In this work, plane tree seed-based activated carbons were characterized in detail for a variety of applications. The particularly important area of application would be in the artificial photosynthesis. After carbonization process of biomass precursor at 650°C, the resulting preliminary activated carbons were activated at various temperatures. The activated carbons were characterized by oxygen functionalities (a particularly important role has ester oxygen groups) which provide a unique microstructure. The chemical compositions of as-prepared activated carbons were analyzed through Fourier transform infrared and Raman spectra as well as gas chromatography–mass spectroscopy analysis, while morphology was observed by scanning electron microscopy analysis. Applied analysis showed that detected graphite mainly becomes uniformly nanocrystalline system. The current study also explored the applicability of carbon material obtained from plane tree seed as a potential gaseous adsorbent. The characterization showed that the tested material contains both mesopores and micropores, and this should be advantageous for the gas sorption process, since mesopores may provide low-resistant pathways for the diffusion of CO2 molecules, while the micropores are the most suitable for trapping of CO2. The sorption process analysis (including adsorption/desorption isotherms behavior) shows indication that the rate-limiting step of CO2 adsorption onto activated carbon is probably governed by diffusion-controlled process, especially at temperatures below 850°C.
WickramaratneNPJaroniecM.Importance of small micropores in CO2 capture by phenolic resin-based activated carbon spheres. J Mater Chem A2013;
52: 112–116.
2.
HilemanB.Climate change threatens global economy. Chem Eng News2006;
84: 7–8.
3.
SunYLiHLiG, et al.
Characterization and ciprofloxacin adsorption properties of activated carbons prepared from biomass wastes by H3PO4 activation. Bioresour Technol2016;
217: 239–244.
4.
Garcés-PoloSIVillarroel-RochaJSapagK, et al.
Comparative study of CO2 diffusion from adsorption kinetic measurements on microporous materials at low pressures and temperatures. Chem Eng J2016;
302: 278–286.
5.
GoelCBhuniaHBajpaiPK.Development of nitrogen enriched nanostructured carbon adsorbents for CO2 capture. J Environ Manag2015;
162: 20–29.
6.
RochelleGT.Amine scrubbing for CO2 capture. Science2009;
325: 1652–1654.
7.
HerawanSGHadiMSAyobMR, et al.
Characterization of activated carbons from oil-palm shell by CO2 activation with no holding carbonization temperature. Sci World J2013;
2013: 1–6.
8.
ElloASde SouzaLKCTrokoureyA, et al.
Development of microporous carbons for CO2 capture by KOH activation of African palm shells. J CO2 Util2013;
2: 35–38.
9.
ParshettiGKChowdhurySBalasubramanianR.Biomass derived low-cost microporous adsorbents for efficient CO2 capture. Fuel2015;
148: 246–254.
10.
JiménezVRamírez-LucasAAntonio DíazJ, et al.
CO2 capture in different carbon materials. Environ Sci Technol2012;
46: 7407–7414.
11.
MahviAHNouriJOmraniGA, et al.
Application of Platanus orientalis leaves in removal of cadmium from aqueous solution. World Appl Sci J2007;
2: 40–44.
12.
ChuangCLChiangPCChangEE.Kinetics of benzene adsorption onto activated carbon. Environ Sci Pollut Res2003;
10: 6–8.
13.
NathKPanchaniSBhakharMS, et al.
Preparation of activated carbon from dried pods of Prosopis cineraria with zinc chloride activation for the removal of phenol. Environ Sci Pollut Res2013;
20: 4030–4045.
14.
AlOthmanZAHabilaMAAliR, et al.
Valorization of two waste streams into activated carbon and studying its adsorption kinetics, equilibrium isotherms and thermodynamics for methylene blue removal. Arab J Chem2014;
7: 1148–1158.
15.
FooPYL and Lee LY. Preparation of Activated Carbon from Parkia Speciosa Pod by Chemical Activation. In: Proceedings of the World Congress on engineering and computer science (eds Ao SI, Douglas C, Grundfest WS and Burgstone J), San Francisco, USA, 2010, p.1. Hong Kong: Newswood Limited.
16.
KleszykPRatajczakPSkowronP, et al.
Carbons with narrow pore size distribution prepared by simultaneous carbonization and self-activation of tobacco stems and their application to supercapacitors. Carbon2015;
81: 148–157.
17.
ASTM D5373-14e2. Standard test methods for determination of carbon, hydrogen and nitrogen in analysis samples of coal and carbon in analysis samples of coal and coke, ASTM International, West Conshohocken, PA, 2014.
18.
ISO 1928. Solid mineral fuels – determination of gross calorific value by the bomb calorimetric method and calculation of net calorific value, 2009.
19.
TAPPI/ANSI T 257 cm-12:201. Sampling and preparing wood for analysis, Test Method, revised March 2013.
20.
T 264. Preparation of wood for chemical analysis, Test Method T 264 cm-97: 2002, revised March 2013.
21.
BrowningBL.Methods of wood chemistry.
vol. 2.
New York:
Interscience Publishers, 1967, pp.561–587.
22.
SchoeningAGJohanssonG.Absorptiometric determination of acid-soluble lignin in semichemical bisulfite pulps and in some woods and plants. Svensk Papperstid1965;
68: 607–613.
23.
TAPPI UM 250. Standard method. Acid-soluble lignin in wood and pulp. In: 1991 TAPPI useful methods, Tappi, Atlanta, GA, USA, 1991.
24.
TAPPI T 207. Standard method. Water solubility of wood and pulp. In: 1999 TAPPI useful methods, Tappi, Atlanta, GA, USA, 1999.
25.
ASTM D1102-84.Standard test method for ash in wood.
West Conshohocken, PA:
ASTM International, 2013.
26.
WilsonLWeihongWYBlasiakW, et al.
Thermal characterization of tropical biomass feedstocks. Energy Conv Manag2011;
52: 191–198.
27.
HaiyuMShuzhongWLinC, et al.
Thermal behavior and the evolution of char structure during co-pyrolysis of platanus wood blends with different rank coals from northern China. Fuel2015;
158: 602–611.
28.
El MayYJeguirimMDorgeS, et al. Thermogravimetric analysis and kinetic study on palm of phoenix dactylifera L. In: The Seventh Mediterranean combustion symposium, Chia Laguna, Cagliari, Sardinia, Italy, MCS, 2011, vol.
7, pp.1–9. Pittsburgh, PA, USA: The Combustion Institute.
29.
BendahouADfresneAKaddamiH, et al.
Isolation and structural characterization of hemicelluloses from palm of Phoenix dactylifera L. Carbohydr Polym2007;
68: 601–608.
30.
StrezovV.System approach to biomass pyrolysis: product characterization, Bionature. In:The third international conference on bioenvironment, biodiversity and renewable energies, IARIA conference (eds Din P and Lorenz P),
St. Maarten, The Netherlands Antilles, 2012, pp.7–11. New York, USA: International Academy, Research, and Industry Association (IARIA).
31.
VhathvarothaiNNessJYuQJ.An investigation of thermal behaviour of biomass and coal during copyrolysis using thermogravimetric analysis. Int J Energy Res2014;
38: 1145–1154.
32.
RowellRMPettersenRTshabalalaMA.Cell wall chemistry. In: RowellRM (ed) Handbook of wood chemistry and wood composites. 2nd ed.Boca Raton, USA:
Taylor & Francis Group, 2013, pp.33–75.
33.
EmandiAVasiliuCIBudrugeacP, et al.
Quantitative investigation of wood composition by integrated FT-IR and thermogravimetric methods. Cellulose Chem Tech2011;
45: 579–584.
34.
EjikemeEMEjikemePCNAbaluBN.Equilibrium, kinetics and thermodynamics studies on MB adsorption using hamburger seed shell activated carbon. Int J Eng Tech2014;
14: 74–83.
35.
ZhangSMinZHTayHL, et al.
Effects of volatile-char interactions on the evolution of char structure during the gasification of Victorian brown coal in steam. Fuel2011;
90: 1529–1535.
36.
GuoXTayHLZhangS, et al.
Changes in char structure during the gasification of a Victorian brown coal in steam and oxygen at 800°C. Energy Fuel2008;
22: 4034–4038.
37.
BadzianARBackmannPKHartnettT, et al.Amorphous hydrogenated carbon films. In: KoidlPOelhafenP (eds) Proceedings of the E-MRS meeting,
Stasbourg, France, 1987, vol.
17, pp.63–67.
38.
EndoMKimYHayashiT, et al.
Nanotube coalescence-inducing mode: a novel vibrational mode in carbon systems. Small2006;
2: 1031–1036.
39.
FerrariACMeyerJCScardaciV, et al.
Raman spectrum of graphene and graphene layers. Phys Rev Lett2006;
97: 187401–187405.
40.
FerrariAC.Raman spectroscopy of graphene and graphite: disorder, electron-phonon coupling, doping and nonadiabatic effects. Solid State Commun2007;
143: 47–57.
41.
MernaghTPCooneyRPJohnsonRA.Raman spectra of graphon carbon black. Carbon1984;
22: 39–42.
42.
ChoNHKrishnanKMVeirsDK, et al.
Chemical structure and physical properties of diamond-like amorphous carbon films prepared by magnetron sputtering. J Mater Res1990;
5: 2543–2554.
43.
FerrariACRodilSERobertsonJ.Interpretation of infrared and Raman spectra of amorphous carbon nitrides. Phys Rev B2003;
67: 155306–155326.
44.
FerrariAC.A model to interpret the Raman spectra of disordered, amorphous and nanostructured carbons. Mater Res Soc Symp Proc2001;
675: 5.1–5.12.
45.
TuinstraFKoenigJL.Raman spectrum of graphite. J Chem Phys1970;
53: 1126–1130.
46.
WangYAlsmeyerDCMcCreeryRL.Raman spectroscopy of carbon materials: structural basis of observed spectra. Chem Mater1990;
2: 557–563.
47.
MogeraUDhanyaRPujarR, et al.
Highly decoupled graphene multilayers: turbostraticity at its best. J Phys Chem Lett2015;
6: 4437–4443.
48.
JorioASaitoRDresselhausG, et al.Raman spectroscopy in graphene related systems.
Weinheim, Germany:
Wiley-VCH Verlag GmbH & Co., 2011, pp.3–18.
49.
LähdetieA.Wood biomass characterization by Raman spectroscopy, school of chemical technology, department of Forest products technology. Aalto University, Doctoral Dissertations, Helsinki, Finland, 2013, pp.1–67.
50.
LiKKhannaRZhangJ, et al.
Comprehensive investigation of various structural features of bituminous coals using advanced analytical techniques. Energy Fuels2015;
29: 7178–7189.
51.
EdaGChhowallaM.Chemically derived graphene oxide: towards large-area thin-film electronics and optoelectronics. Adv Mater2010;
22: 2392–2415.
52.
SingKSWEverettDHHaulRAW, et al.
Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity. Pure Appl Chem1985;
57: 603–620.
53.
BrunauerSDemingLSDemingWE, et al.
On a theory of the van der Waals adsorption of gases. J Am Chem Soc1940;
62: 1723–1732.
54.
GreggSJSingKSWSalzbergHW.Adsorption surface area and porosity. J Electrochem Soc1967;
114: 279C.
55.
Wei W, Yang L, Zhong WH, et al. Fast removal of methylene blue from aqueous solution by adsorption onto poorly crystalline hydroxyapatite nanoparticles. Dig J Nanomater Biostruct 2015; 19: 1343--1363.
56.
LuaAYangCTGuoJ.Effect of pyrolysis conditions on the properties of activated carbon prepared from pistachio-nutshells. J Anal Appl Pyrol2004;
72: 279–287.
57.
GuoSPengJLiW, et al.
Effects of CO2 activation on porous structures of coconut shell-based activated carbons. Appl Surf Sci2009;
255: 8443–8449.
58.
Firdaus MazlanMAUemuraYYusupS, et al.
Activated carbon from rubber wood sawdust by carbon dioxide activation. Proc Eng2016;
148: 530–537.
59.
YahyaMAAl-QodahZNgahCWZCW, et al.
Preparation and characterization of activated carbon from desiccated coconut residue by potassium hydroxide. Asian J Chem2015;
27: 2331–2336.
60.
YahyaMAAl-QodahZZanariah NgahCW.Agriculture bio-waste materials as potential sustainable precursors used for activated carbon production: a review. Renew. Sustain Energy Rev2015;
46: 218–235.
61.
Gonzalez-SerranoECorderoTRodriguez-MirasolJ, et al.
Removal of water pollutants with activated carbons prepared from H3PO4 activation of lignin from kraft black liquors. Water Res2004;
38: 3043–3050.