Enzymatic hydrolysis (EH) lignin was utilized to replace phenol partially for preparing phenol-formaldehyde (PF) resin adhesives. The influence of the degree of lignin substitution on the properties of the lignin phenol-formaldehyde (LPF) resin adhesive was investigated. The results demonstrated that up to 50% of phenol in the resin could be replaced by EH lignin without damaging the bonding strength of the adhesive, and a lower free phenol content was observed in LPF resin adhesives. Fourier transform infrared spectroscopy spectra of the resins revealed that the introduction of lignin did not appreciably change the final chemical structure of the adhesive, but did negatively impact the resin's thermal ultimate stability. Furthermore, compared to bio-ethanol production residue-modified phenol-formaldehyde (ERPF) resin, the LPF resin exhibited higher bonding strength at the same level of the phenol substitution. This result of the comparison indicated that the raw biomass extraction process improved the performance of the bio-based PF resin.
HiguchiT.Biosynthesis of lignin. Biosynthesis and biodegradation of wood components Academic Press, New York.1985, 141 pp.
4.
DanielsonB., SimonsonR.Kraft lignin in phenol formaldehyde resin. Part 1. Partial replacement of phenol by kraft lignin in phenol formaldehyde adhesives for plywood. J Adhes Sci Technol. 1998, 12, 923–939.
CetinNS., ÖzmenN.Use of organosolv lignin in phenol–formaldehyde resins for particleboard production: I. Organosolv lignin modified resins. Int J Adhes Adhes2002, 22, 477–480.
7.
ChengS., YuanZ., LeitchM., AndersonM., XuCCHighly efficient de-polymerization of organosolv lignin using a catalytic hydrothermal process and production of phenolic resins/adhesives with the depolymerized lignin as a substitute for phenol at a high substitution ratio. Ind Crop Prod. 2013, 44, 315–322.
8.
DomínguezJ., OlietM., AlonsoM., RojoE., RodríguezF.Structural, thermal and rheological behavior of a bio-based phenolic resin in relation to a commercial resol resin. Ind Crop Prod. 2013, 42, 308–314.
9.
PérezJ. M., RodriguezF., AlonsoM. V., OlietM., EcheverríaJ. M.Characterization of a novolac resin substituting phenol by ammonium lignosulfonate as filler or extender. Bioresources. 2007, 2, 270–283.
10.
JinY., RuanX., ChengX., LüQ.; Liquefaction of lignin by polyethyleneglycol and glycerol. Bioresource Technol. 2011, 102, 3581–3583.
LüQ. F., HuangZ. K., LiuB., ChengX.Preparation and heavy metal ions biosorption of graft copolymers from enzymatic hydrolysis lignin and amino acids. Bioresource Technol.2012, 104, 111–118.
13.
ZhangW., MaY., WangC., LiS., ZhangM., ChuF.Preparation and properties of lignin–phenol–formaldehyde resins based on different biorefinery residues of agricultural biomass. Ind Crop Prod. 2013, 43, 326–333.
14.
PérezS., SamainD.Structure and engineering of celluloses. Adv Carbohyd Chem Bi. 2010, 64, 25–116.
15.
ZhangT., ZhouY., LiuD., PetrusL.Qualitative analysis of products formed during the acid catalyzed liquefaction of bagasse in ethylene glycol. Bioresource Technol.2007, 98, 1454–1459.
16.
GuoG., LiS., WangL., RenS., FangG.Separation and characterization of lignin from bio-ethanol production residue. Bioresource Technol.2013, 135, 738–741.
17.
MansouriN. E. E., SalvadóJ.Structural characterization of technical lignins for the production of adhesives: application to lignosulfonate, kraft, soda-anthraquinone, organosolv and ethanol process lignins. Ind Crop Prod.2006, 24, 8–16.
18.
KhanM., AshrafS.Studies on thermal characterization of lignin. J Therm Anal Calorim.2007, 89, 993–1000.
19.
WangM., WeiL., ZhaoT.Cure study of addition-cure-type and condensation–addition-type phenolic resins. Eur Polym J.2005, 41, 903–912.
20.
KhanM. A., AshrafS.M., MalhotraV. P.Development and characterization of a wood adhesive using bagasse lignin. Int J Adhe Adhes.2004, 24, 485–493.
21.
GabilondoN., LópezM., RamosJ., EcheverríaJ., MondragonI.Curing kinetics of amine and sodium hydroxide catalyzed phenol-formaldehyde resins. J Therm Anal Calorim.2007, 90, 229–236.
22.
AlonsoM., OlietM., PérezJ., RodrıguezF., EcheverrıaJ.Determination of curing kinetic parameters of lignin–phenol–formaldehyde resol resins by several dynamic differential scanning calorimetry methods. Thermochim Acta.2004, 419, 161–167
23.
TurunenM., AlvilaL., PakkanenT.T., RainioJ.Modification of phenol–formaldehyde resol resins by lignin, starch, and urea. J Appl Polym Sci. 2003, 88, 582–588.
24.
WangM., LeitchM., XuC.Synthesis of phenol–formaldehyde resol resins using organosolv pine lignins. Eur Polym J.2009, 45, 3380–3383.