference, AIAA Paper No. 2001-1221.

7. Liechti, K.M. and Chai, Y.S. (1992). Asymmetric shielding in interfacial fracture under in-plane shear. J. Appl. Mech., 69: 295-304.

8. Shivakumar, K.N. and Crews, J.H. (1987). Energy dissipation associated with crack extension in an elastic-plastic material. Eng. Fract. Mech., 28(3): 319-330.

9. Viana-Camps, G.M. and Carlsson, L.A. Mechanical properties and fracture characterization of cross-linked PVC foam cores. J. Sandwich Struct. Mater. (in press).

10.

10. Divinycell, Technical Specification - H Grade. Divinycell International AB, Laholm, Sweden.

11.

11. ANSYS 5.5 (1998). Swanson Analysis Systems, Inc., Huston, PA.

12.

12. Gibson, L.J. and Ashby, M.F. (1997). Cellular Solids: Structure and Properties, 2nd Edn., Cambridge: Cambridge University Press.

13.

13. Gibson, L.J. , Zhang, M.F. and Triantafillou, T.C. (1989). Failure surfaces for cellular materials under multiaxial loads - I. Modeling. Int. J. Mech Sci., 31: 635-663.

14.

14. Christensen, R.M. , Freeman, D.C. and de Teresa, S.J. (2000). Failure criteria for isotropic materials, applications to low-density types. Submitted to Int. J. Solid. Struct.

15.

15. Timoshenko, S. (1976). Strength of Materials (Part II). Advanced Theory and Problems, 3rd Edn., Malabar: Krieger Publishing.

16.

16. Tveergaard, V. and Hutchinson, J.W. (March 1994). Toughness of an interface along a thin ductile layer joining two solids. Report MECH-230, Division of Applied Sciences, Cambridge: Harvard University.

17.

17. Hunston, D.L. , Kinloch, A.J. , Shaw, S.J. and Wang, S.S. (1984). Characteization of the fracture behavior of adhesive joints. Adhesive Joints. Plenum Publishing, Corporation. pp. 789-807.

18.

18. Carlsson, L.A. (1996). Fracture of laminated composites with interleaves. Key Eng. Mater., 121-122: 489-520.

19.

19. Ozdil, F. and Carlsson, L.A. (1992). Plastic zone estimates in mode I interlaminar fracture of interleaved composites. Eng. Fract. Mech., 41(5): 645-658.

20.

20. Hutchinson, J.W. and Suo, Z. (1992). Mixed mode cracking in layered materials. Adv. in Appl. Mech., 29: 63-191.

21.

21. Li, X. and Carlsson, L.A. (2001). Fracture mechanics analysis of tilted sandwich debond (TSD) specimen. J. Compos. Mater., 35: 2145-2168.

22.

22. Bull, P.H. and Hallstrom, S. (1998). Mechanical Properties of 50 mm Thick Divinycell H200. Report S98-04, Stockholm: Department of Aeronautics, Royal Institute of Technology.