The stress corrosion cracking (SCC) resistance of the laser beam welded (LBW) AISI 316LN austenitic stainless steel (SS) was assessed and compared to the base metal (BM). The weld joint was produced using a 2.5 kW laser power source at 1500 mm/min welding speed. Microstructural characterization of the base metal and weld joint were done by the following techniques: (i) Optical Microscopy (OM), (ii) Scanning Electron Microscopy (SEM) and (iii) Transmission Electron Microscopy (TEM). The primary mechanical properties such as strength, toughness and hardness of the welded joint were evaluated and compared with the base metal. Stress Corrosion Cracking (SCC) assessment was done in boiling 45 wt% MgCl2 solution at constant load condition as per American Society for Testing and Materials (ASTM) standard G36-94. From the SCC experiment data, steady-state elongation rate (), transition time () and time to failure () were found and generalized equations to predict the time to failure of the base metal and LBW joint were successfully derived. The passive film rupture mechanism majorly influenced the SCC failure for 316LN and welded joint. The formation of the discontinuous δ-ferrite network, residual stress and nitrogen pore nucleation at the fusion zone of the LBW joint deteriorated the SCC resistance. The metallographic and fractographic studies revealed brittle transgranular SCC failure of the base metal as well as the LBW joint in all the stress conditions.
Radhika K and Lakshminarayanan AK. An insight into the stress corrosion cracking resistance of friction stir processed and micro-arc oxidation coated ZE41 grade magnesium alloy. Proc I Mech E Part C: J Mech Eng Sci 2020. DOI: 10.1177%2F0954406220920315.
5.
HeXLiangHYanZ, et al.
Stress corrosion cracking behavior of micro-arc oxidized AZ31 alloy. Proc IMechE, Part C: J Mechanical Engineering Science2020;
234: 1640–1652.
6.
BatoolSKhanMJafferySHI, et al.
Analysis of weld characteristics of micro-plasma arc welding and tungsten inert gas welding of thin stainless steel (304 L) sheet. Proc IMechE, Part C: J Mechanical Engineering Science2016;
230: 1005–1017.
7.
Buvanashekaran G, et al. A study of laser welding modes with varying beam energy levels. Proc I Mech E Part C: J Mech EngSci 2009; 223: 1141–1156.
8.
Qi K, et al. Microstructure and Corrosion Properties of Laser-Welded SAF 2507 Super Duplex Stainless Steel Joints. J Mater Eng Perform 2019; 28: 287–295.
9.
Youmin R, et al. Study on deformation and residual stress of laser welding 316L T-joint using 3D/shell finite element analysis and experiment verification. Int J AdvManuf Technol 2017; 89: 2077–2085.
10.
Salminen A, et al. The characteristics of high power fibre laser welding. Proceedings of the Institution of Mechanical Engineers, Proc I Mech E Part C: J Mech Eng Sci 2010; 224: 1019–1029.
11.
Anita T, et al. Pitting and stress corrosion cracking studies on AISI type 316N stainless steel weldments. Def Tech 2018; 14: 226–237.
12.
Singh RK, et al. Friction stir welding of nuclear grade SA508Gr. 3Cl. 1 and SS304LN dissimilar steels. Proc I Mech E Part C: J Mech Eng Sci 2018; 232: 3814–3822.
13.
Lu WF, et al. Effects of dendrite axis and fusion boundary on stress corrosion cracking of ER 308 L/SS 304L welds in a high-temperature water environment. Int J Press Vessels Pip 2020; https://doi.org/10.1016/j.ijpvp.2019.103940.
14.
Mankari K and Acharyya SG. Development of stress corrosion cracking resistant welds of 321 stainless steel by simple surface engineering. App Surf Sci 2017; 426: 944–950.
15.
Cai JB et al. Stress corrosion cracking of austenitic weld deposits in a salt spray environment. J Nucl Mater 2015; 465: 774–783.
16.
Orlikowski J and Krakowiak S. Pitting corrosion and stress-corrosion cracking of buffer tanks in a brewery. Eng Fail Anal 2013; 29: 75–82.
17.
Li Y et al. Failure analysis of the 304 stainless steel tube in a gas analyzer. Eng Fail Anal 2012; 20: 35–42.
18.
Rao MA et al. Stress corrosion cracking failure of a SS 316L high-pressure heater tube. Eng Fail Anal 2018; 90: 14–22.
19.
Ziaei SMR et al. Failure analysis: Chloride stress corrosion cracking of AISI 316 stainless steel downhole pressure memory gauge cover. Eng Fail Anal 2013; 33: 465–472.
Lakshminarayanan AK and Balasubramanian V. Evaluation of Microstructure and Mechanical Properties of Laser Beam Welded AISI 409M Grade Ferritic Stainless Steel. J Iron Steel Res Int 2012; 19: 72–78.
22.
ASTM Designation: G36 – 94. Standard practice for evaluating stress-corrosion-cracking resistance of metals and alloys in a boiling magnesium chloride solution, www.astm.org/Standards/G36 (2018, accessed 30 September 2020).
23.
AlwinBLakshminarayananAKVasudevanM, et al.
Assessment of stress corrosion cracking resistance of activated tungsten inert gas-welded duplex stainless steel joints. J Materi Eng and Perform2017;
26: 5825–5836.
24.
ChowdhurySNirsanametlaYManapuramM, et al.
Investigation on keyhole mode fiber laser welding of SS 316 in a self-protected atmosphere. Proc IMechE, Part C: J Mechanical Engineering Science2019;
233: 6602–6615.
25.
LippoldJCKoteckiDJ. Welding metallurgy and weldability of stainless steels.
USA:
Wiley-Interscience, 2005.
26.
Bo C et al. Effects of shielding gas composition on the welding stability, microstructure and mechanical properties in laser-arc hybrid welding of high nitrogen steel. Mat Res Express 2018. DOI: 10.1088/2053-1591/aad6c5.
27.
LiHYangSZhangS, et al.
Microstructure evolution and mechanical properties of friction stir welding super-austenitic stainless steel S32654. Mater Des2017;
118: 207–217.
28.
ChiKMacleanMSMcPhersonNA, et al.
Single sided single pass submerged arc welding of austenitic stainless steel. Mater Sci Technol2007;
23: 1039–1048.
29.
RongYHuangYZhangG, et al.
Laser beam welding of 316 L T-joint: microstructure, microhardness, distortion, and residual stress. Int J Adv Manuf Technol2017;
90: 2263–2270.
30.
RagavendranMVasudevanM.
Laser and hybrid laser welding of type 316 L(N) austenitic stainless steel plates. Mater Manuf Processes2020;
35: 922–934.
31.
AlyousifOMNishimuraR.
The stress corrosion cracking behavior of austenitic stainless steels in boiling magnesium chloride solutions. Corros Sci2007;
49: 3040–3051.
32.
StratulatA, et al.
Grain boundary structure and intergranular stress corrosion crack initiation in high-temperature water of a thermally sensitized austenitic stainless steel, observed in situ. Corros Sci2014;
85: 428–435.
33.
YoonY-SHaH-YLeeT-H, et al.
Effect of N and C on stress corrosion cracking susceptibility of austenitic Fe18Cr10Mn-based stainless steels. Corros Sci2014;
80: 28–36.
34.
ZhongYZhouCChenS, et al.
Effects of temperature and pressure on stress corrosion cracking behavior of 310 S stainless steel in chloride solution. Chin J Mech Eng2017;
30: 200–206.
35.
SpencerDT, et al.
The initiation and propagation of chloride-induced transgranular stress-corrosion cracking (TGSCC) of 304 L austenitic stainless steel under atmospheric conditions. Corros Sci2014;
88: 76–88.
36.
Kwok CT, et al. Stress corrosion cracking of laser-welded stainless steels. In: Proceedings of the 1st international joint symposium on joining and welding, Japan, 6–8 November 2013, pp.547–552.
37.
RajasekaranRLakshminarayananAKVasudevanM, et al.
Role of welding processes on microstructure and mechanical properties of nuclear-grade stainless steel joints. Proc IMechE, Part L: J Materials: Design and Applications2019;
233: 2335–2351.
38.
GhoshSRanaVPSKainV, et al.
Role of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel. Mater Des2011;
32: 3823–3831.
39.
LvH, et al.
Stress corrosion property of 304 stainless steel and Q345 steel laser-MAG hybrid welded joints. Int J Mod Phys B2020;
33: 1–6.
40.
VinothkumarM, et al.
Stress corrosion cracking behaviour of gas tungsten arc welded super austenitic stainless steel joints. Def Technol2015;
11: 282–291.
41.
QiYM, et al.
Stress corrosion cracking behavior of 316 L stainless steel exposed to CO2–H2S–Cl− environments in the absence and presence of methyl diethanolamine (MDEA). Corrs Eng Sci Technol2016;
51: 507–512.
42.
HarstonDScullJC.
Fractographic observations on the stress corrosion cracking of some austenitic stainless steels inMgCl2 solutions at 154°C. Corros Sci1970;
26: 387–395.