Restricted accessResearch articleFirst published online 2024
Tailoring mechanical,microstructural and toughening characteristics of plasma-sprayed graphene-reinforced samarium niobate coatings for extreme environments
Thermal barrier coatings (TBCs) are advanced ceramic layers applied to metal components to provide insulation and protection against high temperatures in extreme operating environments. This study investigated the effects of graphene nanoplatelet (GNP) reinforcement on samarium niobate (SN: SmNbO4) TBCs for extreme environments. Four ceramic top coat compositions were plasma-sprayed onto Inconel 718 substrates: Yttria-stabilized zirconia (YSZ), SmNbO4 (SN), and SN reinforced with 1 and 1.5 wt% GNPs (SN-1GNP, SN-1.5GNP). The research examined microstructural characteristics, phase evolution, mechanical properties and toughening mechanisms. GNP reinforcement significantly improved coating density, with SN-1.5GNP reaching 97.4 ± 1.64% compared to 91.3 ± 1.69% for SN and 86.6 ± 1.47% for YSZ. Hardness and elastic modulus were enhanced by 86.38% and 57.91% for SN-1GNP, and 101.09% and 65.23% for SN-1.5GNP respectively. Moreover, fracture toughness experienced a significant increase from 1.86 ± 0.4 to 5.48 ± 0.7 MPa·m1/2, facilitated by toughening mechanisms, like splat bridging, GNP pull-out, crack arrest and ferroelastic domain switching. Additionally, the SN-1.5GNP coating exhibited a higher adhesion strength of 36.84 MPa, thereby leading to improved layer distribution and lesser chance of delamination. Compared to YSZ, these findings suggest that GNP-reinforced SN coatings offer enhanced performance for extreme environment applications.
DavisSJLewisNSShanerM, et al.Net-zero emissions energy systems. Science2018; 360: eaas9793.
2.
PyeSBroadOBatailleC, et al.Modelling net-zero emissions energy systems requires a change in approach. Clim Policy2021; 21: 222–231.
3.
TakeishiKKrewinkelR. Advanced gas turbine cooling for the carbon-neutral era. Int J Turbomach Propuls Power2023; 8: 19.
4.
VaßenRBakanEMackDE,et al.A perspective on thermally sprayed thermal barrier coatings: current Status and trends. J Therm Spray Technol2022; 31: 685–698.
5.
LiZSongY. Thermal barrier coating for aerial and aerospace engine. In: SongY (ed.) Inorganic and organic thin films. 1st ed. USA: Wiley, 2021, pp.615–645.
6.
DavimJP. Introduction to mechanical engineering. Cham: Springer International Publishing, 2018.
7.
DavimJP (ed) Thermal sprayed coatings and their tribological performances. UK: IGI Global, 2015 Jan 31.
8.
MondalKNuñezLDowneyCM,et al.Thermal barrier coatings overview: design, manufacturing, and applications in high-temperature industries. Ind Eng Chem Res2021; 60: 6061–6077.
9.
GuoLHeWChenW, et al.Progress on high-temperature protective coatings for aero-engines. Surf Sci Technol2023; 1: 6.
10.
AryaRKVerrosGDDavimJP. (eds) Functional coatings: innovations and challenges. India: John Wiley & Sons, 2024 Feb 28.
11.
GrilliMLValeriniDSlobozeanuAE, et al.Critical raw materials saving by protective coatings under extreme conditions: a review of last trends in alloys and coatings for aerospace engine applications. Materials2021; 14: 1656.
12.
RoncalloGBarbareschiECacciamaniG,et al.Effect of cooling rate on phase transformation in 6–8 wt% YSZ APS TBCs. Surf Coat Technol2021; 412: 127071.
StöverDPrachtGLehmannH, et al.New material concepts for the next generation of plasma-sprayed thermal barrier coatings. J Therm Spray Technol2004; 13: 76–83.
15.
LuoXLuoLZhaoX, et al.Single-phase rare-earth high-entropy zirconates with superior thermal and mechanical properties. J Eur Ceram Soc2022; 42: 2391–2399.
16.
LimaRS. Perspectives on thermal gradients in porous ZrO2-7–8 wt.% Y2O3 (YSZ) thermal barrier coatings (TBCs) manufactured by air plasma spray (APS). Coatings2020; 10: 12.
17.
MahadeSMuloneABjörklundS, et al.Incorporation of graphene nano platelets in suspension plasma sprayed alumina coatings for improved tribological properties. Appl Surf Sci2021; 570: 151227.
18.
VaggeSTGhogareS. Thermal barrier coatings. Mater Today Proc2022; 56: 1201–1216.
19.
LuX. Study of Yttria stabilized zirconia/alumina composite coatings produced by electrophoretic deposition and sintering. United Kingdom: The University of Manchester, 2006.
20.
WuJWeiXPadtureNP, et al.Low-thermal-conductivity rare-earth zirconates for potential thermal-barrier-coating applications. J Am Ceram Soc2002; 85: 3031–3035.
21.
XuQPanWWangJ, et al.Rare-earth zirconate ceramics with fluorite structure for thermal barrier coatings. J Am Ceram Soc2006; 89: 340–342.
22.
RenKWangQCaoY, et al.Multicomponent rare-earth cerate and zirconocerate ceramics for thermal barrier coating materials. J Eur Ceram Soc2021; 41: 1720–1725.
23.
ZhouFWangS. New materials for thermal barrier coatings. In: PaksereshtAAmirtharaj MosasKK (eds) Ceramic coatings for high-temperature environments. Cham: Springer International Publishing, 2024, pp.87–123.
24.
BryceKShihY-THuangL,et al.Calcium-Magnesium-Aluminosilicate (CMAS) corrosion resistance of high entropy rare-earth phosphate (Lu0.2Yb0.2Er0.2Y0.2Gd0.2)PO4: a novel environmental barrier coating candidate. J Eur Ceram Soc2023; 43: 6461–6472.
25.
Morán-RuizAVidalKLarrañagaA,et al.Characterization of Ln4Al2O9 (Ln = Y, Sm, Eu, Gd, Tb) rare-earth aluminates as novel high-temperature barrier materials. Ceram Int2018; 44: 8761–8767.
26.
ZhaoZChenHXiangH, et al.High entropy defective fluorite structured rare-earth niobates and tantalates for thermal barrier applications. J Adv Ceram2020; 9: 303–311.
27.
DouRZhangQGaoJ, et al.Rare-earth tantalates and niobates single crystals: promising scintillators and laser materials. Crystals2018; 8: 55.
28.
ArulnesanSWKayserPKimptonJA,et al.Studies of the fergusonite to scheelite phase transition in LnNbO4 orthoniobates. J Solid State Chem2019; 277: 229–239.
29.
YangJPanWHanY, et al.Mechanical properties, oxygen barrier property, and chemical stability of RE 3 NbO 7 for thermal barrier coating. J Am Ceram Soc2020; 103: 2302–2308.
30.
ZhuJMengXXuJ, et al.Ultra-low thermal conductivity and enhanced mechanical properties of high-entropy rare earth niobates (RE3NbO7, RE = Dy, Y, Ho, Er, Yb). J Eur Ceram Soc2021; 41: 1052–1057.
31.
LaiLGanMWangJ, et al.New class of high-entropy rare-earth niobates with high thermal expansion and oxygen insulation. J Am Ceram Soc2023; 106: 4343–4357.
32.
RamírezCBelmonteMMiranzoP,et al.Applications of ceramic/graphene composites and hybrids. Materials2021; 14: 2071.
33.
MarkandanKChinJKTanMTT. Recent progress in graphene based ceramic composites: a review. J Mater Res2017; 32: 84–106.
34.
ChenDLiJSunK,et al.Graphene-reinforced metal matrix composites: fabrication, properties, and challenges. Int J Adv Manuf Technol2023; 125: 2925–2965.
35.
KumarASharmaKDixitAR. Carbon nanotube- and graphene-reinforced multiphase polymeric composites: review on their properties and applications. J Mater Sci2020; 55: 2682–2724.
36.
MuloneAMahadeSBjörklundS, et al.Development of yttria-stabilized zirconia and graphene coatings obtained by suspension plasma spraying: thermal stability and influence on mechanical properties. Ceram Int2023; 49: 9000–9009.
37.
MukherjeeBAsiq RahmanOSIslamA, et al.Plasma sprayed carbon nanotube and graphene nanoplatelets reinforced alumina hybrid composite coating with outstanding toughness. J Alloys Compd2017; 727: 658–670.
38.
KeshriAKAgarwalA. Wear behavior of plasma-sprayed carbon nanotube-reinforced aluminum oxide coating in marine and high-temperature environments. J Therm Spray Technol2011; 20: 1217–1230.
39.
KaradgeMZhaoXPreussM,et al.Microtexture of the thermally grown alumina in commercial thermal barrier coatings. Scr Mater2006; 54: 639–644.
40.
GuoXChengSCaiW, et al.A review of carbon-based thermal interface materials: mechanism, thermal measurements and thermal properties. Mater Des2021; 209: 109936.
41.
VozniakovskiiAKidalovSVoznyakovskiiA,et al.Hardness and thermal conductivity of a composite based on aluminum modified with a hybrid material detonation nanodiamond/few-layer graphene. Fuller Nanotub Carbon Nanostructures2022; 30: 205–210.
42.
CuiEZhaoJWangX,et al.Improved fracture resistance and toughening mechanisms of GNPs reinforced ceramic composites. Ceram Int2022; 48: 24687–24694.
43.
SinghPPanditNKeshriAK. Plasma-sprayed GNP/CNT reinforced lanthanum-cerate coatings: hot corrosion assessment in Na2SO4-V2O5 environment. Surf Coat Technol2024; 481: 130676.
44.
MoradiAAnsariRHassanzadeh-AghdamMK. Synergistic effect of carbon nanotube/graphene nanoplatelet hybrids on the elastic and viscoelastic properties of polymer nanocomposites: finite element micromechanical modeling. Acta Mech2024; 235: 1887–1909.
45.
SinghPSatishCIslamA, et al.Multifunctional hybrid composite: plasma sprayed al and graphene reinforced alumina coating. J Alloys Compd2024; 984: 173984.
46.
SatishCKumarKVKiranPS, et al.Role of powder morphology on α-phase content in plasma sprayed alumina coatings. Ceram Int2024; 50: 25484–25493.
47.
MoonJChoiHKimH,et al.The effects of heat treatment on the phase transformation behavior of plasma-sprayed stabilized ZrO2 coatings. Surf Coat Technol2002; 155: 1–10.
48.
AbbasRAAjeeSABashMAA,et al.Elimination of YSZ thermal barrier coatings degradation using an electrophoretic deposition technique. AIP Conf Proc2024; 3002: 080028.
49.
GuptaKMurtazaQYuvrajN. Development of ZrB2-SiC plasma-sprayed ceramic coating for thermo-chemical protection in hypersonic vehicles. J Mater Eng Perform2024; 33: 1401–1410.
50.
DasBPandaBNSharmaF,et al.Recent developments in cladding and coating using cold metal transfer technology. J Mater Eng Perform2024; 33: 3130–3147.
51.
WuFWuPZhouY, et al.The thermo-mechanical properties and ferroelastic phase transition of RENbO 4 (RE = Y, La, Nd, Sm, Gd, Dy, Yb) ceramics. J Am Ceram Soc2020; 103: 2727–2740.
52.
LiBChenLHuM, et al.Ferroelastic tetragonal-monoclinic phase transition and anisotropic thermal expansion of LuNbO4 ceramics. Scr Mater2023; 228: 115258.
53.
ZhangPFengYLiY, et al.Thermal and mechanical properties of ferroelastic RENbO4 (RE = Nd, Sm, Gd, Dy, Er, Yb) for thermal barrier coatings. Scr Mater2020; 180: 51–56.
54.
MircheKKPandeyKKPandeySM,et al.Microstructure and corrosion behavior of plasma-sprayed nanodiamond-reinforced NiAl nanocomposite coating. J Therm Spray Technol2023; 32: 1299–1310.
55.
SiqueiraKPFMoreiraRLDiasA. Synthesis and crystal structure of lanthanide orthoniobates studied by vibrational spectroscopy. Chem Mater2010; 22: 2668–2674.
56.
RamaraoSDMurthyVRK. Structural phase transformation and microwave dielectric studies of SmNb1−x(Si1/2Mo1/2)xO4 compounds with fergusonite structure. Phys Chem Chem Phys2015; 17: 12623–12633.
57.
MauryaSSGrainAKKumarR, et al.High temperature wear behavior of nanodiamond reinforced nickel-aluminum composite coatings. Wear2024; 542-543: 205280.
58.
WuYHeWGuoH. Improved fracture toughness and multiple toughening mechanisms of NdPO4/NdYbZr2O7 composites. Ceram Int2020; 46: 16612–16619.
59.
PortinhaATeixeiraVCarneiroJ, et al.Characterization of thermal barrier coatings with a gradient in porosity. Surf Coat Technol2005; 195: 245–251.
60.
KumariSIslamAMircheKK, et al.Plasma sprayed graphene reinforced titanium nitride composite coating: an effective solution for mitigating the corrosion attack. Surf Coat Technol2022; 445: 128704.
61.
BianchiLLegerACVardelleM, et al.Splat formation and cooling of plasma-sprayed zirconia. Thin Solid Films1997; 305: 35–47.
62.
TillmannWKhalilOBaumannI. Influence of direct splat-affecting parameters on the splat-type distribution, porosity, and density of segmentation cracks in plasma-sprayed YSZ coatings. J Therm Spray Technol2021; 30: 1015–1027.
63.
KulkarniAVaidyaAGolandA, et al.Processing effects on porosity-property correlations in plasma sprayed yttria-stabilized zirconia coatings. Mater Sci Eng A2003; 359: 100–111.
64.
DavimJ. Ceramic Matrix Composites: Materials, Manufacturing and Engineering. Berlin, Boston: De Gruyter, 2016.
65.
LiaoX-JZhangLSunY-Q, et al.Effect of inter-splat bonding quality on the dependence of wear behavior of plasma-sprayed stainless steel coating on applied load. J Therm Spray Technol2024; 33: 1559–1569.
66.
LokachariSLengKRincon RomeroA, et al.Processing–microstructure–properties of columns in thermal barrier coatings: a study of thermo-chemico-mechanical durability. ACS Appl Mater Interfaces2024; 16: 10646–10660.
IslamAKumarKPandeyKK, et al.Exceptionally high fracture toughness of carbon nanotube reinforced plasma sprayed lanthanum zirconate coatings. J Alloys Compd2019; 777: 1133–1144.
69.
ChoudharySIslamAMukherjeeB, et al.Plasma sprayed Lanthanum zirconate coating over additively manufactured carbon nanotube reinforced Ni-based composite: unique performance of thermal barrier coating system without bondcoat. Appl Surf Sci2021; 550: 149397.
70.
ÇakırMVErkliğAAhmedBF. Graphene nanoparticle effect on flexural and shear behaviors of adhesively bonded single lap joints of GFRP composites. J Braz Soc Mech Sci Eng2021; 43: 11.
71.
KumarRPandeyKKIslamA,et al.Graphene nanoplatelets: a promising corrosion inhibitor and toughening inclusion in plasma sprayed cerium oxide coating. J Alloys Compd2019; 809: 151819.
72.
RamírezC. 10 Years of research on toughness enhancement of structural ceramics by graphene. Philos Trans R Soc Math Phys Eng Sci2022; 380: 20220006.
73.
ÇakırMVÖzbekÖ. Mechanical performance and damage analysis of GNP-reinforced adhesively bonded joints under shear and bending loads. J Adhes2023 Apr 4; 99: 869–892.
74.
ZhuJXuJZhangP, et al.Enhanced mechanical and thermal properties of ferroelastic high-entropy rare-earth-niobates. Scr Mater2021; 200: 113912.
75.
IslamAPandeyKKSinghP, et al.Microstructural, mechanical and tribological properties of carbon nanotubes reinforced plasma sprayed molybdenum disulphide composite coatings. Ceram Int2022; 48: 32757–32766.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.