This study aims to assess the effects of ageing in boiling water on the transverse tensile mechanical properties of unidirectional commingled GF/PP composites, as well as the influence of the fibre/matrix adhesion on the water absorption and desorption mechanisms. For this purpose, different interfacial qualities were obtained by a modification of the fibre reinforcement sizing (polypropylene specific sizing, or no sizing), and of the matrix (with or without coupling agent). A very good retention of the mechanical properties was observed for those composites which had been treated so as to improve the fibre/matrix adhesion. It is also shown that the better the adhesion, the longer the water remained inside the composite material. This induced effect appears to be the counterpart of the protecting role against moisture of a strong interface. The interfacial interactions act as barriers both during absorption and during desorption. This leads to water molecule entrapment. Hence, the persistence of water trapped at the interfaces in the case of sized glass fibres composites leads us to recommend investigations on the long term effects on longitudinal tension properties, since the effects of zero-stress ageing are known to reduce fibre strength.
References
1.
Opportunities in continuous fibre reinforced thermoplastic composites 2003-2008, 240 pages, E-Composites Inc. (June 2003).
2.
LietardV., KrawczakP., and PabiotJ., Influence of the fibre/matrix interface on the long term dynamic and environmental stress cracking behaviour of glass/epoxy composites, Twelfth International Conference on Composite Materials (ICCM-12), Paris (05-09 July 1999).
3.
KotakiM., and HamadaH., Effect of interfacial properties and weave structure on mode I interlaminar fracture behaviour of glass satin woven fabric composites, Composites Part A, 28, 3 (1997), 257–266.
4.
TancrezJ. -P., Study of the brittleness of injection-moulded short-glass-fibre-reinforced polypropylene matrix composites (in French), PhD dissertation, Université de Lille1/Ecole des Mines de Douai (1994).
5.
GerardP., Control and optimization of anisotropy and heterogeneity of short glass fibre reinforced thermoplastic matrix molded by injection (in French), PhD dissertation, Université de Lille1/Ecole des Mines de Douai (1998).
6.
CziganyT., and Karger-KocsisJ., Comparison of the failure mode in short and long glass fibre-reinforced injection moulded polypropylene composites by acoustic emission, Polymer Bulletin, 31, 4 (1993), 495–501.
7.
ShonaikeG. O., HamadaH., MaekawaZ., MatsudaM., YubaT., and MatsuoT., The influence of cooling conditions on the mechanical properties of commingled yarn composites, J. Thermoplastic Composite Materials, 9, 1 (January 1996), 76–89.
8.
YeL., and FriedrichK., Interlaminar fracture of co -mingled yarn based glass/polypropylene composites, Composites Science and Technology, 46, 2 (1993), 187–198.
9.
SvenssonN., ShishooR., and GilchristM., Manufacturing of thermoplastic composites from commingled yarns – a review, J. Thermoplastic Composite Materials, 11, 1 (1998), 22–56.
10.
MillerJ. D., and IshidaH., Adhesive-adherend interface and interphase, in Fundamentals of adhesion, Ed. by LeeL. H., Plenum Press, New York (1991).
11.
IlerR. K., The chemistry of silica, John Wiley & Sons Inc. (1979).
12.
van den OeverM., and PeijsT., Continuous-glass-fibre-reinforced polypropylene composites II. Influence of maleic-anhydride modified polypropylene on fatigue behaviour, Composites Part A, 29, 3 (1998), 227–239.
13.
HamadaH., FujiharaK., and HaradaA., The influence of sizing conditions on bending properties of continuous glass fiber reinforced polypropylene composites, Composites Part A, 31, 9 (2000), 979–990.
14.
NygardP., and GustafsonC. -G., Interface and impregnation relevant tests for continuous glass fiber – polypropylene composites, Composites Part A, 34, 10 (2003), 995–1006.
15.
IshidaH., A review of recent progress in the studies of molecular and microstructure of coupling agents and their functions in composites, coatings and adhesive joints, Polymer Composites, 5, 2, (April 1984), 101–123.
16.
PlueddemannE. P., Silane coupling agents, 2nd edn. Plenum Press, New York (1990).
17.
OsterholtzF. D., and PohlE. R, Hydrolysis and condensation of organofunctional alkoxysilanes, in Silanes and other coupling agents, Ed. MittalK., VSP, (1992), 119–141.
18.
ArklesB., SteinmetzJ. R., ZazycznyJ., and MehtaP., Factors contributing to the stability of alkoxysilanes in aqueous solution, in Silanes and other coupling agents, Ed. MittalK., VSP, (1992), 91–104.
19.
LarivièreD., KrawczakP., TibériC., and LucasP., Interfacial properties in commingled yarn thermoplastic composites. Part I: Characterization of the fibre/matrix adhesion, Polymer Composites, in press.
20.
JanevskiA., Bogoeva-GacevaG., and MaderE., DSC analysis of crystallization and melting behavior of polypropylene in model composites with glass and poly(ethylene terephtalate) fibers, J. Applied Polymer Science, 25, 6 (2004), 577–588.
21.
Bogoeva-GacevaG., JanevskiA., and MaderE., Characterization of a maleic anhydride-modified polypropylene as an adhesion promoter for glass fiber composites, J. Adhesion Science and Technology, 14, 3 (2000), 363–80.
22.
ConstableR. C., and AdurA. M., Chemical coupling of glass-filled polypropylene using acid or anhydride modified polypropylene, ANTEC, (1991), 1892–1896.
23.
KarianE. H. G., and WagnerH. R., Assessment of interfacial adhesion in chemically coupled glass fibre reinforced polypropylene, ANTEC, (1993), 3449–3455.
24.
LinC. W., Modification of polypropylene by peroxide-catalyzed grafting of maleic anhydride for adhesive bonding, J. of Materials Science Letters, 12, 8 (1993), 612–614.
25.
TeiichiS., and KotaroK., US patent 4461809: Surface treating as an undercoat on surface of polyolefin shaped articles (24 July 1984).
26.
FranceP. W., DuncanD. J., SmithD. J., and BealesK. J., Strength and fatigue of multi-component optical glass fibres, J. Materials Science, 18, (1983), 785–792.
27.
CameronN. M., The effects of environment and temperature on the strength of E-glass fibres. Part 1: High vacuum and low temperature, Glass Technology, 9, 1 (February 1968), 14–21.
28.
CameronN. M., The effects of environment and temperature on the strength of E-glass fibres. Part 2: Heating and ageing, Glass Technology, 9, 5 (October 1968), 14–21.
29.
BarberoE. J., and DamianiT., Phenomenological Prediction of Tensile Strength of E-Glass Composites from Available Ageing and Stress Corrosion Data, J. Reinforced Plastics and Composites, 22, 4 (2003), 373–394.