The effect of five different stirring times of friction stir spot welding on lap-shear specimens of Al 6061-T6 alloy has been experimentally analyzed. The welding condition with 2 s of stirring shows the optimum mechanical behavior in comparison to the others. The static strength and fatigue behavior of the joint are justified using the microhardness profiles. The static results prove that the increase of stirring time beyond the 2 s case has little effect on improving the static strength. The fatigue results reveal two different failure modes, which are shear fracture at high load levels and transverse crack growth at low load levels. At medium load levels, although the final failure is similar to high load levels, the transverse growth of the crack outside the welding zone, just like low load levels, is also observed.
RosendoTParraBTierMet al.Mechanical and microstructural investigation of friction spot welded AA6181-T4 aluminium alloy. Mater Design2011; 32: 1094–1100.
2.
ZhangZYangXZhangJet al.Effect of welding parameters on microstructure and mechanical properties of friction stir spot welded 5052 aluminum alloy. Mater Design2011; 32: 4461–4470.
3.
TozakiYUematsuYTokajiK. Effect of processing parameters on static strength of dissimilar friction stir spot welds between different aluminium alloys. Fatigue Fract Eng Mater Struct2007; 30: 143–148.
4.
RosendoTTierMMazzaferroJet al.Mechanical performance of AA6181 refill friction spot welds under Lap shear tensile loading. Fatigue Fract Eng Mater Struct2015; 38: 1443–1455.
5.
LathabaiSPainterMCantinGet al.Friction spot joining of an extruded Al–Mg–Si alloy. Scripta Mater2006; 55: 899–902.
6.
TranV-XPanJPanT. Effects of processing time on strengths and failure modes of dissimilar spot friction welds between aluminum 5754-O and 7075-T6 sheets. J Mater Process Technol2009; 209: 3724–3739.
7.
LinY-CChenJ-N. Influence of process parameters on friction stir spot welded aluminum joints by various threaded tools. J Mater Process Technol2015; 225: 347–356.
8.
GargABhattacharyaA. On lap shear strength of friction stir spot welded AA6061 alloy. J Manuf Process2017; 26: 203–215.
9.
ShenZYangXYangSet al.Microstructure and mechanical properties of friction spot welded 6061-T4 aluminum alloy. Mater Design2014; 54: 766–778.
10.
LinP-CPanJPanT. Failure modes and fatigue life estimations of spot friction welds in lap-shear specimens of aluminum 6111-T4 sheets. Part 2: Welds made by a flat tool. Int J Fatigue2008; 30: 90–105.
11.
SuZ-MHeR-YLinP-Cet al.Fatigue analyses for swept friction stir spot welds in lap-shear specimens of alclad 2024-T3 aluminum sheets. Int J Fatigue2014; 61: 129–140.
12.
SuZ-MHeR-YLinP-Cet al.Fatigue of alclad AA2024-T3 swept friction stir spot welds in cross-tension specimens. J Mater Process Technol2016; 236: 162–175.
13.
HassanifardSAhmadiSRPourMM. Weld arrangement effects on the fatigue behavior of multi friction stir spot welded joints. Mater Design2013; 44: 291–302.
14.
AhmadiSRHassanifardSPourMM. Fatigue life prediction of friction stir spot welds based on cyclic strain range with hardness distribution and finite element analysis. Acta Mech2012; 223: 829–839.
15.
HassanifardSMohammadpourMRashidHA. A novel method for improving fatigue life of friction stir spot welded joints using localized plasticity. Mater Design2014; 53: 962–971.
16.
ChowdhurySChenDBholeSet al.Lap shear strength and fatigue life of friction stir spot welded AZ31 magnesium and 5754 aluminum alloys. Mater Sci Eng A2012; 556: 500–509.
17.
ChowdhurySChenDBholeSet al.Lap shear strength and fatigue behavior of friction stir spot welded dissimilar magnesium-to-aluminum joints with adhesive. Mater Sci Eng A2013; 562: 53–60.
18.
MalafaiaAMilanMOliveiraMet al.Fatigue behavior of friction stir spot welding and riveted joints in an Al alloy. Procedia Eng2010; 2: 1815–1821.
19.
VenukumarSBabyBMuthukumaranSet al.Microstructural and mechanical properties of walking friction stir spot welded AA 6061-T6 sheets. Procedia Mater Sci2014; 6: 656–665.
20.
UematsuYTokajiKTozakiYet al.Fatigue behaviour of dissimilar friction stir spot weld between A6061 and SPCC welded by a scrolled groove shoulder tool. Procedia Eng2010; 2: 193–201.
21.
UematsuYTokajiKTozakiYet al.Fatigue behaviour of dissimilar friction stir spot welds between A6061-T6 and low carbon steel sheets welded by a scroll grooved tool without probe. Fatigue Fract Eng Mater Struct2011; 34: 581–591.
22.
Committee AIH, Committee AIAPD. Metals handbook: properties and selection, New York: ASM International, 1990.
ASTM E384-10. Standard test method for Knoop and Vickers hardness of materials. West Conshohocken, PA: ASTM, 2010.
26.
ISO-14324. Resistance spot welding–destructive tests of welds—method for the fatigue testing of spot welded joints, Geneva, Switzerland: The International Organization for Standardization, 2003.
27.
BadarinarayanHShiYLiXet al.Effect of tool geometry on hook formation and static strength of friction stir spot welded aluminum 5754-O sheets. Int J Mach Tools Manuf2009; 49: 814–823.
28.
TozakiYUematsuYTokajiK. Effect of tool geometry on microstructure and static strength in friction stir spot welded aluminium alloys. Int J Mach Tools Manuf2007; 47: 2230–2236.
29.
BozziSHelbert-EtterABaudinTet al.Influence of FSSW parameters on fracture mechanisms of 5182 aluminium welds. J Mater Process Technol2010; 210: 1429–1435.
30.
SatoYSTakauchiHParkSHCet al.Characteristics of the kissing-bond in friction stir welded Al alloy 1050. Mater Sci Eng A2005; 405: 333–338.
31.
BarrosPCampanelliLAlcântaraNet al.An investigation on friction spot welding of AA2198-T8 thin sheets. Fatigue Fract Eng Mater Struct2017; 40: 535–542.
32.
VenukumarSMuthukumaranSYalagiSGet al.Failure modes and fatigue behavior of conventional and refilled friction stir spot welds in AA 6061-T6 sheets. Int J Fatigue2014; 61: 93–100.
33.
UematsuYTokajiKTozakiYet al.Effect of re-filling probe hole on tensile failure and fatigue behaviour of friction stir spot welded joints in Al–Mg–Si alloy. Int J Fatigue2008; 30: 1956–1966.