This study presents a method for measuring the low volumetric wear expected in ceramic total disc replacements, which can be used to replace intervertebral discs in the spine, using non-contacting optical methods. Alumina-on-alumina ball-on-disc tests were conducted with test conditions approximating those of cervical (neck region of the spine) total disc replacement wear tests. The samples were then scanned using a three-dimensional non-contacting optical profilometer and the data used to measure surface roughness and develop a method for measuring the wear volume. The results showed that the magnification of the optical lens affected the accuracy of both the surface roughness and wear volume measurements. The method was able to successfully measure wear volumes of 0.0001 mm3, which corresponds to a mass of 0.0001 mg, which would have been undetectable using the gravimetric method. A further advantage of this method is that with one scan the user can measure changes in surface topography, volumetric wear and the location of the wear on the implant surface. This method could also be applied to more severe wear, other types of orthopaedic implants and different materials.
HughesSPFFreemontAJHukinsDWL. The pathogenesis of degeneration of the intervertebral disc and emerging therapies in the management of back pain. J Bone Joint Surg Br2012; 94: 1298–1304.
2.
InghamEFisherJ. The role of macrophages in osteolysis of total joint replacement. Biomaterials2005; 26: 1271–1286.
3.
InghamEFisherJ. Biological reactions to wear debris in total joint replacement. Proc IMechE, Part H: J Engineering in Medicine2000; 214: 21–37.
4.
Van OoijAOnerFCVerboutAJ. Complications of artificial disc replacement: a report of 27 patients with the SB Charité disc. J Spinal Disord Tech2003; 16: 369–383.
5.
Van OoijAKurtzSMStesselsF. Polyethylene wear debris and long-term clinical failure of the Charité disc prosthesis: a study of 4 patients. Spine2007; 32: 223–229.
6.
PuntIMVisserVMVan RhijnLW. Complications and reoperations of the SB Charité lumbar disc prosthesis: experience in 75 patients. Eur Spine J2008; 17: 36–43.
7.
KurtzSMTothJMSiskeyR. The latest lessons learned from retrieval analyses of ultra-high molecular weight polyethylene, metal-on-metal, and alternative bearing total disc replacements. Semin Spine Surg2012; 24: 57–70.
8.
YoonTRRoweSMJungST. Osteolysis in association with a total hip arthroplasty with ceramic bearing surfaces. J Bone Joint Surg Am1998; 80: 1459–1468.
9.
XinHShepherdDETDearnKD. A tribological assessment of a PEEK based self-mating total cervical disc replacement. Wear2013; 303: 473–479.
10.
MoghadasPMahomedAHukinsDWL. Wear in metal-on-metal total disc arthroplasty. Proc IMechE, Part H: J Engineering in Medicine2004; 227(4): 356–361.
11.
ClarkeICGoodVWilliamsP. Ultra-low wear rates for rigid-on-rigid bearings in total hip replacements. Proc IMechE, Part H: J Engineering in Medicine2000; 214: 214–331.
12.
SagbasBNuman DurakbasaM. Measurement of wear in orthopaedic prosthesis. Acta Phys Pol A2012; 121: 131–134.
13.
CarmignatoSSpinelliMAffatatoS. Uncertainty evaluation of volumetric wear assessment from coordinate measurements of ceramic hip joint prostheses. Wear2011; 270: 584–590.
14.
BluntLBillsPJiangX. The role of tribology and metrology in the latest development of bio-materials. Wear2009; 266: 424–431.
15.
BillsPBrownLJiangX. A metrology solution for the orthopaedic industry. J Phys Conf Ser2005; 13: 316–319.
16.
WilliamsSRWuJJUnsworthA. Wear and surface analysis of 38 mm ceramic-on-metal total hip replacements under standard and severe wear testing conditions. Proc IMechE, Part H: J Engineering in Medicine2011; 225: 783–796.
17.
SerraETucciAEspositoL. Volumetric determination of the wear of ceramics for hip joints. Biomaterials2002; 23(4): 1131–1137.
18.
TurgerAKöhlerJDenkenaB. Manufacturing conditioned roughness and wear of biomedical oxide ceramics for all-ceramic knee implants. Biomed Eng Online2013; 12: 84.
19.
BS ISO 18192-1:2011. Implants for surgery: wear of total intervertebral spinal disc prostheses. Part 1: loading and displacement parameters for wear testing and corresponding environmental conditions for test. London: British Standards Institute, 2011.
20.
Ceramic Characteristics Data Sheet received via personal communication from James Taylor, Goodfellows Ceramic and Glass Division, 2August2012.
BS ISO 14242-2:2000. Implants for surgery: wear of total hip joint prostheses. Part 2: methods of measurement. London: British Standards Institute, 2000.