Fluorinated polyimide and PVA blending membranes were prepared by aqueous solution casting. We chose a poly (amic acid) ammonium salt (PAAS) in aqueous solution based on a novel green strategy as the PI precursor. The blending membranes were characterized by ATR-FTIR, DSC, TGA and gas permeation measurement. The ATR-FTIR analysis revealed that the imidization reaction of 6FPI based on aqueous precursor was completed at 180°C and hydrogen bonds formed between PVA and 6FPI. 6FPI showed good compatibility with PVA segment in blending membranes without obvious separated phase structure. The blending membranes showed high separation properties, for blending with 6FPI the gas separation performance stability was improved due to the hydrogen bonds between hydroxyl groups of PVA and carbonyl groups of 6FPI, and the rigid structure of 6FPI. At high operating pressure 10 bar, the CO2 permeability and CO2/N2 selectivity remained rather high. Using water as the solvent in the PAAS synthesis and membrane preparation is more environmentally friendly and less costly.
ShollDSLivelyRP. Seven chemical separations to change the world. Nature2016; 523: 435–437.
2.
SandersDFSmithZPGuoR, et al.Energy-efficient polymeric gas separation membranes for a sustainable future: a review. Polymer2013; 54: 4729–4761.
3.
ZhangYSunarsoJLiuS, et al.Current status and development of membranes for CO2/CH4 separation: a review. Int J Greenhouse Gas Control2013; 12: 84–107.
4.
ParkHPKamcevJRobesonLM, et al.Maximizing the right stuff: the trade-off between membrane permeability and selectivity. Science2017; 356: eaab0530.
5.
MerkelTCLinHWeiX, et al.Power plant post-combustion carbon dioxide capture: An opportunity for membranes. J Membrane Sci2010; 359: 126–139.
6.
ZhaoYWinston HoWS. Steric hindrance effect on amine demonstrated in solid polymer membranes for CO2 transport. J Membrane Sci2012; 415-416: 132–138.
7.
ZhangXFHouTChenJ, et al.Facilitated transport of CO2 through the transparent and flexible cellulose membrane promoted by fixed-site carrier. ACS Appl Mater Interfaces2018; 10: 24930–24936.
8.
MaoZJieXCaoY, et al.Synthesis of visible-light sensitive M–BiVO4 (M=Ag, Co, and Ni) for the photocatalytic degradation of organic pollutants. Separat Purificat Technol2011; 77: 179–184.
9.
WindJDPaulDRKorosWJ. Natural gas permeation in polyimide membranes. J Membr Sci2004; 228: 227–236.
10.
TesoroG.Polyvinyl alcohol fibers, by Ichiro Sakurada, Marcel Dekker, New York, 1985, 449 pp. Price: $99.75. J Polym Sci Pt C: Polym Lett1986; 24: 485–486.
11.
MaXSwaidanRBelmabkhoutY, et al.Synthesis and gas transport properties of hydroxyl-functionalized polyimides with intrinsic microporosity. Macromolecules2012; 45: 3841–3849.
12.
JungCHLeeYM. Gas permeation properties of hydroxyl-group containing polyimide membranes. Macromolecul Res2008; 16: 555–560.
13.
ZhaoJWangZWangJ, et al.High-performance membranes comprising polyaniline nanoparticles incorporated into polyvinylamine matrix for CO2/N2 separation. J Membr Sci2012; 403-404: 203–215.
14.
DengLKimT-JHäggM-B. Facilitated transport of CO2 in novel PVAm/PVA blend membrane. J Membr Sci2009; 340: 154–163.
15.
DilshadMRIslamASabirA, et al.Fabrication and performance characterization of novel zinc oxide filled cross-linked PVA/PEG 600 blended membranes for CO2/N2 separation. J Industr Eng Chem2017; 55: 65–73.
ZhaoYHoWSW. Carbon dioxide-selective membranes for high-pressure synthesis gas purification. Industr Eng Chem Res2012; 50: 12152–12161.
23.
TasselliFJansenJSidariF, et al.Morphology and transport property control of modified poly(ether ether ketone) (PEEKWC) hollow fiber membranes prepared from PEEKWC/PVP blends: influence of the relative humidity in the air gap. J Membr Sci2005; 255: 13–22.
24.
BaiHHoWSW. Carbon dioxide-selective membranes for high-pressure synthesis gas purification. Industr Eng Chem Res2011; 50: 12152–12161.
25.
RaharjoRDFreemanBDPaulDR, et al.Pure and mixed gas CH4 and n-C4H10 permeability and diffusivity in poly(dimethylsiloxane). J Membr Sci2007; 306: 75–92.
26.
RaharjoRFreemanBSandersE. Pure and mixed gas CH4 and n-C4H10 sorption and dilation in poly(dimethylsiloxane). J Membr Sci2007; 292: 45–61.
27.
PowellCEQiaoGG. Polymeric CO2/N2 gas separation membranes for the capture of carbon dioxide from power plant flue gases. J Membr Sci2006; 279: 1–49.
28.
YampolskiiY. Polymeric gas separation membranes. Macromolecules2012; 45: 3298–3311.
29.
KaseY. Advanced membrane technology and applications. Hoboken, NJ: John Wiley & Sons, Inc, 2008, pp. 581–598.
30.
GarciaCLopez-GonzalezMde AbajoJ, et al.Effects of tricresylphosphate on gas transport coefficients in matrimid and 6FDA-TMPD polyimides. Macromolecules2011; 44: 3862–3873.
31.
TenaAFernándezLSánchezM, et al.Mixed matrix membranes of 6FDA-6FpDA with surface functionalized γ-alumina particles. An analysis of the improvement of permselectivity for several gas pairs. Chem Eng Sci2010; 65: 2227–2235.
32.
LiuYWangJGuoJ, et al.Bioinspired functional organohydrogels with synergistic multiphases heterostructure. Polymer2020; 190: 122216.
33.
LiuYGuoJWangJ, et al.UHMWPE for biomedical applications: performance and functionalization. Eur Polym J2020; 125: 109526.
34.
Alexander SternS. Polymers for gas separations: the next decade. J Membr Sci1994; 94: 1–65.
35.
MiYHiroseT. Aromatic polyoxyalkylene amidoamines as curatives for epoxy resins—derivatives from t-butyl isophthalic acid. J Polym Res1996; 3: 11–19.
36.
YuYLiuSWangY, et al.Asymmetric membranes prepared with trifluoromethylphenylated poly(ether ether ketone) for gas separation. High Perform Polym2014; 27: 10–18.
37.
CaoZZhaoXWangD, et al.Preparation and characterization of electrospun alginate nanofibers loaded with ciprofloxacin hydrochloride. Eur Polym J2017; 96: 393–402.
38.
YuYWangYLiT, et al.Synthesis, properties and gas separation performance of poly(arylene ether sulfone) containing imide pendant groups. RSC Adv2017; 7: 42468–42475.
39.
ImHKimHKimCK, et al.Enhancement of gas selectivities of hexafluoroisopropylidene-based polyimides with poly(methylmethacrylate) blending. Ind Eng Chem Res2009; 48: 8663–8669.
40.
XiaoYLowBTHosseiniSS, et al.The strategies of molecular architecture and modification of polyimide-based membranes for CO2 removal from natural gas—a review. Prog Polym Sci2009; 34: 561–580.
41.
LowBTXiaoYChungTS, et al.Simultaneous occurrence of chemical grafting, cross-linking, and etching on the surface of polyimide membranes and their impact on H2/CO2 separation. Macromolecules2008; 41: 1297–1309.
42.
Xiao-DongWQiangZ. Studies on miscibility of polyacetal with novolak. Chem J Chinese Universities2001; 22: 669–672.
43.
DilshadMRIslamAHamidullahU, et al.Effect of alumina on the performance and characterization of cross-linked PVA/PEG 600 blended membranes for CO2/N2 separation. Separat Purificat Technol2019; 210: 627–635.
44.
LiuBWangGHuW, et al.Poly(aryl ether ketone)s with (3-methyl)phenyl and (3-trifluoromethyl)phenyl side groups. J Polym Sci Pt A: Polym Chem2002; 40: 3392–3398.
45.
LiuBHuWChenC, et al.Soluble aromatic poly(ether ketone)s with a pendant 3,5-ditrifluoromethylphenyl group. Polymer2004; 45: 3241–3247.
46.
MondalAMandalB. Synthesis and characterization of crosslinked poly(vinyl alcohol)/poly(allylamine)/2-amino-2-hydroxymethyl-1,3-propanediol/polysulfone composite membrane for CO2/N2 separation. J Membr Sci2013; 446: 383–394.
47.
RobesonLM. The upper bound revisited. J Membr Sci2008; 320: 390–400.
48.
SanaeepurHAmooghinAEMoghadassiA, et al.Preparation and characterization of acrylonitrile–butadiene–styrene/poly(vinyl acetate) membrane for CO2 removal. Separat Purificat Technol2011; 80: 499–508.
49.
XinQWuHJiangZ, et al.SPEEK/amine-functionalized TiO2 submicrospheres mixed matrix membranes for CO2 separation. J Membr Sci2014; 467: 23–35.
50.
WindJDStaudt-BickelCPaulDR, et al.The effects of crosslinking chemistry on co2 plasticization of polyimide gas separation membranes. Industr Eng Chem Res2002; 41: 6139–6148.
51.
BosAPüntIStrathmannH, et al.Suppression of gas separation membrane plasticization by homogeneous polymer blending. AIChE J2001; 47: 1088–1093.
52.
IsfahaniAPGhaleiBWakimotoK, et al.Plasticization resistant crosslinked polyurethane gas separation membranes. J Mater Chem A2016; 4: 17431–17439.
53.
AiliDHansenMKRenzahoRF, et al.Heterogeneous anion conducting membranes based on linear and crosslinked KOH doped polybenzimidazole for alkaline water electrolysis. J Membr Sci2013; 447: 424–432.
54.
YuYWangJWangY, et al.Polyethyleneimine-functionalized phenolphthalein-based cardo poly(ether ether ketone) membrane for CO2 separation. J Industr Eng Chem2020; 83: 20–28.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.