Preparation and properties of bismaleimide resin blended with alkynyl-terminated modifiers

Abstract

A kind of modified bismaleimide resin, with good processability, heat resistance, and impact strength was developed, using 4,4^′-dipropargyloxydiphenyl ether (DPEDPE), N-(4-propargyloxyphenyl)maleimide (4-PPM), and 3-ethynylphenyl maleimide (3-EPM) as modifiers. The DPEDPE, 4-PPM, and 3-EPM were synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) and ¹H-nuclear magnetic resonance (¹H NMR), and used to modify the N,N^′-(4,4^′-diphenylmethane)bismaleimide (BDM)/2,2^′-diallyl bisphenol A (DABPA) resin system (BD) to obtain the different blend resin systems of DPEDPE-modified BD (BDD), 4-PPM-modified BD (BDP), and 3-EPM-modified BD (BDE). The curing temperature of BD resin increases with increase of the alkynyl-terminated modifier content. The processability of BD resin was improved with addition of the propargyloxy-terminated compounds. The temperature of 5% weight loss, residual yield at 800°C and glass transition temperature of the cured BD resin increase with increase of the alkynyl-terminated modifier content and can reach 443°C, 46.7% and higher than 380°C. The tensile strength of the cured BD resin decreases with increase of alkynyl-terminated modifier content. The impact strength of the cured BD resin increases with increase of the propargyloxy-terminated compound content and can increase by 65%. The tensile strength, elastic modulus, and impact strength of the cured BD resin blended with DPEDPE can be 73.7 MPa, 4.1 GPa, and 19.6 kJ m⁻², respectively. Moreover, the cured BD resin blended with DPEDPE has good water absorption resistance.