Wear Characteristics of Conventional Ultrahigh-Molecular-Weight Polyethylene Versus Highly Cross-Linked Polyethylene in Total Ankle Arthroplasty

Abstract

Background:

The aim of this study was to compare the polyethylene wear rate, particle size, and particle shape of primary semiconstrained, fixed-bearing, bone-sparing total ankle arthroplasty using conventional ultrahigh-molecular-weight polyethylene (CPE) versus highly cross-linked polyethylene (HXLPE) by applying a level walking input using a joint simulator.

Methods:

Two fixed-bearing total ankle replacement systems with different types of polyethylene liners were tested: (1) CPE sterilized in ethylene oxide, and (2) HXLPE sterilized with gas plasma after electron beam irradiation. Three implants for each design underwent wear testing using gravimetric analysis over 5 million simulated walking cycles. A fourth implant was used as a load soak control. Equivalent circle diameter (ECD) and equivalent shape ratio (ESR) were computed to determine particle size and particle shape, respectively.

Results:

The mean wear rate from 1.5 to 5 million cycles (MC) was 2.0 ± 0.3 mg/MC for HXLPE and 16.7 ± 1.3 mg/MC for CPE (P < .001). The total number of particles per cycle generated for HXLPE and CPE were 0.17 × 10⁶ particles/cycle and 0.53 × 10⁶ particles/cycle, respectively (P < .001). The mean ECD of HXLPE particles (0.22 ± 0.11 μm) was significantly smaller than the mean ECD of CPE particles (0.32 ± 0.14 μm) (P < .001). HXLPE particles were significantly more round than CPE particles (P < .001).

Conclusions:

HXLPE liners had a significantly lower wear rate and produced significantly fewer and rounder particles than CPE liners. The results of this study suggest that HXLPE has more favorable wear characteristics for total ankle arthroplasty.

Clinical Relevance:

Polyethylene wear particles have been linked to osteolysis after total ankle arthroplasty. There is no consensus on the importance of highly cross-linked polyethylene in total ankle arthroplasty with regard to implant wear. This is the first nonindustry study to compare the polyethylene wear rate, particle size, and particle shape of fixed-bearing total ankle arthroplasty conventional polyethylene versus highly cross-linked polyethylene. The lower wear rate and different particle size/morphology of highly cross-linked polyethylene could be beneficial in vivo to decrease osteolysis.

Keywords

osteolysis highly cross-linked polyethylene conventional polyethylene wear ankle arthroplasty ankle replacement ankle arthritis

Get full access to this article

View all access options for this article.

References

Affatato

Goldoni

Testoni

Toni

Mixed oxides prosthetic ceramic ball heads. Part 3: effect of the ZrO₂ fraction on the wear of ceramic on ceramic hip joint prostheses. A long-term in vitro wear study. Biomaterials. 2001;22(7):717-723.

Affatato

Leardini

Giannini

Viceconti

Meniscal wear at a three-component total ankle prosthesis by a knee joint simulator. J Biomech. 2007;40(8):1871-1876.

Affatato

Vandelli

Bordini

Toni

Fluid absorption study in ultra-high molecular weight polyethylene (UHMWPE) sterilized and unsterilized acetabular cups. Proc Inst Mech Eng H. 2001;215(1):107-111.

Bell

Fisher

Simulation of polyethylene wear in ankle joint prostheses. J Biomed Mater Res B Appl Biomater. 2007;81(1):162-167.

Bischoff

Fryman

Parcell

Orozco Villasenor

DA.

Influence of crosslinking on the wear performance of polyethylene within total ankle arthroplasty. Foot Ankle Int. 2015;36(4):369-376.

Dalat

Barnoud

Fessy

Besse

; French Association of Foot Surgery AFCP. Histologic study of periprosthetic osteolytic lesions after AES total ankle replacement. A 22 case series. Orthop Traumatol Surg Res. 2013;99(6)(suppl):S285-S295.

Glyn-Jones

Isaac

Hauptfleisch

et al . Does highly cross-linked polyethylene wear less than conventional polyethylene in total hip arthroplasty? A double-blind, randomized, and controlled trial using roentgen stereophotogrammetric analysis. J Arthroplasty. 2008;23(3):337-343.

Kadoya

Revell

al-Saffar

et al . Bone formation and bone resorption in failed total joint arthroplasties: histomorphometric analysis with histochemical and immunohistochemical technique. J Orthop Res. 1996;14(3):473-482.

Kobayashi

Freeman

Bonfield

et al . Number of polyethylene particles and osteolysis in total joint replacements. A quantitative study using a tissue-digestion method. J Bone Joint Surg Br. 1997;79(5):844-848.

10.

Kobayashi

Minoda

Kadoya

et al . Ankle arthroplasties generate wear particles similar to knee arthroplasties. Clin Orthop Relat Res. 2004;424:69-72.

11.

Matthews

Besong

Green

et al . Evaluation of the response of primary human peripheral blood mononuclear phagocytes to challenge with in vitro generated clinically relevant UHMWPE particles of known size and dose. J Biomed Mater Res. 2000;52(2):296-307.

12.

McCalden

MacDonald

Rorabeck

et al . Wear rate of highly cross-linked polyethylene in total hip arthroplasty. A randomized controlled trial. J Bone Joint Surg Am. 2009;91(4):773-782.

13.

McKellop

Shen

DiMaio

Lancaster

JG.

Wear of gamma-crosslinked polyethylene acetabular cups against roughened femoral balls. Clin Orthop Relat Res. 1999;369:73-82.

14.

Muratoglu

Mark

Vittetoe

Harris

Rubash

HE.

Polyethylene damage in total knees and use of highly crosslinked polyethylene. J Bone Joint Surg Am. 2003;85(suppl 1):S7-S13.

15.

Nakashima

Sun

Trindade

et al . Signaling pathways for tumor necrosis factor-alpha and interleukin-6 expression in human macrophages exposed to titanium-alloy particulate debris in vitro. J Bone Joint Surg Am. 1999;81(5):603-615.

16.

Oral

Christensen

Malhi

Wannomae

Muratoglu

OK.

Wear resistance and mechanical properties of highly cross-linked, ultrahigh-molecular weight polyethylene doped with vitamin E. J Arthroplasty. 2006;21(4):580-591.

17.

Popoola

Yao

Johnson

Blanchard

CR.

Wear, delamination, and fatigue resistance of melt-annealed highly crosslinked UHMWPE cruciate-retaining knee inserts under activities of daily living. J Orthop Res. 2010;28(9):1120-1126.

18.

Reggiani

Leardini

Corazza

Taylor

Finite element analysis of a total ankle replacement during the stance phase of gait. J Biomech. 2006;39(8):1435-1443.

19.

Schipper

Haddad

Pytel

Zhou

Histological analysis of early osteolysis in total ankle arthroplasty. Foot Ankle Int. 2017;38(4):351-359.

20.

Scott

Morrison

Mishra

Jani

Particle analysis for the determination of UHMWPE wear. J Biomed Mater Res B Appl Biomater. 2005;73(2):325-337.

21.

Sieving

Mayton

Nasser

Wooley

PH.

Morphological characteristics of total joint arthroplasty-derived ultra-high molecular weight polyethylene (UHMWPE) wear debris that provoke inflammation in a murine model of inflammation. J Biomed Mater Res A. 2003;64(3):457-464.

22.

Thomas

Simpson

Mehmood

et al . The seven-year wear of highly cross-linked polyethylene in total hip arthroplasty: a double-blind, randomized controlled trial using radiostereometric analysis. J Bone Joint Surg Am. 2011;93(8):716-722.

23.

Utzschneider

Paulus

Datz

et al . Influence of design and bearing material on polyethylene wear particle generation in total knee replacement. Acta Biomater. 2009;5(7):2495-2502.

24.

White

Paxson

Tanner

Whiteside

LA.

Effects of sterilization on wear in total knee arthroplasty. Clin Orthop Relat Res. 1996;331:164-171.

Supplementary Material

Please find the following supplemental material available below.

For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.

For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.

0.00 MB

0.21 MB