Identification of the evolution of the damage variable, D, in continuum creep damage theory was developed directly from the metallographical A-parameter. As the observed fraction of cavitated grain boundaries on the observation plane, A-parameter was first related to the cavity area fraction on the grain boundary facet planes by perform ing a probability analysis. Then, two specific A-D relations were obtained corresponding to the instantaneous and continuous nucleation of cavities, respectively. An A-D relation of more generality was also derived from one of the proposed A-D relations by using the Kachanov-Rabotnov creep damage theory. Finally, the creep damage behavior of a practi cal alloy was identified from A-parameter by using the developed A-D relations in addition to the previous one. Some comparisons and discussions were made based on the test results of this alloy.
Murakami, S.1987. "Progress of Continuum Damage Mechanics," JSME Int. J. , 30:701-710.
6.
Chaboche, J.L.1988. "Continuum Damage Mechanics: Part I-General Concepts, Part II-Damage Growth, Crack Initiation, and Crack Growth" ASME J. Appl. Mech. , 55:59-72.
7.
Kachanov, L.M.1958. "On Rupture Time under Creep Conditions," Izv. Akad. Nauk. ,SSSR. Otd. Tekh. Nauk, 8:26-31.
8.
Leckie, F.A. and D.R. Hayhurst.1974. "Creep Rupture of Structures;" Proc. R. Soc. Lond. , Ser. A, 340:323-347.
9.
Hayhurst, D.R. , P.R. Dimmer and C.J. Mornson.1984. "Development of Continuum Damage in the Creep Rupture of Notched Bars ," Phil. Trans. R. Soc. Lond., A311:103-129.
10.
Hayhurst, D.R. , P.R. Brown and C.J. Morrison.1984. "The Role of Continuum Damage in Creep Crack Growth;" Phil. Trans. R. Soc. Lond. , A311:131-158.
11.
Murakami, S. and N. Ohno.1981. "A Continuum Theory of Creep and Creep Damage," in Creep in Structures, A. R. S. Ponter and D. R. Hayhurst, eds., Berlin: Springer, pp. 422-444.
12.
Murakami, S.1988. "Mechanical Modeling of Material Damage," ASME J. Appl. Mech., 55:280-286.
13.
Chaboche, J.L.1984. 'Anisotropic Creep Damage in the Framework of Continuum Damage Mechanics," Nuclear Engng. Des. , 79:309-319.
14.
Saanouni, K. , J.L. Chaboche and C. Bathias.1986. " On the Creep Crack Growth Predicted by a Local Approach," Engng. Fract. Mech. , 25:677-691.
15.
Murakami, S. , M. Kawai and H. Rong.1988. "Finite Element Analysis of Creep Crack Growth by a Local Approach," Int. J. Mech. Sci. , 30:491-502.
16.
Tvergaard, V.1984. "Constitutive Relations for Creep in Polycrystals with Gram-Boundary Cavitation," Acta, Metall., 32:1977-1990.
17.
Cocks, A.C.F. and F.A. Leckie.1987. "Creep Constitutive Equations for Damaged Materials," in Advances in Appl. Mech. , T. Y. Wu and J. W. Hutchinson, eds., 25:239-294.
18.
Shammas, M.S.1988. "Metallographic Methods for Predicting the Remanent Life of Ferritic Coarse-Grained Weld Heat Affected Zones Subject to Creep Cavitation," Int. Conf. on Life Assessment, VGB, KEMA, EPRI, Essen, Arnhem, Palo Alto, 1988 .
19.
Viswanathan, R.1989. Damage Mechanisms and Life Assessment of High-Temperature Components. ASM International .
20.
Kadoya, Y., H. Karato, T. Goto, Y. Kadoya and K. Kawamoto1988. "State-of-the-Art NDE Techniques for Crack-Initiation Life Assessment of High-Temperature Rotors," Int. Conf. on Life Assessment and Extension, Hague, Paper 2.1.2, pp. 9-19.
21.
Cane, B.J. and M.S. Shammas.1984. "A Method for Remanent Life Estimation by Quantitative Assessment of Creep Cavitation on Plant," CEGB Report TPRD/L/2645/N84.
22.
Shammas, M.S.1987. "Predicting the Remanent Life of 1Cr1/2Mo Coarse-Grained Heat Affected Zone Material by Quantitative Cavitation Measurements," CEGB Report TPRD/ L/3199/R87.
Dyson, B.F.1976. "Constraints on Diffusional Cavity Growth Rates," Metal Sci. , 10:349-353.
25.
Dyson, B.F. and D. McLean.1977. "Creep of Nimonic 80A in Torsion and Tension," Metal Sci. , 11:37-46.
26.
Riedel, H.1985. "Continuous Nucleation of Grain Boundary Cavities in Creep Rupture," Zeit. Metallk., 76:669-675.
27.
Wilkinson, D.S.1987. "The Effect of Time-Dependent Void Density on Gram Boundary Creep Fracture-II. Continuous Nucleation ," Acta Metall. , 35:2791-2799.
28.
Ashby, M.F. and B.F. Dyson.1984. "Creep Damage Mechanics and Micromechanisms ," Proc. of ICF-4, New Delhi, 1:3-30.