Abstract
In the present paper, plasma-assisted physical vapor depositions (PAPVDs) have been used to extract the TiN and titanium aluminum nitride (TiAlN). Further, plasma nitriding (PN) has been used prior to thin-film deposition of TiN on AISI 304 stainless steel material using intentional biasing (in the coating). PAPVD is integrated to investigate the thermal resistant effect coating of AISI 304 stainless steel by TiN coating using finite-element analysis. The morphology of elements on the coating was studied by field emission scanning electron microscopy, X-ray diffraction (XRD), and energy-dispersive X-ray spectroscopy. From XRD analysis, it has been observed that at the coated zone Ti, TiN was found on the AISI 3O4 stainless steel. The results in microhardness through the Vickers microhardness tester have been measured up to 350 Hv for the base sample at a 10 g load. Moreover, TiN/(PN + TiN) coated samples were measured with an average microhardness of 2220, 963, and 720 Hv for the nitride sample. In addition to this, the microhardness of TiAlN was found up to 1890 and 2400 Hv for different samples. The thickness of the film is around 1.4279 µm (TiN) and 1.888 µm (TiAlN) in 1 h of deposition.
Keywords
Get full access to this article
View all access options for this article.