Electromigration and thermomigration reliability of Sn96.5%Ag3.0%Cu0.5 (SAC305 by weight) solder joints under alternating current is studied experimentally with the maximum current density from 2.1 × 105 A/cm2 to 1.76 × 106 A/cm2, and frequency from 100 kHz to 4 MHz. During the experiment, hot spots are observed at current crowding corners and the skin layer of solder joints. As a result, highly localized current density and joule heating exist. The combined effect of electron wind force and thermal gradient drives mass to diffuse toward the center of solder joints. Resistance change due to temperature change and current crowding was carefully recorded. Ten percent resistance change after thermal steady state was defined as failure. Scanning electron microscopic images show void formation in current crowding corners and in the skin layer of solder joints. Damage of solder joints under alternating current stressing is observed a combined process of both electromigration and thermomigration, and to be proportional to the loading frequency and current density. Owing to the reversed electron wind force, material healing is observed in most of our test vehicles. A statistical mean time to failure equation is proposed for lead-free solder joints under alternating current stressing.
AbdulhamidMFLiSBasaranC (2008) Thermomigration in lead-free solder joints. International Journal of Materials and Structural Integrity, 2: 11–34.
2.
AbdulhamidMFBasaranC (2009) Influence of thermomigration on lead-free solder joint mechanical properties. ASME Journal of Electronic Packaging, 131(12): 011002–011002.
3.
AmiriMNaderiMKhonsariMM (2011) An experimental approach to evaluate the critical damage. International Journal of Damage Mechanics, 20(1): 89–112.
4.
Aronstein J (1996a) AC and DC electromigration in aluminum. In: Proceedings of the 42nd IEEE Holm conference on electrical contacts. Joint with the 18th international conference on electrical contacts, 16–20 September 1996. New York: IEEE.
5.
Aronstein J (1996b) AC and DC electromigration in aluminum contact junctions. In: Proceedings of the 1996 42nd IEEE Holm conference on electrical contacts joint with the 18th international conference on electrical contacts, Chicago, IL, USA, 16 September––20 September 1996.
6.
BasaranCGomezJLinM (2007) Damage mechanics modeling of concurrent thermal and vibration loading on electronics packaging. Multidiscipline Modeling in Materials and Structures, 2: 309–326.
7.
BasaranCYanC (1998) A thermodynamic framework for damage mechanics of solder joints. Journal of Electronic Packaging, 120: 379–384.
8.
BasaranCJiangJ (2002) Measuring intrinsic elastic modulus of Pb/Sn solder alloys. Mechanics of Materials, 34: 349–362.
9.
BasaranCLinM (2007) Damage mechanics of electromigration in microelectronics copper interconnects. International Journal of Materials and Structural Integrity, 1: 16–39.
10.
BasaranCLinM (2008) Damage mechanics of electromigration induced failure. Mechanics of Materials, 40(1–2): 66–79.
11.
BasaranCWenY (2003) Coarsening in BGA solder balls: modeling and experimental evaluation. Journal of Electronic Packaging, 125(3): 426–430.
BasaranCLiSHopkinsDC (2009a) Electromigration time to failure of SnAgCuNi solder joints. Journal of Applied Physics, 106(1): 013707–013707–10.
14.
BasaranCLinMYeH (2003) A thermodynamic model for electrical current induced damage. International Journal of Solids and Structures, 40(26): 7315–7327.
15.
BasaranCLiSAbdulhamidMF (2008) Thermomigration induced degradation in solder alloys. Journal of Applied Physics, 103(12): 123520–9.
16.
BasaranCLiSHopkinsDCVeychardD (2009b) Electromigration time to failure of SnAgCuNi solder joints. Journal of Applied Physics, 106: 013707–013707.
17.
Basaran C, Li S, Hopkins DC, et al. (2012) Mean time to failure of SnAgCuNi solder joints under DC. In: 13th IEEE intersociety conference on thermal and thermomechanical phenomena in electronic systems (ITherm), 2012.
18.
BasaranCYeHHopkinsDC (2005a) Failure modes of flip chip solder joints under high electric current density. Journal of Electronic Packaging, 127(2): 157–163.
19.
BasaranCZhaoYTangH (2005c) A damage-mechanics-based constitutive model for solder joints. Journal of Electronic Packaging, 127: 208–214.
20.
BastawrosAFKimK-S (2001) Electric-current induced crack growth in thin films: experimental observations and continuum description. International Journal of Damage Mechanics, 10(3): 195–213.
21.
ChaungCMLinKL (2003) Effect of microelements addition on the interfacial reaction between Sn-Ag-Cu solders and the Cu substrate. Journal of Electronic Materials, 32(12): 1426–1431.
22.
ChengY-WSiewertT (2003) Predicting tensile properties of the bulk 96.5Sn-3.5Ag lead-free solder. Journal of Electronic Materials, 32(6): 535–540.
23.
DariavachNCallahanPLiangJ (2006) Intermetallic growth kinetics for Sn-Ag, Sn-Cu, and Sn-Ag-Cu lead-free solders on Cu, Ni, and Fe-42Ni substrates. Journal of Electronic Materials, 35(7): 1581–1592.
24.
EnglishATTaiKLTurnerPA (1972) Electromigration in conductor stripes under pulsed dc powering. Applied Physics Letters, 21(8): 397–398.
25.
Hatanaka K, Noguchi T and Maeguchi K (1989) A generalized lifetime model for electromigration under pulsed DC/AC stress conditions. In: 1989 symposium on VLSI technology. Digest of Technical Papers (Cat. No.89CH2694–8), 22–25 May 1989. Tokyo: Business Center for Academic Societies Japan.
26.
HsiaoH-YChenC (2009) Thermomigration in Pb-free SnAg solder joint under alternating current stressing. Applied Physics Letters, 94: 092107–092107.
27.
JiangTCheungNWChenmingH (1994) An electromigration failure model for interconnects under pulsed and bidirectional current stressing. IEEE Transactions on Electron Devices, 41(4): 539–545.
28.
LeeTYTuK-NKuoSM (2001) Electromigration of eutectic SnPb solder interconnects for flip chip technology. Journal of Applied Physics, 89(6): 3189–3194.
29.
LiSBasaranC (2009) A computational damage mechanics model for thermomigration. Mechanics of Materials, 41(3): 271–278.
30.
LiSAbdulhamidMFBasaranC (2008a) Simulating damage mechanics of electromigration and thermomigration. Simulation, 84(8–9): 391–401.
31.
LiSAbdulhamidMFBasaranC (2008b) Damage mechanics of low temperature electromigration and thermomigration. IEEE Transactions on Advanced Packaging, 32: 478–485.
32.
Liew B-K, Cheung NW and Hu C (1989) Electromigration interconnect lifetime under AC and pulse DC stress. In: 27th annual proceedings of reliability physics (Cat. No.89CH2650-0), 11–13 April 1989. New York: IEEE.
33.
LinMBasaranC (2005) Electromigration induced stress analysis using fully coupled mechanical-diffusion equations with nonlinear material properties. Computational Materials Science, 34(1): 82–98.
34.
Shingubara S, Oshima K, Ting H, et al. (2004) Pulsed DC and AC electromigration studies of Cu dual damascene interconnects. In: Seventh international workshop on stress-induced phenomena in metallization, 14–16 June 2004. College Park, MD: AIP.
35.
Su P and Li L (2009) A comparison study of electromigration performance of Pb-free flip chip solder bumps. In: 59th electronic components and technology conference, May 2009, pp. 903–908.
36.
TangHBasaranC (2001) Influence of microstructure coarsening on thermomechanical fatigue behavior of Pb/Sn eutectic solder joints. International Journal of Damage Mechanics, 10(3): 235–255.
37.
Tao J (1996) Electromigration design rules for bidirectional current. In: Proceedings of international reliability physics symposium, 30 April–2 May 1996. New York: IEEE.
38.
TaoJCheungNWHuC (1993b) Metal electromigration damage healing under bidirectional current stress. IEEE Electron Device Letters, 14: 554–556.
39.
TaoJYoungKKCheungNW (1993a) Electromigration reliability of tungsten and aluminum vias and improvements under AC current stress. IEEE Transactions on Electron Devices, 40: 1398–1405.
40.
TaoJLiewB-KChenJF (1998) Electromigration under time-varying current stress. Microelectronics Reliability, 38: 295–308.
41.
Tao J, Cheung NW and Hu C (1997) Electromigration failures under bidirectional current stress. In: 4th international workshop on stress induced phenomena in metallization, 4–6 June 1997. College Park, MD: AIP.
42.
Ting L, May J, Hunter W, et al. (1993) AC electromigration characterization and modeling of multilayered interconnects. In: Proceedings of IEEE international reliability physics symposium, 23–25 March 1993. New York: IEEE.
43.
TuK-N (2007) Solder Joint Technology: Materials, Properties, and Reliability, New York: Springer.
44.
WuWHPengSPLinCS (2009) Study of DC and AC electromigration behavior in eutectic Pb-Sn solder joints. Journal of Electronic Materials, 38: 2184–2193.
45.
Yao W and Basaran C (2012a) Skin effect and material degradation of lead-free solder joint under AC. In: 13th IEEE intersociety conference on thermal and thermomechanical phenomena in electronic systems (ITherm) ITherm 2012, San Diego, CA, May 30–June 1, 2012.
46.
YaoWBasaranC (2012b) Electromigration analysis of solder joints under AC load: a mean time to failure model. Journal of Applied Physics, 111(6): 063703–063703.
47.
YaoWBasaranC (2012c) Reduced impedance and superconductivity of SnAgCu solder alloy at high frequency. Electronic Materials Letters, 8(5): 503–505.
48.
Yao W and Basaran C (2013a) Electromigration in lead-free solder joints under high frequency pulsed current: an experimental study. Int J of Damage Mechanics. Epub ahead of print 12 March 2013. DOI: 10.1177/1056789513477668.
49.
YaoWBasaranC (2013b) Electromigration damage mechanics of lead-free solder joints under pulsed DC: a computational model. Computational Materials Science, 71(0): 76–88.
50.
YeH (2004) Mechanical Behavior of Microelectronics and Power Electronics Solder Joints under High Current Density: Analytical Modeling and Experimental Investigation, Buffalo: State University of New York.
51.
YeHBasaranCHopkinsDC (2003) Thermomigration in Pb-Sn solder joints under joule heating during electric current stressing. Applied Physics Letters, 82(7): 1045–1047.
52.
YeHBasaranCHopkinsDC (2004a) Mechanical implications of high current densities in flip-chip solder joints. International Journal of Damage Mechanics, 13(4): 335–345.
53.
YeHBasaranCHopkinsDC (2004b) Pb phase coarsening in eutectic Pb/Sn flip chip solder joints under electric current stressing. International Journal of Solids and Structures, 41(9–10): 2743–2755.
54.
YeHBasaranCHopkinsDC (2006) Experimental damage mechanics of micro/power electronics solder joints under electric current stresses. International Journal of Damage Mechanics, 15(1): 41–67.
55.
YeHBasaranCHopkinsDC (2008) Experimental damage mechanics of micro/power electronics of solder joints under electrical current stresses. International Journal of Damage Mechanics, 15: 28–28.
56.
YoonJ-WLeeC-BJungS-B (2003) Growth of an intermetallic compound layer with Sn-3.5Ag-5Bi on Cu and Ni-P/Cu during aging treatment. Journal of Electronic Materials, 32(11): 1195–1202.
57.
You H-N, Kim B-J and Joo Y-C (2009) Electromigration behavior of micro SN bump under pulsed DC. In: 2009 IEEE international reliability physics symposium, IRPS 2009, 26 April–30 April 2009. Montreal, Canada: Institute of Electrical and Electronics Engineers Inc.
58.
ZhangFLiMBalakrisnanB (2002) Failure mechanism of lead-free solder joints in flip chip packages. Journal of Electronic Materials, 31(11): 1256–1263.