An Intelligent Degradable Polymer Composite Which Closely Matches Bone

Abstract

Polyhydroxybutyrate (PHB) and its copolymers with polyhydroxyvalerate (PHV) are a range of slowly degrading polyesters with potential for use in orthopaedic surgery. The polymer degradation profile is unpredictable and thus a composite of PHB/7 % PHV and a completely soluble phosphate based glass reinforcement was compounded. This glass may be produced with a defined solubility rate and this was shown to control the overall degradation of the PHB/glass composite, in terms of both mass loss and change in mechanical properties. The piezoelectric properties of the composite were examined and the strain generated potentials were seen to be of a similar order of magnitude to that of bone. In vivo studies were carried out and as with the in vitro work, the reaction could be closely correlated with the composite solubility. Furthermore, tissue reaction at various stages could be closely linked to the composite solubility.

Get full access to this article

View all access options for this article.

References

Baptist, J.N. and F.X. Werber. 1964. "Poly(B-Hydroxybutyric Acid), Naturally Occurnng Thermo-Plastic Material", Soc. Plast. Eng. Trans. , 4:245-250.

Bos, R.R.M. , G. Boenng , F.R. Rozema and J.W. Leenslag. 1987. "Resorbable Poly(L-Lactide) Plates and Screws for the Fixation of Zygomatic Fractures", J. Oral Maxillofac. Surg., 45:751-753.

Bostman, O. , E. Hirvensalo , J. Makinen and P. Rokkanen. 1990. "Foreign Body Reactions to Fracture Fixation Implants of Biodegradable Synthetic Polymers", J. Bone Jt. Surg., 72-B(4):592-596.

Burme, J. 1982. "Controlled Release Glass (CRG)-A New Biomatenal ", Ph.D. thesis, University of Strathclyde.

Hastings, G.W. , F.A. Mahmud and M. Martini. 1989. "Non-Contacting Electrode System for the Measurement of Strain Generated Potentials in Bone,"J. Biomed. Eng. , 11(5):403-408.

Knowles, J.C. and G.W. Hastings. 1992. "In vitro Degradation of a Polyhydroxybutyrate/Polyhydroxyvalerate Copolymer", J. Mat. Sci. Mat. in Med. , 3:352-358.

Knowles, J.C. , F.A. Mahmud and G.W. Hastings. 1991. "Piezoelectric Characteristics of a Polyhydroxybutyrate-Based Composite", Clin. Mat., 8:155-158.

Leenslag, J.W. , A.J. Pennings , R.R.M. Bos , F.R. Rozema and G. Boering. 1987. "Resorbable Materials of Poly(L-Lactide) VII. In vivo and in vitro Degradation", Biomaterials, 8:311-314.

Santavirta, S. , Y.T. Konttinen , T. Saito , M. Gronblad , E. Partio , P. Kemppinen and P. Rokkanen. 1990. "Immune Response to Polyglycolic Acid Implants ; J. Bone Jt. Surg., 72-B(4):597-600.

10.

Tanner, K.E. , C. Doyle and W. Bonfield. 1990. "The Strength of the Interface Developed between Biomaterials and Bone", in Advances in Biomaterials , Vol. 9, G. Heimke , U. Soltesz and A. J. C. Lee , eds., Amsterdam. Elsevier Science Publishers B.V.

11.

Tormala, P. , J. Vasemus , S. Vaimonpaa , J. Laiho , T. Pohjonen and P. Rokkanen. 1991. "Ultra High Strength Absorbable Self Reinforced Polyglycolide (SR-PGA) Composite Rods for Internal Fixation of Bone Fractures: m vitro and in vivo Study", J. Biomed. Mat. Res. , 25:1-22.