Liquid silicone rubber (LSR) vulcanizates have been prepared from vinyl-end capped polydimethylsiloxane (PDMS) and polymethylhydrogenosiloxane (PMHS) in presence of platinum catalyst using solution casting technique. The science involving synthesis of usable silicone rubber by curing with polymethylhydrogenosiloxane has been studied in details. The effects of vinyl content of PDMS and the ratio of hydride crosslinker to vinyl concentration on crosslink density, mechanical, dynamic-mechanical and thermal properties have been discussed. It has been found that at optimum level of crosslinker, the LSR vulcanizate shows a maximum crosslink density with highest improvement in mechanical and thermal properties. The amount of crosslinker required, depends upon the number of vinyl functionality per unit length of the polymer chain and the chemical composition of the hydride crosslinker. This study makes a novel attempt to determine cure kinetics of PDMS by using Fourier Transform Infrared spectroscopy. Measurements have been done at three different temperatures and found to follow the first order reaction with respect to consumption of vinyl (C=C) and silyl hydride groups (Si-H). The activation energy and kinetic parameters have been determined as well.
References
1.
BhowmickA.K., and StephensH.L., Handbook of Elastomers, 2nd edn.Marcel Dekker, New York, (2001), p. 605–615.
2.
LynchW., Handbook of Silicone Rubber Fabrication, Reinhold Company, New York, (1978) p. 1–25.
3.
MortonM., Rubber Technology, Reinhold Company, New York, (1985), p. 378–408.
4.
LewisF.M., The science and technology of silicone rubber, Rubber Chem. Technol., 35 (1962), 1222–1275.
MarciniecB., Hydrosilylation: A Comprehensive Review on Recent Advances, Silicone Chem.1 (2002), 155–175.
7.
JosephS.C., Polymeric Encyclopedia Vol. 10 (Q-S); C.R.C: New York, (2002), pp 7663–7676.
8.
SpeierJ.L., WebsterJ.A., and BarnesG.H., The Addition of Silicon Hydrides to Olefinic Double Bonds. Part II. The Use of Group VIII Metal Catalysts, J. Amer. Chem. Soc.79 (1956), 974–979.
9.
KarstedtB.D., and ScotiaN.Y., Platinum Complexes of Unsaturated Siloxanes and Platinum Containing Organosiloxanes, U. S. Patent 3,775452 (1974).
10.
WillingD.N., Catalysts for the Reaction of SiH with Organic Compounds Containing Aliphatic Unsaturation U. S. Patent 3,419,593 (1974).
11.
NielsonJ.M., Halocarbon Catalyst Inhibitors for Reactive Organosilicone Compositions U.S. Patent 3,383,356 (1968).
12.
KookootsedesG.J., U. S. Patent 3,453,234 (1969).
13.
KookootsedesG.J., and PlueddemannE.P., Acetylenic Inhibited Platinum Catalyzed Organopolysiloxane Composition U. S. Patent 3,445,420 (1969).
14.
BobearW.J., and LathamN.Y., Inhibitor for Platinum Catalyzed Silicone Rubber Compositions U. S. Patent 4,061,609 (1977).
15.
BrookM.A., Platinum in silicone breast implants, Biomater.27 (2006), 3274–3286.
16.
JiaY., SunS., LiuL., MuY., and AnL., Design of silicone rubber according to requirements based on the multi-objective optimization of chemical reactions, Acta Mater, 52 (2004), 4153–4159.
17.
JiaY., WangX., FengL., and AnL., Integrated processing-structure-property analysis on rubber in-mold vulcanization, European Polymer Journal, 45 (2009) 1759–1764
18.
JiaY., SunS., LiuL., and JiZ., Finite element simulation of mechanical property evolvement of silicone rubber in the hot vulcanizing process, Polym. Int., 53 (2004), 41–47.
19.
PolmanteerK.E., and LentzC.W., Reinforcement studies–effect of silica structure on properties and crosslink density, Rubber Chem. Technol., 60 (1988), 795–809.
20.
ZhaoS., and FengS., Vinyl-containing silicone resin as the crosslinking agent of heat-curable silicone rubber, J. Appl. Polym. Sci., 83 (2002), 3123–3127.
21.
RoyA.K., and TaylorR.B., The first alkene-platinum-silyl complexes: Lifting the hydrosilation mechanism shroud with long-lived precatalytic intermediates and true Pt catalysts, J. Amer Chem. Soc, 124 (2002), 9510–9524.
22.
CancouetP., PerninS., HelaryG., and SauvetG., Functional polysiloxanes. II. Neighboring effect in the hydrosilylation of poly(hydrogenmethylsiloxane-co-dimethylsiloxane)s by allylglycidylether, J. Polym. Sci. Part A: Polym. Chem., 38 (2000), 837–845.
23.
HirojiE., KatsuyoshiN., and OsamuT., Curable Organopolysiloxane Gel Composition. European Patent EP 0509515 A1 (1992).
24.
HiroshiI., ShinichiS., TakashiM., and HirolumiK., Curable silicone composition. European Patent EP 0527008 A1(1993).
25.
LewisL.N., Method for Making a Platinum Hydrosilylation Catalyst European Patent EP 0979837A2, (1999).
26.
BilgrienC.J., LutzM.A., and NgugenB.T., Curable Compositions Containing an Anaerobically Inactive Hydrosilation Catalyst and Method for Preparing and Composition U. S. Patent 5,364,922, (1994).
27.
McAfeeR.J., AdkinsJ.R., GetsonJ.C., Platinum Catalyst and a Curable Organopolysiloxane Composition Containing Said Platinum Catalyst U. S. Patent 5,525, 564(1996).
28.
MaxsonT.M., and MillerL.W., Method for controlling cure initiation and curing times of platinum group metal curing fluorosilicone compositions, U. S. Patent 5,665,794, (1997).
29.
MajiP.K., and BhowmickA.K., Influence of number of functional groups of hyperbranched polyol on cure kinetics and physical properties of polyurethanes, J. Polym. Sci. Part A: Polym. Chem., 47 (2009), 731–745.
30.
BiswasA., BandyopadhyayA., SinghaN.K., and BhowmickA.K., Chemical modification of metallocene-based polyolefinic elastomers by acrylic acid and its influence on physico-mechanical properties: Effect of reaction parameters, crystallinity and pendant chain length, J. Polym. Sci. Part A: Polym. Chem., 45 (2007), 5529–5540.
31.
SarkarM.D., DeP.P., and BhowmickA.K., Influence of Styrene Content on the Hydrogenation of Styrene-Butadiene Copolymer, J. Appl. Polym. Sci., 71 (1999), 1581–1595.
32.
PuskasJ.E., KwonY., AntonyP., and BhowmickA.K., Synthesis and characterization of novel dendritic (arborescent, hyperbranched) polyisobutylene-polystyrene block copolymers, J. Polym. Sci. Part A: Polym. Chem., 43 (2005), 1811–1826.
33.
DattaH., SinghaN.K., and BhowmickA.K., Beneficial effect of nanoclay in atom transfer radical polymerization of ethyl acrylate: A one pot preparation of tailor-made polymer nanocomposite, Macromolecules, 41 (2008), 50–57.
34.
ArangurenM.I., Crystallization of polydimethylsiloxane: effect of silica filler and curing. Polymer, 39 (1998), 4897–4901.
35.
BhowmickA.K., HallM.A., and BenareyH.A., Rubber Products Manufacturing Technology, Marcel Dekker, New York, (1994) p. 317–320.
36.
FloryP.J., and RehnerJ.H., Statistical Mechanics of Cross-Linked Polymer Networks II. Swelling, J. Chem. Phys., 11 (1943), 521–530.
37.
SargentR.J., and WeberP.W., End Group Analysis Accounts for the Low Molecular Weight Observed in the 1,3-Divinyltetramethyldisiloxane-Pt Complex Catalyzed Hydrosilylation Copolymerization of α,ω-Dienes and 1,3-Dihydridotetramethyldisiloxane, Macromolecules, 32 (1999), 2826–2829.
38.
ArklesB.C., Curable silicone containing compositions and methods of making same, US Patent 4,500,688 (1985).
39.
SierawskiD.A., Method of preventing discoloration of platinum containing silicone gels, US Patent 4,122,246 (1978).
40.
HofmannW., Vulcanization and Vulcanizing Agents, Maclaren Sons, London, p. 326–333 (1967).
41.
BurnsideD.S., and GiannelisE.P., Nanostructure and Properties of Polysiloxane-Layered Silicate Nanocomposites, J. Polym. Sci. Part B: Polym. Phys., 38 (2000), 1595–1604.
42.
YimA., and ChahalR.S., The effect of polymer—filler interaction energy on the T′g of filled polymers, J. Colloid. Inter Sci., 43 (1973), 583–590.
43.
KoleS., BhattacharyaA., TripathyD.K., and BhowmickA.K., Influence of curative, filler, compatibilizer, domain size, and blend ratio on the dynamic mechanical properties of silicone-EPDM blends, J. Appl. Polym. Sci.48 (1993), 529–545.
44.
JonesR.G., AndoW., and ChojnowskiJ., Silicone Containing Polymers, 1st edn.Kluwer Academic Pub, New York, (2000) p. 185–211.
45.
SocratesG., Infrared Characteristic Group Frequencies.John Wiley and Sons, Bristol, (1980) p. 126–127.
46.
LewisL.N., SteinJ., GaoY., ColbornR.E., and HutchinsG., Platinum catalysts used in the silicones industry. Their synthesis and activity in hydrosilylation, Platinum Metals Rev., 41(2), (1997), 66–75.
47.
PolmanteerK.E., Silicone Rubber, its Development and Technological Progress, Rubber Chem. Technol, 61, (1988), 470–502.
48.
YiS., HiltonH.H., Effects of Thermo-Mechanical Properties of Composites on Viscosity, Temperature and Degree of Cure in Thick Thermosetting Composite Laminates during Curing Process, J. Comp. Mater, 32 (1998), 600–622.